Effect of sodium fluoride on the properties of acrylic resin denture base material subjected to long-term water immersion
...Show More Authors

Background: Fluoridated acrylic resin material can present more stable properties when compared with conventional one.The most widely used fluoride –containing substance added to dental resin materials is sodium fluoride (Naf). This study evaluated the effect of Naf in different concentration to the acrylic resin denture base material and its effect on tensile strength ,modules of elasticity with long –term water immersion (after 4 months immersion in de-ionized water) Materials and methods: Eighty specimens from dumbbells shaped metal pattern for tensile strength test were preparedaccording to ISO 527: 1993 plastic –Determination tensile properties ,in dimensions(60mm, 12mm, 3 ± 0.2mm) length, width and depth respectively were allocated to two groups according to water immersion there were 40 specimens before immersion and 40 specimens after water immersion for 4 months in de-ionized water(the de-ionized water was changed every day),these two groups were sub divided in to four groups according to the concentration of Naf,Naf powder were added to monomer of acrylic in concentrations of 1%,2%and 5% Naf .0% Naf(control group) ,then mixing were done with polymer according to manufacture instructions ,the conventional flasking ,packing procedure were used following that (fast cycle). For tensile strength test the measuring was done by Instron machine,the values of modulus of elasticity were obtained from tensile test . Results: Results showed that the addition of sodium fluoride to acrylic resin material werelower the tensile strength and modules of elasticity with highly significant differences p<0.01 when compared to control group regardless the concentration of Naf,But after immersion (for 4 month ) the tensile strength and modules of elasticity increased in comparison to groups before immersion (with highly significance differences p <0.01 ), highly significance differences (p <0.0)were found between groups after and before immersion in all concentrations except for tensile strength between 1%Naf and 2%Naf after immersion there was no significant differences(p>0.05), and for modules of elasticity between control and 1%Naf, 1% Naf and 2%Naf( after immersion ),there was only significant differences between them(p<0.05). Conclusions: Addition of fluoride to acrylic resin material lower the tensile strength and modules of elasticity when compared to control group regardless the concentration of Naf, But after immersion (for 4 months ) the tensile strength and modules of elasticity increased in comparison to groups before immersion (with highly significance differences p <0.01).

View Publication Preview PDF
Quick Preview PDF
Publication Date
Tue Dec 24 2024
Journal Name
Journal Of Baghdad College Of Dentistry
Effect of silver nitrate incorporation into heat polymerized acrylic resin on some mechanical properties
...Show More Authors

Background: Polymers are very rarely used in their form. These modifications are carried out in order to improve the properties of polymers.Recently silver have been used successfully as antimicrobial (medical and dental) biomaterials that can prevent caries and infection of implants Purposes: The aim of the present in vitro study is to evaluate the effect of addition of silver nitrate to acrylic resin in different concentrationsthrough several tests part of these are: The effect of this additive on impact strength, transverse strength, and tensile strength of AgNO3 – loaded resin, and to assess any effect of addition of silver nitrate on coloration of acrylic resin. Materials and methods: Different concentrations of silver nitrate

... Show More
View Publication Preview PDF
Publication Date
Fri Jan 01 2021
Journal Name
Materials Today: Proceedings
Impact of phosphate ester addition on the cytotoxicity of heat cured denture base material
...Show More Authors

This study aims to evaluate and compare the cytotoxicity and biocompatibility of a modified heat-cured acrylic denture base material containing 15% phosphoric acid 2-hydroxyethyl methacrylate ester (PA2HEME) with those of nonmodified PMMA. Discs with a diameter of 12 mm and a thickness of 2 mm were prepared using a heat-cured PMMA denture base material and divided into control and experimental groups. The experimental group was modified with 15% phosphoric acid 2-hydroxyethyl methacrylate ester (PA2HEME). The modified and nonmodified materials were tested via FTIR, and the effect of modification on surface roughness was evaluated with AFM. An in vitro test was conducted to examine the cytotoxicity and biocompatibility of heat-cured acry

... Show More
View Publication
Scopus (1)
Crossref (1)
Scopus Clarivate Crossref
Publication Date
Tue Dec 24 2024
Journal Name
Journal Of Baghdad College Of Dentistry
Effect of post-pressing times on adaptation of maxillary heat cured acrylic denture base at posterior palatal seal area
...Show More Authors

Background: The purpose of this study was to verify the influence of post- pressing time of acrylic resin (immediate, 6, 12 and 24 hour) on the dimensional accuracy of denture base whish is a critical factor in the retention and stability of the complete denture that may occur during polymerization shrinkage. Materials and Methods: Forty maxillary stone casts were poured in plastic mold (Columbia Dentoform corp. NEW YORK, type III dental stone (Geastone, Zeus Sri Loc.Tamburine Roccastrada, GR, Italy). The stone casts were randomly assigned into 4 groups of 10 specimens each according to the post-pressing times into (immediate, 6, 12 and 24 h.). Heat cure acrylic resin denture base was constructed according to the previously mentioned pressi

... Show More
View Publication Preview PDF
Publication Date
Tue Dec 24 2024
Journal Name
Journal Of Baghdad College Of Dentistry
Evaluation of the effect of addition of polyester fiber on some mechanical properties of heat cure acrylic resin
...Show More Authors

Background: This study aimed to evaluate the effect addition of polyester fibers on the some mechanical properties of heat cured acrylic resin (implant strength, flexural strength and hardness) Materials and methods: Ninety specimens were used in the study. Thirty specimens were used for impact strength measurements (80mm X 10mm X 4mm) length, width and thickness respectively. The specimens divided into three test groups (n=10), first group formed from heat cure acrylic resin without fiber reinforcement. Second group was formed from heat cure acrylic resin was reinforced with 2 mm length polyester fiber and third group was formed from heat cure acrylic resin reinforced with 4mm length polyester fiber, impact strength measured by impact test

... Show More
View Publication Preview PDF
Publication Date
Tue Dec 24 2024
Journal Name
Journal Of Baghdad College Of Dentistry
The effect of plasma treatment on shear bond strength of soft denture liner with two different types of denture base material (heat cure and light cure)
...Show More Authors

Background: In this study we evaluate the effect of plasma treatment (oxygen and argon) gas in two different exposure times on the surface of heat cure and light cure acrylic resin. Materials and method: 100 specimens of heat cure and light cure acrylic resin were fabricated. The measurements of the samples were (75mm, 25mm and 4.5mm) length, width and depth respectively with stopper of 3mm depth. Two types of gas used oxygen and argon in (5,10) min by using (DC-glow discharge plasma device) then we apply cold cure soft lining material, with the help of Instron machine we test the shear stress value. Results: A highly significant effect after argon and oxygen gases treatment in both 5 and 10 min exposure times on shear bond strength to soft

... Show More
View Publication Preview PDF
Publication Date
Mon Jun 01 2009
Journal Name
Al-khwarizmi Engineering Journal
Study the Effect Different Radioactive Dose on Mechanical Properties of Composite Material from Novolak Resin Exposure to High – Energy Radiation
...Show More Authors

The research involves using phenol – formaldehyde (Novolak) resin as matrix for making composite material, while glass fiber type (E) was used as reinforcing materials. The specimen of the composite material is reinforced with (60%) ratio of glass fiber.

      The impregnation method is used in test sample preparation, using molding by pressure presses.

      All samples were exposure to (Co60) gamma rays of an average energy (2.5)Mev. The total doses were (208, 312 and 728) KGy.

      The mechanical tests (bending, bending strength, shear force, impact strength and surface indentation) were performed on un irradiated and irrad

... Show More
View Publication Preview PDF
Publication Date
Tue Dec 24 2024
Journal Name
Journal Of Baghdad College Of Dentistry
Effect of silica layer on bonding strength of thermoplastic nylon to cold cure acrylic resin
...Show More Authors

Background: The combination of thermoplastic nylon resin materials and auto polymerizing resin is necessary in some situation for repair and adjustment. This study evaluated shear bond strength between thermoplastic nylon material (flexible) and auto polymerizing acrylic resin subjected to holes and silica coated layer. Materials and Method: Forty five (45) specimens were prepared from flexible acrylic bonded to auto-polymerizing acrylic resin and divided into three groups according to the surface treatments as follows: Group A: 15 specimens of flexible acrylic bonded with cold-cure acrylic by holes. Group B: 15 specimens of flexible acrylic bonded with cold-cure acrylic by silica coated layer. Group C: 15 specimens of flexible acrylic bon

... Show More
View Publication Preview PDF
Publication Date
Thu Mar 30 2023
Journal Name
Iraqi Journal Of Science
Effect of immersion in chemical solution on the mechanical & physical properties for composite material reinforced by Nano alumina Particles
...Show More Authors

In this research Epoxy resin was reinforced by nano alumina (AL2O3) particles in grain size(25-30 nm) with two weight ratios (2,4)% then compared with pure Epoxy. Four mechanical tests were performed on these materials include Hardness, flexural, impact & compression strengths before and after immersion in tap water and chemical solutions (CH3COOH) acid, (KOH) base at (0.5N) ,The diffusivity coefficients of all prepared samples were calculate after immersion in water and chemical solutions mentioned above , the results were showed that the Flexural, Impact & Hardness increase after addition the ceramic particles (AL2O3) while the immersion process results showed illustrated different values from sample to other.

View Publication Preview PDF
Publication Date
Wed Sep 19 2018
Journal Name
Biomedical And Pharmacology Journal
Influence of Silver Nanoparticles on the Specific Properties of Acrylic Resin for Ocular Prosthesis
...Show More Authors

Scleral acrylic resin is widely used to synthesize ocular prosthesis. However, the properties of this material change over time, thus requiring the prosthesis to be refabricated. Many studies were conducted to improve these properties by reinforcing this material with nanoparticles. This study aims to evaluate the effect of silver nanoparticle powder on the mechanical properties (transverse flexural strength, impact strength, shear bond strength, surface microhardness, and surface roughness) of scleral acrylic resin used for ocular prostheses. Two concentrations were selected from the pilot study and evaluated for their effects on scleral acrylic resin properties. According to the pilot study, 0.01 and 0.02wt% AgNPs powder improved

... Show More
View Publication
Scopus (4)
Crossref (4)
Scopus Crossref
Publication Date
Wed Nov 07 2018
Journal Name
Iraqi National Journal Of Nursing Specialties
Evaluation of the Hardness of Cold Cured Acrylic Resin Material by Processing at Different Temperature
...Show More Authors

Objective(s): This study aims to evaluate the hardness of two commercially available cold cured acrylic resin material
(Vertex and PAN) when polymerized at different temperature in comparison to those polymerized by conventional
methods in air at 23C ± 5C.
Methodology: Eighty specimens, forty from cold cured acrylic (Vertex Type) and forty from cold cured acrylic (PAN
type) were prepared, flasking and packing procedure were done according to manufacturer direction and divided
according to processing as follow: 20 specimens (10 from Vertex type and 10 from PAN type) were processed in air for
two hours at 23C ± 5C under press (bench curing) as a control, and 60 specimens (30 from Vertex type and 30 from
PAN type) wer

... Show More
View Publication Preview PDF