Abstract                                                         

The issue of the protection of the environment is a shared responsibility between several destinations and sectors, and constitutes a main subject in which they can achieve sustainable development. In the sectors of government programs can be set up towards the establishment of the government sector to the green environment, so to be the implementati

SAPO-11 is synthesized from silicoaluminophosphate in the presence of di-n-propylamine as a template. The results show that the sample obtained has good crystallinity, 396m2/g BET surface area, and 0.35 cm3/g pore volume. The hydroisomerization activity of (0.25)Pt (1)Zr (0.5)W/SAPO-11 catalyst was determined using n-decane and base oil. All hydroisomerization experiments of n-decane were achieved at a fixed bed plug flow reactor at a temperature range of 200-275°C and  LHSV 0.5-2h-1.  The results show that the n-decane conversion increases with increasing temperature and decreasing LHSV, the maximum conversion of 66.7 % was achieved at temperature 275°C and LHSV of 0.5 h-1. Meanwhile, the same catalyst was used to improve base oil spec

In two commercial broiler breeds (Cobb 500 and Hubbard F-15), the polymorphisms of the chicken insulin-like growth factor 2 (IGF2) gene were studied. A total of three hundred avian blood samples were obtained. Using a fast salt-extraction technique, genomic DNA was isolated. Using polymerase chain reaction, 1146 bp fragments of the gene were amplified (PCR). The amplified fragments were subjected to restriction enzyme digestion using HinfI endonuclease enzyme, and the digested products were separated on a 2% agarose gel. The findings indicated two alleles T and C for the target locus, with respective frequencies of 73.3% and 26.7%. Three distinct genotype variations, TT, TC, and CC, were found, with genotype frequencies of 59.1 percent, 28.

The recent study aimed to identify the level of Self- Esteem and its relation to some variables (Gender, Experience years, and Educational stage) among psychologists in schools of the Sultanate of Oman. The study sample consisted of (154) psychologists of both male and female who are working in different stages of study in the schools affiliated to the Ministry of Education in the Sultanate of Oman. The sample of the study consisted of (43) male and (111) female psychologists from (11) governorates of the Sultanate. The descriptive analytical methodology was used. In order to collect data the Self-Esteem questionnaire prepared by the researcher were used. Statistical processing was done using the Statistical Package for Social Sciences (

Thin films of pure polycarbonate (PC) with anthracene doping PC films for different doping ratios (10, 20, 30, 40, 50 and 60 ml) were prepared by using a casting method. The influence of anthracene doping ratio on photo-fries rearrangement of polycarbonate was systematic investigated. Furthermore, pure PC and anthracene doping PC films were irradiated via UV light at a wavelength (254 nm) for different periods (5, 240, 288, and 360 hrs). The photo-fries rearrangement occurring in pure PC and anthracene doping PC films were monitored using UV and FTIR spectroscopies. The photo-fries rearrangement leads to scission the carbonate linkage and formation phenylsalicylate and dihydroxybenzophenes. The result of the UV spectrum confirms disappea

Tuberculosis status as the second leading causes of significant morbidity and mortality from an infectious disease worldwide, after human immunodeficiency virus (HIV). Sample collection was conducted at the Institute of Chest and Respiratory Diseases/Baghdad Medical City in Baghdad. The collection interval was from August to October 2014, 629 suspected TB patients were examined during this period. The results revealed among total 629 specimens, 56 (8.9%) of the specimens were positive by direct examination and 573 (91.1%) negative specimens by smear microscopy. Fifty six DNA samples were extracted from positive ZN smears of sputum specimens and 40 samples from healthy persons (as control) were subjected to molecular diagnosis by real tim

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c