The aim of this work is to enhance the mechanical properties of the glass ionomer cement GIC (dental materials) by adding Zirconium Oxide ZrO₂ in both micro and nano particles. GIC were mixed with (3, 5 and 7) wt% of both ZrO₂ micro and nanoparticles separately. Compressive strength (CS), biaxial flexural strength (BFS), Vickers Microhardness (VH) and wear rate losses (WR) were investigated. The maximum compression strength was 122.31 MPa with 5 wt. % ZrO₂ micro particle, while 3wt% nanoparticles give highest Microhardness and biaxial flexural strength of 88.8 VHN and 35.79 MPa respectively. The minimum wear rate losses were 3.776µg/m with 7 wt. % ZrO₂ nanoparticle. GIC-contai

Aims: This study was conducted to assess the effect of the addition of yttrium oxide (Y2O3) nanoparticles on the tensile bond strength, tear strength, shore A hardness, and surface roughness of soft-denture lining material. Materials and Methods: Y2O3 NPs with 1.5 and 2 wt.% were added into acrylic-based heat-cured soft-denture liner. A total of 120 specimens were prepared and divided into four groups according to the test to be performed (tensile bond strength, tear strength, surface hardness, and surface roughness). Results: There was a highly significant increase in tensile bond strength between the soft liner and the acrylic denture base, tear strength, and hardness at both concentrations as compared to the control group, whereas ther

        This study highlights the problems of translating Shakespeare's food and drink-related insults (henceforth FDRIs) in (Henry IV, Parts I&II) into Arabic. It adopts (Vinay & Darbelnet's:1950s) model, namely (Direct& Oblique) to highlight the applicability of the different methods and procedures made by the two selected translators (Mashati:1990 & Habeeb:1905) .The present study tries to answer the following questions:(i) To what extent the FDRIs in Henry IV might pose a translational problem for the selected translators to find suitable cultural equivalents for them? (ii) Why do the translators, in many cases, resort to a literal procedure which is almost not worka

In this research, geopolymer mortar had to be designed with 50% to 50% slag and fly ash with and without 1% micro steel fiber at curing temperature of 240℃. The molarity of alkaline solution adjusted with 12 molar sodium hydroxid to sodium silicate was 2 to 1, reaspectivly. The heat of curing increased the geopolymerization proceses of geoplymer mortar, which led to increasing strength, giving the best result and early curing age. The heat was applied for two days by four hours each day. It was discovered in the impact test that the value first crack of each mix was somewhat similar, but the failure increased 72%  for the mixture that did not contain fiber. For the energy observation results it was shown that the mixt

    To fabricate an inexpensive surface coating with excellent mechanical properties with good water resistance and thermal diffusion, white eggshell fibers with particle size (~1micrometer) has been added by different weight percentages (1,2,3,4,5,6,7 and 8 %) to Unsaturated Polyester.

The weight ratio (4%) of eggshell powder is a good ratio to be added to polyester to improve its mechanical properties, such as hardness, impact strength, and wear resistance. The hardness was improved by (3.75%); impact strength has the same value as polyester, flexural strength by (8.43%) and high improvement in wear resistance (74.4%), as well as to get further improvements in mechanical properties of polyester, the eggshell powder was added