Herein, date palm (Phoenix dactylifera) bunch (DPB) waste was transformed into activated carbon (DPAC) adsorbent by using microwaveinduced ZnCl2 activation for 15 min at a power of 600 W. Several analytical methods were used to explain the physicochemical parameters of DPBAC including XRD, pHpzc, BET, SEM–EDX, and FTIR. Afterwards, the adsorptive performance of DPBAC was thoroughly investigated for the removal of two structurally different organic dyes namely methyl violet (MV) and fuchsin basic (FB). The key adsorption parameters, including the dose of DPBAC (A: 0.02–0.06 g), the solution pH (B: 4–10), and the contact time (C: 2–20 min) were statistically optimized using the Box-Behnken design with response surface methodology (RSM

A new series of chalcone derivatives featuring an oxadiazole-quinoline moiety were successfully synthesized through a multi-step reaction sequence, commencing with quinoline-2-carboxylic acid as the starting material. First, the carboxylic group was chlorinated to form an acid chloride, following reacted with hydrazine hydrate. The resulting product underwent cyclization with carbon disulfide in an alkaline solution to produce 5-(quinolin-2-yl)-1,3,4-oxadiazole-2-thiol, followed by alkylation using chloroacetone. In the final step, an aldol condensation reaction was carried out by grinding the acetone derivative with various aromatic aldehydes, yielding the desired chalcones. The synthesized compounds were characterized by Rf, FTIR,

In this work, electrochemical process was presented to polymerized eugenol on Gr.2 and Gr.5 titanium alloys before and after treated by Micro Arc Oxidation (MAO), where Gr.2 is commercial pure titanium and Gr.5 is Ti-6Al-4V dental alloys. The deposited layers were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). The adhesion strength of polymeric thin-film was estimation by using pull-off adhesion test and the result was the adhesion strength of PE was (1.23 MPa) on Gr.2 before MAO and increase to (1.98 MPa) on Gr.2 after MAO treatment. The corrosion behavior of Gr.2 and Gr.5 alloy in artificial saliva environment at