Background: Poly propylene fibers with and without silane treatment have been used to reinforce heat cure denture base acrylic but, some mechanical properties like transverse strength, impact strength, tensile strength, hardness, wear resistance and wettability. Which are related to the clinical use of the prosthesis are not evaluated yet. The aim of the study is to identify the influence of incorporation of treated and untreated fibers on these properties Materials and methods: Eighty four heat cure acrylic specimens were constructed by conventional flasking technique. They were divided into six groups according to the tests and each group was subdivided into two subgroups control and experimental groups (seven samples for each subgroup).Transversestrength and Tensile strength test were performed using Instron universal testing machine. The impact strength test was evaluated by the use of Impact testing device. Wear resistance was evaluated by pin on disk wear measurement method while, a digital microscope supplied with high resolution camera was utilized to measure the contact angle reflecting wettability grade. Descriptive statistics and independent t test were used for statistical significance. Results:The results revealed that the addition of Silanated polypropylene fibers produced significant difference in transverse strength and highly significant difference in tensile strength, the impact strength,Wettability value compared with the control group also the results showed that the hardness test was not significant and different control group . Wear resistance was highly significant decreased in experimental groups Conclusion: Incorporation of silanated treated Poly propylene fibers to heat cure Poly methyl methacrylate resin was beneficial regarding the tested properties to improve the mechanical properties of the resin. Key words: Poly propylene fibers, transverse strength, impact strength, tensile strength, hardness, wear resistance, wettability.
The investigation of the effect of tempering on thermal analysis of
Al-Ti-Si alloy and its composites with MgO and SiC particles was
performed. Thermal analysis was performed before and after
tempering by DSC scan. Optical microscopy was used to identify the
phases and precipitations that may be formed in base alloy and
composites. X-ray diffraction test indicated that the Al3Ti is the main
phase in Al-Ti-Si alloy in addition to form Al5Ti7Si12 phase. Some
chemical reactions can be occurred between reinforcements and
matrix such as MgO.Al2O3 in Al-Ti/MgO, and Al4C3 and Al(OH)3 in
Al-Ti/SiC composite. X-ray florescence technique is used to
investigate the chemical composition of the fabricated specimens.
H
(1)
Concentrations 25, 50 and 100 mg of nano-capsules linolenic acid and non-capsulated fatty acid for 1kg of Milk was used for yogurt manufacture. The results showed no significant differences in the ratio of titration acidity and pH values between all processed treatments at the beginning and during of period storage. The treatments was added to it coated omega-3 by nano method were the least exposed to the oxidation process from the non-capsules omega-3, And for shield of The poly lactic acid had a significant role in the protection of alpha-linolenic acid against lipolysis by the formation of a protective layer to protect the acid from the activity of lipases enzymes, and the addition of fatty acid linolenic to milk was determined the gr
... Show MoreIn this research PbS thin film have been prepared by chemical bath deposition technique (CBD).The PbS film with thickness of (1-1.5)μm was thermally treated at temperature of 100°C for 4 hours. Some Structural characteristics was studied by using X-ray diffraction (XRD)and optical microscope photograph some of chemical gas sensing measurements were carried out ,it shown that the sensitivity of (CO2) gas depend on the grain Size and deposition substrate. The grain size of PbS film deposited on on glass closed to 21.4 nm while 37.97nm for Si substrate. The result of current-voltage characterization shwon the sensitivity of prepared film deposited on Si better than film on glass.
Natural fibers and particles reinforced composites are being broadly used due to their bio and specific properties such as low density and easy to machine and production with low cost. In this work, water absorption and mechanical properties such as tensile strength, flexural strength and impact strength of recycled jute fibers reinforced epoxy resin were enhanced by treating these fibers with alkaline solution. The recycled jute fibers were treated with different concentration of (NaOH) solution at (25 0C) for a period of (24) hours. From the obtained results, it was found that all these properties are improved when fibers treated with (7.5wt% NaOH) related to untreated fibers. Conversely, the mentioned properties of composit
... Show More
The present research deals with the influencing factors which depends on the way perceptual of the graphic designer which enters in the design logos of the loco European health, where the search include four chapters, the researcher reviewed in the chapter 0ne the methodical frame of the research ,as reviewed in the second chapter the theoretical frame, and the previous studies which included three sections, the first section included the perceptual understandable and types of it, and the second section included the influencing factors in the designer perceptual ways and its division . While the third section included the perceptual in graphic designer through the percepted shapes and the relation with ground and colors for express the i
... Show More
A new Schiff base (4-chlorophenyl)(phenyl methanimine (6R,7R)-3-methyl-8-oxo-7-(2-phenylpropanamido)-5-thia-1-azabicyclo[4.2.0]oct-2-ene-2-carboxylate=HL=C29H24ClN3O4S) has been synthesized from β-lactam antibiotic (cephalexin mono hydrate (CephH)=(C16H19N3O5S.H2O) and 4- chlorobenzophenone. Metal mixed ligand complexes of the Schiff base were prepared from chloride salt of Fe(II), Co(II), Ni(II), Cu(II), Zn(II) and Cd(II), in 50% (v/v) ethanol – water medium in aqueous ethanol(1:1) and Saccharin(C7H5NO3S) containing sodium hydroxide. Several physical tools in particular; IR, C:H:N , 1H NMR,13C NMR for ligand, melting point, molar conductance, magnetic moment. and determination of the percentage of the metal in the complexes by flame(AAS
... Show Morenew Schiff base 4-chlorophenyl)methanimine (6R,7R)-3-methyl-8-oxo-7-(2-phenylpropanamido)-5-thia-1-azabicyclo[4.2.0]oct-2-ene-2-carboxylate= (HL)= C23H20 ClN3O4S) has been synthesized from β-lactam antibiotic (cephalexin mono hydrate(CephH)=(C16H19N3O5S.H2O) and 4-chlorobenzaldehyde . Figure(1) Metal mixed ligand complexes of the Schiff base were prepared from chloride salt of Fe(II),Co(II),Ni(II),Cu(II),Zn(II) and Cd (II), in 50% (v/v) ethanol –water medium (SacH ) .in aqueous ethanol(1:1) containing and Saccharin(C7H5NO3S) = sodium hydroxide. Several physical tools in particular; IR, CHN, 1H NMR, 13C NMR for ligand and melting point molar conductance, magnetic moment. and determination the percentage of the metal in the complexes by fl
... Show More