In this paper, chip and powder copper are used as reinforcing phase in polyester matrix to form composites. Mechanical properties such as flexural strength and impact test of polymer reinforcement copper (powder and chip) were done, the maximum flexural strength for the polymer reinforcement with copper (powder and chip) are (85.13 Mpa) and (50.08 Mpa) respectively was obtained, while the maximum observation energy of the impact test for the polymer reinforcement with copper (powder and chip) are (0.85 J) and (0.4 J) respectively  

The aim of present work is to improve mechanical and fatigue properties for Aluminum alloy7049 by using Nano composites technique. The ZrO₂ with an average grain diameter of 30-40 nm, was selected as Nano particles, to reinforce Aluminum alloy7049 with different percentage as, 2, 4, 6 and 7 %. The Stir casting method was used to fabricate the Nano composites materials due to economical route for improvement and processing of metal matrix composites. The experimental results were shown that the adding of zirconium oxide (ZrO₂) as reinforced material leads to improve mechanical properties. The best percentage of improvement of mechanical properties of 7049 AA was with 4% wt. of ZrO₂ about (7.76% ) for ultim

   A reseach is carried out by using Alumina material type α-Al2O3 which has partical size 63μm doped with different percentage weight of MgO (0.1%,0.3%and0.5%) and by using dry press method to prepare the samples ,A force press 50KN used and sintering to 1500oC with   soaking time  of  6 hours.        The physical properties were studied such as "Bulk density ,Porosity and water absorption "also the mechanical properties such as (hardness,compressive strength ), the result shows that the best ratio of maginsa(MgO) added to Alumina (Al2O3)is 0.5%and this  worked to improve   Physical and mechanical properties .

Piroxicam is a non-steroidal anti-inflammatory drug (NSAID) used in the treatment of musculo-skeletal and joint disorders. The problem with this drug is its poor solubility in water and hence poor bioavailability after oral administration. In order to improve its solubility and dissolution behavior, hydrophilic additives such as starch, lactose, superdisintegrants including crospovidone (C.P), cross carmellose sodium (CCS), and sodium starch glycolate (SSG) were physically dry mixed with the drug by simple trituration. The improvement in the solubility in 0.1 N HCl was obtained as the amount of starch or lactose increased in the physical mixture, while for superdisintegrants, they further improve the solubility when they are present in s

In this study, gold nanoparticle samples were prepared by the chemical reduction method (seed-growth) with 4 ratios (10, 12, 15 and 18) ml of seed, and the growth was stationary at 40 ml. The optical and structural properties of these samples were studied. The 18 ml seed sample showed the highest absorbance. The X- ray diffraction (XRD) patterns of these samples showed clear peaks at (38.25^o, 44.5^o, 64.4^o, and 77.95^o). The UV-visible showed that the absorbance of all the samples was in the same range as the standard AuNPs. The field emission-scanning electron microscope (FE-SEM) showed the shape of AuNPs as nanorods and the particle size between 30-50 nm. Rhodamine-610 (RhB) was prepared at 10<

Purpose This study investigated periodontal ligament (PDL) restoration in osseointegrated implants using stem cells. Methods Commercial pure titanium and zirconium oxide (zirconia) were coated with beta-tricalcium phosphate (β-TCP) using a long-pulse Nd:YAG laser (1,064 nm). Isolated bone marrow mesenchymal cells (BMMSCs) from rabbit tibia and femur, isolated PDL stem cells (PDLSCs) from the lower right incisor, and co-cultured BMMSCs and PDLSCs were tested for periostin markers using an immunofluorescent assay. Implants with 3D-engineered tissue were implanted into the lower right central incisors after extraction from rabbits. Forty implants (Ti or zirconia) were subdivided according to the duration of implantation (healing period: 45 o