Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

Asphalt binder is a thermoplastic material that conducts as an elastic solid at lower service temperatures or throughout fast loading rate. At a high temperature or slow rate of loading, asphalt binder conducts as a different liquid. The classical duplication generates a required to assess the mechanical properties of asphalt concrete at the anticipated service temperature to reduce the stress cracking, which happens at lower temperatures, fatigue, and the plastic deformation at higher temperatures (rutting). In this study, an achievement was made to assess the effect of temperature on the mechanical characteristics of asphalt concrete mixes. A total of 132 asphalt concrete samples were attended utilizing two asphalt cement grades (40-50) a

In this research, the mechanical properties of natural rubber blends in different proportions (70:30, 85:15, 100: 0 55:45 and phr) was studied through the use of two types of fillers (carbon black and titanium dioxide Nano) which show through tests conducted on the prepared models that increase fillers content which leads to improve the tensile properties (tensile strength, elastic modulus, elongation, hardness and compressibility). As shown by the results that the presence of polypropylene (PP) in the mix combination works to reduce the degree of intumescent and increase its content in the composition of mixtures which leads to get a great resistance to chemicals (acids, bases and oils).

Knowing the distribution of the mechanical rock properties and the far field stresses for the field of interest is an important task for many applications concerning reservoir geomechanics, including wellbore instability analysis, hydraulic fracturing, sand production, reservoir compaction, and subsidence. A major challenge with determining the rock's mechanical properties is that they cannot be directly measured at the borehole. Furthermore, the recovered carbonate core samples for performing measurements are limited and they provide discrete data for specific depths.

   The purpose of this study is to build 2D and 3D geomechanical models of the Khasib reservoir in the East Baghdad oil field/ Central area. TECHLOG.2015.3 softwa

Synthesis of a new ligand, namely [bis(2-(2-methyl-5-nitro-1H-imidazol-1-yl)ethyl) hydrogen borate] (BIB), utilizing the reaction of metronidazole with boric acid in a (2:1) mole ratio The metal complexes were synthesized utilizing the reaction of (NiCl₂.6H₂O and CuCl₂ .2H₂O) with (BIB) ligand in a 2:1 (L:M) mole ratio. All synthesized compounds were characterized utilizing spectroscopic techniques such as infrared (FTIR), nuclear magnetic resonance of protons(¹H NMR), ultra violet and visible radiation (UV-Vis), thermal analysis (TG), atomic absorption (A.A.S.), micro elemental analysis (C.H.N.S.), melting point (m.p.), magnetic susceptibility, molar conductivity, and chlor

The  research includes attempts to prepare anthranil ic acid (C7H7N02) complexes  with some metals: [Pd (II), Fe(ll), and  Fe (Ill))  which have been characterized by using:

Thermal stability (melti ng point, d composition poit), molar conductivity, IR,   UV-visible   spectra,   elemental   analysis   (C-H-N)   and   magnetic properties.  The   general  formula   has   been  given for  the   prepared complexes:-

- M(C2H6N02)2 Where M= [Pd(ll), Fe(TI), Hg(ll)]

:.. M(C1H6N02)l Where  M= [Fe(llf)]

The aim of this research is to develop mechanical properties of a new aluminium-lithium-copper alloy. This alloy prepared under control atmosphere by casting in a permanent metal mould. The microstructure was examined and mechanical properties were tested before and after heat treatment to study the influence of heat treatment on its mechanical properties including; modulus of elasticity, tensile strength, impact, and fatigue. The results showed that the modulus of elasticity of the prepared alloy is higher than standard alloy about 2%. While the alloy that heat treated for 6 h and cooled in water, then showed a higher ultimate tensile stress comparing with as-cast alloy. The homogenous heat treatment gives best fatigue

The research aims to investigate the effects of GMAW or MIG welding process on the mechanical properties of dissimilar aluminum alloys 2024-T351 and AA 6061- T651. A series of experimental techniques have been conducted to evaluate mechanical properties of the alloys, by carrying out hardness, tensile and bending tests for welded and un-welded specimens.

Metal inert gas (MIG) has been carried out on sheet metal using ER- 4043(AlSi₅) as a filler metal and argon as shielded gas. The welded joints were tested by X-ray radiography and Faulty pieces were excluded.

Welding joints without defects are subjected to heat treatment including heating the joints in furnace to 170 °C for half an hour then air cooling to rel

Overlapped have been prepared from epoxy resin material added to carbon Nanotube and percentages weight (0.1, 0.05, 0.01) % Studied the mechanical properties of the composite (bending, tensile an d hardness) has been found that the Flexural and tensile modulus of the composites were higher than the pure epoxy resin this may be due to the high mechanical strength of carbon nano tube (CNT). The hardness of the epoxy carbon Nanotube composites increased and the reason is due to increased overlap and stacking between the additives and material basis, which reduces the movement of polymer molecules leading to increased resistance to scratching material and cutting, will become more resistance to plastic deformation.

  The present study was conducted on sixty five pregnant women that infected with    acute toxoplasmosis, serum samples were tested for detection specific anti-Toxoplasma gondii IgM using the rapid Toxo IgG/IgM Chromatographic immune assay test cassette and ELISA, and fifty healthy married women (not pregnant)  as  was considered as control group.       The level of serum IL-6, IL-8, IL-12, TNF-α, TGF-β1, IP-10, MIP-1, MIG and ICAM were significantly increased (P <0.005) in pregnant patients infected with acute toxoplasmosis, while serum level of MCP-1(14.46 ± 1.38pg/ml) was not significantly increased when compared to controls(11.25 ± 0.24pg/ml)  , these levels can be used as i