Background: Calcium hydroxide and calcium-silicate materials used as direct pulp capping materials. The aims of this in vitro study is to compare among these materials in, the calcium ion release and pH change in soaking water after immersion of materials’ specimens in deionized water. Also Solubility and water sorption of materials’ specimens measured after soaking time. Calcium-silicate materials used were Biodentine, TheraCal and MTA Plus. Materials and methods: Four materials used in this study; Urbical lining (as control group), Biodentine, TheraCal and MTA Plus. Ten discs fabricated from each tested material, by using plastic moulds of 9 mm diameter and 1 mm thickness. Each specimen was immersed in 10 ml of deionized water and stored at 37ºC using incubator for 3 hr, 24hr, 14 days and 30 days as a sequence. The amount of calcium ion (Ca+2) released in soaking water was measured in each tube using atomic absorption spectrophotometer. Also pH analysis for soaking water measured by using pH meter. For solubility and water sorption measurement, the specimen (n=10) weighed with precision weighing scale before immersion in deionzed water to determine the initial Weight (W1) and immediately after weighing immersed in 10 mL of deionized water at 37 °C for 1 week using an incubator, then removed and weighing again (W2). The samples blotted dry using filter paper and dehydrated in an oven at 37 °C for 24 hr. and weighed again (W3). Then percentage of solubility and water sorption were determined. Data obtained were analyzed using one-way ANOVA and Tukey tests at 0.05 significant levels. Results: Statistical analysis showed highly significant differences (P<0. 05) among tested materials and in all tests (Ca+2 release, pH change, solubility and water sorption). Biodentine showed higher calcium ion released at four soaking time (3 hr, 24hr, 14 days and 30 days), with non significant difference with TheraCal and highly significant difference with MTA Plus and control group at 24 hr. immersion time; While MTA Plus showed non significant difference with control group at 24 hr. Less amount of calcium released was in control group. All tested materials induced alkalization of the soaking water that decreased with time. Means of solubility and water sorption showed that MTA Plus and biodentine had higher solubility in comparison with control group, while TheraCal showed less solubility than control group. The results of water sorption showed that less sorption percentage occurred in control group in comparison with other groups. Conclusion: calcium-silicate materials released more Ca+2 with time than calcium hydroxide. TheraCal showed less solubility and higher water sorption in comparison with control group. Biodentine and MTA Plus showed higher solubility and water sorption in comparison with TheraCal and control group.
In this study, polymeric coating was developed by incorporating nano graphene in the polymer blend with applications to oil storage tanks. The oil storage tanks samples were brought from the oil Pipeline Company / Doura refinery in Baghdad. The coating polymer was formed with a blend (epoxy resin and repcoat ZR). The proportion of mixing the mixture was 3:1:1 epoxy resin 21.06 gm: repcoat ZR 10.53 gm: hardener 10.53 gm. The blend/graphene was prepared using in stui-polymerization method with different weight percentage 1, 3, 5, and 7 wt % added to blend. The resulting solution was put in a glass tube on a magnetic stirrer for one hour at a temperature of 40 °C. The result of contact angle and wate
... Show MoreDBN Rashid, Rimak International Journal of Humanities and Social Sciences, 2020
This paper studies the demonstratives as deictic expressions in Standard Arabic and English by outlining their phonological, syntactic and semantic properties in the two languages. On the basis of the outcome of this outline, a contrastive study of the linguistic properties of this group of deictic expressions in the two languages is conducted next. The aim is to find out what generalizations could be made from the results of this contrastive study.
A Al-Nuaimy, B Fadheel…, IPMJ, 2009 - Cited by 1
AN Adil A, F Basman M, 2009
Traumatic spinal cord injury is a serious neurological disorder. Patients experience a plethora of symptoms that can be attributed to the nerve fiber tracts that are compromised. This includes limb weakness, sensory impairment, and truncal instability, as well as a variety of autonomic abnormalities. This article will discuss how machine learning classification can be used to characterize the initial impairment and subsequent recovery of electromyography signals in an non-human primate model of traumatic spinal cord injury. The ultimate objective is to identify potential treatments for traumatic spinal cord injury. This work focuses specifically on finding a suitable classifier that differentiates between two distinct experimental
... Show MoreThis research highlights the light on the general framework of accounting discloser in the Islamic banks, and show the types and the concepts of Cost Efficiency, In this present study, the sample included Fourteen Islamic banks, where the data was collected from the annual financial reports. Accordingly, the study in order to achieve the aims and access to the results based on the analytical method and the descriptive analysis, and conducted a Simple & Multiple Linear Regression analysis, in order to test hypotheses of the research by using of statistical analysis software (SPSS). The research has arrived to many results such as: the commitment of Islamic banks working in the Kingdome of Bahrain (Wholesale) to the requirements of the
... Show More