The dielectric permittivityεand ac conductivityσac of CuInSeTe thin films were measured at temperatures in the range of 303–453 K and frequencies in the range of 100 Hz–10 MHz. It is found that the ac activation energy estimated from the Arrhenius equation is 0.1004 eV which increases with substrate temperature and decreases with the increase of frequency. The exponentsshows a progressive increase withTs. The results are explained in terms of structural difference by the effect ofTs and thermal treatment.

New Schiff base ligand (E)-6-(2-(4-(dimethylamino)benzylideneamino)-2-(4-hydroxyphenyl)acetamido)-3,3- dimethyl-7-oxo-4-thia-1- azabicyclo[3.2.0]heptane-2-carboxylic acid = (HL) was synthesized via condensation of Amoxicillin and 4(dimethylamino)benzaldehyde in methanol. Figure -1 Polydentate mixed ligand complexes were obtained from 1:1:2 molar ratio reactions with metal ions and HL, 2NA on reaction with MCl2 .nH2O salt yields complexes corresponding to the formulas [M(L)(NA)2Cl],where M=Fe(II),Co(II),Ni(II),Cu(II),and Zn(II), A=nicotinamide .

The (E)-4-chloro-N-(2-(dimethylamino)ethyl)-5-((8-hydroxy quinolin-5-yl)diazenyl)-2-methoxybenzamide azo ligand (L) has been synthesized through the reaction of diazonium salt for 5-amino-4-chloro-N-(2-(dimethylamino) ethyl)-2-methoxybenzamide with 8-hydroxyquinoline and identified azo ligand (L) using spectroscopic studies (FTIR, UV-Vis, 1H and 13CNMR, mass), and micro-elemental analysis (C.H.N). Metal chelates of Co(II), Ni(II), Cu(II), as well as Zn(II) have been completed as well as characterized using mass spectra, flame atomic absorption, elemental analysis (C.H.N), infrared, UV-Vis spectroscopy, as well as conductivity, magnetic measurements. The metal-to-ligand ratio in all complexes, as determined by analytical data, was 1:2 and ex

Nano γ-Al₂O₃ support was prepared by co-precipitation method by using different calcination temperatures (550, 600, and 750) ^oC. Then nano NiMo/γ-Al₂O₃ catalyst was prepared by impregnation method were nickel carbonate (source of Ni) and ammonium paramolybdate (source of Mo) on the best prepared nano γ-Al₂O₃ support at calcination temperature 550 ^oC. Make the characterizations for prepared nano γ-Al₂O₃ support at different temperatures and for nano NiMo/γ-Al₂O₃ catalyst like X-ray diffraction, X-ray fluorescent, AFM, SEM, BET surface area, and pore volume.

The N

Ag-doped NiO thin films were fabricated by dip coating and subsequently annealed at 373, 473, 573, and 673 K to elucidate the influence of annealing temperature on their structural, morphological, optical, and NO2-sensing characteristics. X-ray diffraction confirmed the formation of polycrystalline Ag/NiO films, with progressively improved crystallinity and larger crystallite size at elevated annealing temperatures. Atomic force microscopy revealed a homogeneous surface morphology with grain growth, with the average grain diameter increasing from 26.40 to 34.2 nm. Optical analysis showed high visible-region transmittance (65–70%) and a gradual reduction in the optical band gap from 2.75 to 2.07 eV with increasing annealing temperature. Ga

This paper presents the electrical behavior of the top contact/ bottom gate of an organic field-effect transistor (OFET) utilizing Pentacene as a semiconductor layer with two distinctive gate dielectric materials Polyvinylpyrrolidone (PVP) and Zirconium oxide (ZrO2) were chosen. The influence of the monolayer and bilayer gates insulator on OFET performance was investigated. MATLAB software was used to simulate and determine the electrical characteristics of a device. The output and transfer characteristics were studied for ZrO2, PVP and ZrO2/PVP as an organic gate insulator layer. Both characteristics show a high drain current at the gate dielectric ZrO2/PVP equal to -0.0031A and -0.0015A for output and transfer characteristics respectively