Orange peel was used as a plant-derived medium to prepare a ZnO–calcite mixed-phase nanostructured material, which was physicochemically characterized and evaluated for DPPH radical-scavenging, α-glucosidase inhibitory, and in vitro cytotoxic activities. XRD confirmed the coexistence of hexagonal wurtzite ZnO and crystalline calcite, with ZnO apparent crystallite sizes ranging from 9.2 to 28.3 nm (mean 16.4 ± 7.3 nm). FTIR identified Zn–O vibrations, carbonate-related bands, surface hydroxyl groups, and residual organic functionalities, while FESEM revealed irregular agglomerates composed of nanoscale grains. EDX showed Zn, O, C, and Ca as the principal elements, and the material exhibited a zeta potential of -14.86 ± 0.52 mV

Background: Synthetic hydroxyapatite,(Ca10(PO4)6(OH2) can directly bond to bones without infection and fibrous encapsulation, thus is regarded as bioactive and biocompatible. The aim of the study was the estimation of microarchitecture bone parameters include bone mass (gm/cm2) cortical bone width (mm), thread width (mm), marrow space star volume analysis (V*m) and osteoblast, osteocyte cell number. Materials and methods: Ninety-six (96) commercially pure titanium CpTi) used in this study, (48) implants were coated with HA by dipping coating and (48) implants were used as control. They were inserted in (32) Newzland white rabbits and followed for 2 & 6 weeks. Mechanical torque removal test and histomorphometric analysis of bone microarchit

Due to the exceedingly high integration density of VLSI circuits and the resulting high power density, thermal integrity became a major challenge. One way to tackle this problem is Dark silicon. Dark silicon is the amount of circuitry in a chip that is forced to switch off to insure thermal integrity of the system and prevent permanent thermal-related faults. In many-core systems, the presence of Dark Silicon adds new design constraints, in general, and on the communication fabric of such systems, in particular. This is due to the fact that system-level thermal-management systems tend to increase the distance between high activity cores to insure better thermal balancing and integrity. Consequently, a designing dilemma is created wh

Aim of the study: This study's goal was to determine how laser surface alteration affected wettability of injectable thermoplastic acrylic and heat cure acrylic denture base materials. Materials and methods: Injectable thermoplastic acrylic resin (Deflex) and heat cure acrylic (Procryla) were used in this study to produce forty-disc shaped specimens, 20 specimens for each material type. The control group was made up of ten samples of each type of plastic denture base material. The other ten samples were treated with a nano-pulse fiber-optic lens Nd:YAG laser. The results were looked at with the Kruskal-Wallis test and the unpaired t-test (a=.05). Results: Compared to the control groups, the laser-treated groups were more likely to sti

The objective of this study is to demonstrate the corrosion behavior of dental alloys Co-Cr-Mo, Ni-Cr-Mo and Ti-Al-V in artificial saliva at pH=4 and 37oC enriched with ethyl alcohol at 8% percentage. The linear and cyclic polarizations were investigated by electrochemical measurements. Laser surface modification was achieved for the three dental alloys to improve corrosion resistance. The results show that corrosion resistance of Co-Cr-Mo and Ni-Cr-Mo alloys only were increased after laser treatment due to the fact that laser radiation has caused a smoother surface, in addition to the decrement in corrosion current densities (icorr) for Co-Cr-Mo and Ni-Cr-Mo alloys and the reverse scan in cyclic polarization became in the wider range of