Polymer composites were prepared using epoxy resin (EP) and unsaturated polyester (UPE) as a blend matrices, which were mixed together in different percentages (starting from 90:10) of (epoxy/polyester) respectively, and ending with (50:50) of (epoxy/polyester). The optimum mixing ratio (OMR) of the components was decided upon the results of the impact strength value of these blending ratio, which showed the highest value of (16.3) KJ/m2 for the blending ratio (80:20) of (EP/UPE) respectively.
The blend with (OMR) was chosen to be reinforced with three different weight fractions of reinforcement; the 1st one was reinforced with nano titanium oxide (TiO2) with a weight fraction (2% wt.), the 2nd one was reinforced with both nano (TiO2) and surface modified nano silica particles (SiO2) with weight fractions (2% & 0.5%) respectively, and the 3rd one was reinforced with nano (TiO2) and surface modified (SiO2) with weight fractions (2% & 1%) respectively. The tested mechanical properties were (flexural strength, impact strength, hardness, and water uptake).
Hand lay-up technique was used to prepare the samples, and a magnetic stirrer was used to ensure maximum homogeneity of the nano particles in the blend. All fabricated samples were exposed to water for 10 weeks to investigate the effect of nano powders addition on diffusivity and maximum water uptake, obvious degradation in mechanical properties of the composite consisting of (blend matrix/TiO2 reinforcement) and (blend matrix/TiO2+SiO2 reinforcement) were observed as a result of liquid uptake with less severe impact, but more effect on flexural strength and shore D hardness. Fick’s 2nd law was used to explain diffusion mechanism. All the results were discussed.
CuAlTe2 thin films were evaporation on glass substrates using the technique of thermal evaporation at different range of thickness (200,300,400and500) ±2nm. The structures of these films were investigated by X-ray diffraction method; showing that films possess a good crystalline in tetragonal structure. AFM showed that the grain size increased from (70.55-99.40) nm and the roughness increased from (2.08-3.65) nm by increasing the thickness from (200-500) nm. The optical properties measurements, such as absorbance, transmtance, reflectance, and optical constant as a function of wavelength showed that the direct energy gap decreased from (2.4-2.34) eV by the gain of the thickness.
(1)
In the current research, we investigated the absorption spectrum for R590 and C480 dyes in ethanol solvent for different dye solution concentrations of 10-4, 10-5 and 10-6M. These dyes have been prepared and studied before and after gamma irradiation (first, second ionization) using cesium-137 source with absorbed doses of 18.36 Gy (time exposure of 10 days) and 73.44 Gy (with time exposure of 40 days). We noticed that the absorption intensity was decreased with decreasing concentration, before gamma irradiation while the absorption spectrum peak shifted towards the short wavelength (blue shift). It was also found that the intensity of absorption spectrum increased and shifted the absorption spectrum peak towards the long wavelength (red
... Show More
In this investigation , borax (B) (additive I) and chlorinated paraffin (CP.) (additive II) ,were used as flame retardants for each of epoxy and unsaturated polyester resins in the weight ratios of 2,4,6, & 8% by preparing films of (130×130×3) mm dimensions. Also films of these resins with a mixture of [50%(B.)+50%(CP.)] (additive III) in the same weight ratios were prepared in order to study the synergistic effect of these additives on the flammability of the two resins . Three standard test methods were used to measure the flame retardation which are : 1-ASTM : D-2863 2-ASTM : D-635 3-ASTM : D-3014
... Show More
The varied applications of polystyrene in various fields of life led to examining the cause of radiation influence on some rheological behavior of commercial Polystyrene (PS) solution in the chloroform (CHCl3) solvent. Polystyrene grains shape samples were irradiated using the radioactive element Cesium- 137 with (9 µci) activity for 10, 20, and 30 minutes. The viscosity of the polymer solution depends on the concentration and size (i.e. molecular weight) of the dissolved polymer. Experimental data showed that the radiation dose affected the value of viscosity (shear, relative, specific, and reduced). The viscosity value significantly reduced at 10 min radiation dose and when increasing the dose, the viscosity value increased
... Show More
(2)
(2)
This research of using Feldspar in the production self compacting concrete (SCC) ( 5,10,15 )% as partial replacement by weight of cement .In this research some of fresh properties of SCC ( slump flow used V-funnel test and filling ability used ( U- box test ) for concrete mixes and also some of the harden properties of SCC ( compressive and flexural tests ). The research results showed that negative effect of Feldspar on the fresh properties of self compacting concrete but the positive effect of Feldspar on the harden properties of self compacting concrete .
Conducted Althilelat chemical models of crude oil back to the reservoir Fertile from the fields of Baghdad and Kut and models of crude oil back to the reservoir ??????? of Haklbe Tikrit and Baghdad were calculated their properties Alvezaúah Kalkthaqh and weight, quality and degree of August j (API) and know the quality Nfothma that was light or heavy and make the comparison between Alinvtin also conducted chemical analyzes of the two models of Almia associated with each of the oil above Almkmnin and measured Ktvthma and Zojithma and concentrations of some dissolved salts in them and clarify the relationship between the oil reservoir and water associated with oil fields...
(3)
the films of cdse pure and doped with copper ratio glass substrate effect od cucomcentration technique thikness doped with copper is an anonmg and the density of state increases
(67)
(66)
(29)
(20)