Background: the aim of this study was to evaluate the effect of different surface acids treatments (37%phospjoric acid, 5%hydrofluoric acid, 1.23 acidulated phosphate fluoride) of feldspathic ceramic VITA 3D MASTER , and the effect of thermocycling on shear bond strength using a ceramic repair kit (ivoclar/vivadent). Material and Methods: sixty Nickel-Chromium metal base plates were prepared(9mm diameter,3mm depth) using lost wax technique, 2mm thick layer of ceramic(VITA 3D MASTER) fused to metal plates, all specimens were embedded in acrylic resin blocks except their examined surfaces and divided into 3 main groups 20 specimens each, Grp A: treatment with 37%phosphoric acid for 2 mins, Grp B: etching with 5% hydrofluoric acid for 2mins, Grp C: etching with 1.23% acidulated phosphate fluoride for 10 mins; monobond-plus, heliobond, resin composite(Tetric EvoCeram) were applied to each specimen according to manufacturer's instruction using transparent split mold(5mm diameter, 4 mm height); specimens were stored in 37OC distilled water for 12 weeks, 10 specimens of each group were subjected to thermocycling between 5 oC and 55 o C for 800 cycles with 30s dwell time; shear bond strength was determined by a universal testing machine (instron 1122) at a cross head speed 0.5mm/min; One way ANOVA test, LSD test and student-t test were used to analyze shear bond strength. Results: Mean shear bond strength values for the tested groups were: A1= 11.65±0.68 Mpa, A2=10.88±0.58 Mpa, B1=17.93±0.41 Mpa, B2=17.42±0.35 Mpa, C1=15.17±0.61 Mpa, C2=14.51±0.48 Mpa ; one way ANOVA test showed highly significant difference among groups; LSD test revealed that the use of 5% HF for ceramic surface treatment(GB) was highly significant than the treatment with 37%PA(GA) or 1.23%APF(GC) respectively and the use of 1.23%APF(GC) was highly significant than the use of 37%PA(GA); Student t- test showed a significant difference between subgroups of the same group with and without thermocycling. Conclusion: ceramic surface treated with 5% HF acid for 2 mins recorded the highest shear bond strength, followed by surface treatment with 1.23% APF for 10 mins, most specimens treated with 5%HF showed cohesive failure with in ceramic while specimens treated with 1.23%AFP showed more (adhesive/cohesive) failure than adhesive or cohesive alone, and specimens treated with 37% PA showed nearly 50:50 adhesive and combination failure, thermocycling reduced the bond strength of each group significantly
In this research prepared two composite materials , the first prepared from unsaturated polyester resin (UP) , which is a matrix , and aluminum oxide (Al2O3) , and the second prepared from unsaturated polyester resin and aluminum oxide and copper oxide (CuO) , the two composites materials (Alone and Hybrid) of percentage weight (5,10,15)% . All samples were prepared by hand layup process, and study the electrical and thermal conductivity. The results showed decrease electrical conductivity from (10 - 2.39) ×10-15 for (Up+ Al2O3) and from (10 - 2.06)×10-15 for (Up+ Al2O3+ CuO) .But increase thermal conductivity from( 0.17 - 0.505) for (Up+ Al2O3) and from (0.17 - 0.489) for (Up+ Al2O3+ CuO).
(12)
(6)
In this work, results from an optical technique (laser speckle technique) for measuring surface roughness was done by using statistical properties of speckle pattern from the point of view of computer image texture analysis. Four calibration relationships were used to cover wide range of measurement with the same laser speckle technique. The first one is based on intensity contrast of the speckle, the second is based on analysis of speckle binary image, the third is on size of speckle pattern spot, and the latest one is based on characterization of the energy feature of the gray level co-occurrence matrices for the speckle pattern. By these calibration relationships surface roughness of an object surface can be evaluated within the
... Show More
In this research, the effect of changing the flood level of Al-Shuwaija marsh was studied using the geographic information systems, specifically the QGIS program, and the STRM digital elevation model with a spatial analysis accuracy of 28 meters, was used to study the marsh. The hydraulic factors that characterize the marsh and affecting on the flooding such as the ranks of the water channels feeding the marsh and the degree of slope and flat areas in it are studied. The area of immersion water, the mean depth, and the accumulated water volume are calculated for each immersion level, thereby, this study finds the safe immersion level for this marsh was determined.
Many water supplies are now contaminated by anthropogenic sources such as domestic and agricultural waste, as well as manufacturing activities, the public's concern about the environmental effects of wastewater contamination has grown. Several traditional wastewater treatment methods, such as chemical coagulation, adsorption, and activated sludge, have been used to eliminate pollution; however, there are several drawbacks, most notably high operating costs, because of its low operating and repair costs, the usage of aerobic waste water treatment as a reductive medium is gaining popularity. Furthermore, it is simple to produce and has a high efficacy and potential to degrade pollu
... Show MoreIn the present work the Buildup factor for gamma rays were studied in shields from epoxy reinforced by lead powder and by aluminum powder, for NaI(Tl) scintillation detector size ( ×? ), using two radioactive sources (Co-60 and Cs-137). The shields which are used (epoxy reinforced by lead powder with concentration (10-60)% and epoxy reinforced by aluminum powder with concentration (10-50)% by thick (6mm) and epoxy reinforced by lead powder with concentration (50%) with thick (2,4,6,8,10)mm. The experimental results show that: The linear absorption factor and Buildup factor increase with increase the concentration for the powders which used in reinforcement and high for aluminum powder than the lead powder and decrease with inc
... Show More
The current specialized research tagged (intellectual and artistic concepts of the cultural context and their impact on contemporary ceramic sculpture) paves the way for the emergence of the context in ceramics active in life, so that this relationship will indicate the development and presence of ceramics or not and the volume of its circulation in the joints of the culture of the Arab recipient. As a result, the researcher collected scientific materials to serve the subject of the research in four chapters: Chapter One (General Methodological Framework) To clarify the problem of the research, the importance of the research to achieve benefit in higher education and education for scholars and teachers, while the research aims to revea
... Show More
Background: The PMMA polymer denture base materials are low mechanical properties, adaptation of the denture base to underlying tissue is important for retention and stability of denture. The aim of the study was toevaluate the effect of mixtureZrO2-Al2O3 nanoparticles on impact strength, transverse strength, hardness, roughness, denture base adaptation of heat cured acrylic resin denture base material. Materials and methods: One hundred (100) specimens were prepared, the specimens were divided into five groups (20 specimens to each) according to the test type, each group was subdivided in to two subgroups (control and experimental) each subgroup consist of 10 specimens, the experimental group included mixture of 2% (ZrO2-Al2O3ratio2:1) b
... Show MoreThe estimation of the amounts of Surface runoff resulting from rainfall in the water basins is of great importance in water resources management. The study area (Bahr Al-Najaf) is located on the western edge of the plateau and the southwestern part of the city center of Najaf, with an area of 2729.4 (km2). The soil and water assessment tool (SWAT) with ArcGIS software was used to simulate the runoff coming from the three main valleys (Kharr (A and B)), Shoaib Al-Rahimawi, and Maleh), that contribute the flow to the study area. The results of the model showed that the SWAT software was successfully simulating the flow conditions based on the coefficient of determination (R2), the Nash coefficient (NS
... Show More
(1)
The adsorption of Malonic acid, Succinic acid, Adipic acid, and Azelaic acid from their aqueous solutions on zinc oxide surface were investigated. The adsorption efficiency was investigated using various factors such as adsorbent amount, contact time, initial concentration, and temperature. Optimum conditions for acids removal from its aqueous solutions were found to be adsorbent dose (0.2 g), equilibrium contact time (40 minutes), initial acids concentration (0.005 M). Variation of temperature as a function of adsorption efficiency showed that increasing the temperature would result in decreasing the adsorption ability. Kinetic modeling by applying the pseudo-second order model can provide a better fit of the data with a greater correla
... Show More
(12)
(3)
In this paper, magnesium oxide nanoparticles (MgO NPS) have been prepared and characterized and its concentration effect has been studied on polymers surface (MgO NPS). The results showed that the degradation of poly methyl methacrylate increased when using such metal oxide. The results also showed that the metal oxide increased the degradation of poly methyl methacrylate. X-ray diffraction, scanning electron microscopy, atomic force microscopy were used to study the morphological characteristics and size of nano MgO particles analysis. Films were prepared by mixing the different masses of MgO NPS (0.025, 0.05, 0.1, 0.2 and 0.4) % with a polymer solution ratio (W/V) 7 %. Photo-
... Show More
(1)