Zinc oxide films (ZnO) are prepared by an electrolysis technique and without vacuum and then annealed atvarious temperatures (300,400,500)^OC for an hour. The structural analysis performed by X-Ray diffraction (XRD) shows,dominant orientation of this films is plane (101), has a hexagonal structure and  polycrystalline pattern and it was is found that the crystal size increases(24,29) nm at annealing temperatures (300, 400)° C, but the crystal size decreases to (20 nm) at annealing temperature (500 ° C). As the results of a surface nature study of these films showed by examining the atomic force microscope (AFM), the grain  size increases from (60.79 to 88.11) nm, and the surface roughnes

Tin oxide films (SnO2) of thickness (1 ?m) are prepared on glass substrate by post oxidation of metal films technique. Films were irradiated with Nd:YAG double frequency laser of wavelength (532 nm) pulses of three energies (100, 500, 1000) mJ. The optical absorption, transmission, reflectance, refractive index and optical conductivity of these films are investigated in the UV-Vis region (200-900) nm. It was found that the average transmittance of the films is around (80%) at wavelength (550 nm) and showed high transmission (? 90 %) in the visible and near infrared region. The absorption edge shifts towards higher energies, which is due to the Moss-Burstien effect and it lies at (4 eV). The optical band gap increased with increasing of ene

a-Ge: As thin films have prepared by thermal evaporation teclmique, then they were annealing at various temperatures within the

range (373-473)  K.   The  result of  X-ray di ffraction spectrum  was showing  that  all  the  specimens  remained  in  amorphous structure before and after annealing  process. This paper studied the effect of annealing  temperature as  a  function of  wavelength on  the optical energy gap and optical constants for the a-Ge:As thin  films . Results have showed that there was an increasing in the optical energy gap

{Egopt) values with the in ,;rcasing of the annealing temperatures within

In this paper, the fundamental harmonic of a Nd:YAG laser (Q-switched 1064nm wavelength, 1 Hz repetition rate and 9 ns pulse duration) has been used for the ablation of cadmium samples in air at atmospheric pressure and the generation of the cadmium plasma. The experimentally observed lines of cadmium plasma emission have been used to calculate the plasma parameters such as (electron temperature (TReR), electron density (nReR), Debye length (λRDR) and plasma frequency (ωRpR)). Line pair ratio of neutral species have been used for the electron temperature and electron density measurements. Plasma parameters were studied as a functions of laser pulse energy.

The pure and Sb doped GeSe thin films have been prepared by thermal flash evaporation technique. Both the structural and optical measurement were carried out for as deposited and annealed films at different annealing temperatures.XRD spectra revealed that the all films have one significant broad amorphous peak except for pure GeSe thin film which annealed at 573 K, it has sharp peak belong to orthorhombic structure nearly at 2θ=33o. The results of the optical studies showed that the optical transition is direct and indirect allowed. The energy gap in general increased with increasing annealing temperature and decreased with increase the ratio of Sb dopant. The optical parameters such as refractive index, extinction coefficient and real and

The pure and Sb doped GeSe thin films have been prepared by thermal flash evaporation technique. Both the structural and optical measurement were carried out for as deposited and annealed films at different annealing temperatures.XRD spectra revealed that the all films have one significant broad amorphous peak except for pure GeSe thin film which annealed at 573 K, it has sharp peak belong to orthorhombic structure nearly at 2θ=33o . The results of the optical studies showed that the optical transition is direct and indirect allowed. The energy gap in general increased with increasing annealing temperature and decreased with increase the ratio of Sb dopant. The optical parameters such as refractive index, extinction coefficient and r

Pulsed laser deposition (PLD) technique was applied to prepared Chromium oxide (Cr₂O₃) nanostructure doped with Titanium oxide (TiO₂) thin films at different concentration ratios 3,5,7 and 9 wt % of TiO₂. The effect of TiO₂ dopant on the average size of crystallite of the synthesized nanostructures was examined by X-ray diffraction. The morphological properties were discussed using atomic force microscopy(AFM). Observed optical band gap value ranged from 2.68 eV to 2.55 eV by ultraviolet visible(UV-Vis.) absorption spectroscopy with longer wave length shifted  in comparison with that of the bulk Cr₂O₃ ~3eV. This indicated that the synthesized samples a

Polycrystalline Indium oxide (In2O3) and Indium oxide-zinc oxide (IZO) thin films mixed with 10% ZnO content were prepared by spray-pyrolysis technique at relatively low substrate temperature (150 ˚C).Field emission scanning electron microscope (FE-SEM) shows that the nanostructure at 10% ZnO content has pyramid like structure. The hall effect measurements show that the prepared samples have n-type charge carriers .The films were examined as gas sensor against H2S gas at different operating temperatures (200, 250 and 300) oC, and it was found that the IZO sample a good sensitivity to H2S gas ~ 572 % at operating temperature 200 oC, with relatively fast response time of 19 s and recovery time of 17

     In this study, cadmium oxide (CdO) was deposited on glass bases by thermal chemical spraying technique at three concentrations (0.05, 0.1, 0.15) M and then was irradiated by CO₂ laser with 10.6 μm wave length and 1W power. The results of the atomic force microscope AFM test showed that the surfaces of these CdO thin films were homogenous and that the laser irradiated effect resulted in decreasing the roughness of the surface as well as the heights of the granular peaks, indicating a greater uniformity and homogeneity of the surfaces. The optical properties were studied to determine laser effect. The results of optical tests of these thin films showed that the photoluminescence spectra and absorption s