Polyaniline organic Semiconductor polymer was prepared by oxidation polymerization by adding hydrochloric acid concentration of 0.1M and potassium per sulfate concentration of 0.2M to 0.1M of aniline at room temperature, the polymer was deposited at glass substrate, the structural and optical properties were studies through UV-VIS, IR, XRD measurements, films have been operated as a sensor of vapor  H₂SO₄ and HCl  acids.

The use of Conservatism  significant impacts on the financial statements and thus on financial reporting which is produced by these lists so Rate Some of the professionals that the principle of accounting while Rate of others as a constraint, and brought this category based on the uses of this restriction sometimes used the accountant this restriction and especially with the uncertainties in the Sometimes it may collide with some of the cases in which the accountant may be forced to leave in custody as a result of emergence of economic events that gave rise to rights or future commitments should be disclosed.

The emergence in custody mainly was due to the uncertainty and its essence is to report on a

Structural and optical properties of CdO and CdO0.99Cu0.01 thin
films were prepared in this work. Cadmium Oxide (CdO) and
CdO0.99Cu0.01semiconducting films are deposited on glass substrates
by using pulsed laser deposition method (PLD) using SHG with Qswitched
Nd:YAG pulsed laser operation at 1064nm in 6x10-2 mbar
vacuum condition and frequency 6 Hz. CdO and CdO0.99Cu0.01 thin
films annealed at 550 C̊ for 12 min. The crystalline structure was
studied by X-ray diffraction (XRD) method and atomic force
microscope (AFM). It shows that the films are polycrystalline.
Optical properties of thin films were analyzed. The direct band gap
energy of CdO and CdO0.99Cu0.01 thin films were determined from
(αhυ)1/2 v

This study was conducted to determine the activity of plant Sesbania rostrata and two isolate from arbuscular mycorrhizae fungi (A,B) as a bioremediation of soil polluted by cadmium and lead elements in north and south of Baghdad city. The results showed that the average of soil pollution by cadmium and lead elements in north of Baghdad was less than the average of soil pollution in the south of Baghdad which recorded 10.0, 9.0 mg/kg and 27.0, 25.0 mg/kg respectively. The plant Sesbania recorded ability to accumulate the lead element in shoot system 19.65 mg/kg and in root system 27.2 mg/kg and for cadmium element 19.6, 24.6 mg/kg in shoot and root respectively. The results showed that the isolate A from soil pollution is more effected

Phenol oxidation by Fenton's reagent (H2O2 + Fe+2) in aqueous solution has been studied for the purpose of learning
more about the reactions involved and the extent of the oxidation process, under various operating conditions. An initial
phenol concentration of 100 mg/L was used as representative of a phenolic industrial wastewater. Working temperature
of 25C was tested, and initial pH was set at 5.6 . The H2O2 and the Fe+2 doses were varied in the range of
(H2O2/Fe+2/phenol = 3/0.25/1 to 5/0.5/1). Keeping the stirring speed of 200 rpm.
The results exhibit that the highest phenol conversion (100%) was obtained under (H2O/Fe+2/phenol ratio of 5/0.5/1)
at about 180 min. The study has indicated that Fenton's oxidation i

Physical adsorption by nitrogen gas was studied on seven commercial platinum reforming catalysts (RG-402, RG-412, RG-432, RG-451, RG 422,RG-482, PS-10), four prepared platinum catalysts (0.1%Pt/alumina, 0.2 %Pt/alumina, 0.45 %Pt/alumina and 0.55% Pt/alumina), and -alumina support. Physical adsorption was carried out by using Accelerated Surface Area and Porosimetry (ASAP 2400 device) at 77 K . The results indicate that the surface area in genaral decreases with increasing platinum percentage, high platinum loaded (0.45% and 0.55%) it was found that the percent increasing in surface area was lower than those obtained for low platinum loaded catalysts , and at very higher platinum loading 0.6 %Pt , some reduction in surface area was