This work was conducted to study the recovery of catalyst and desirable components from tar formed in phenol production unit and more particularly relates to such a method whereby better recovery of copper salts, phenol, benzoic acid and benzoate salts from tar by aqueous acid solution was accomplished.
The effect of solvent type, solvent concentration (5, 10, 15, 20, 25 and 30 wt%), agitation speed (100, 200, 300 and 400 rpm), agitation time (5, 10, 15, 20 and 25 min), temperature (90, 100, 110, 120, 130 and 140 oC) , phase ratio (1/1, 2/1, 3/1, 4/1 and 5/1) and number of extraction (1, 2, 3, 4, and 5) were examined in order to increase the catalyst and desirable components extraction.
Four types of solvent were used; hydrochloric

                In this investigation a high density polyethylene (HDPE) was used as a substitute to polyvinylchloride in the production of lead acid battery separators. This has been achieved by preparing mixtures of different percentages of the feed materials which include a high density polyethylene (HDPE) locally produced, filler materials such as silica and oils such as dioctylphthalate (DOP) or paraffin which were added to the mixture to improve the final properties of the separator. The materials were compounded by two roll-mills under the same conditions. The following parameters are involved:           &nb

The limitations of conventional cement mortar as a widely used construction material include low tensile capacity, high permeability, and susceptibility to chemical degradation. The increasing demand for durable and sustainable construction materials has led to increased attention in modifying cementitious materials through nanotechnology. This study investigates the influence of nano-silica (NS) and nano-alumina (NA) on the physical, strength-related, and durability characteristics of cement mortar to determine the optimum nanomaterial type and dosage for performance enhancement. Six mortar mixes, in addition to a reference mix, were designed and prepared by adding 1%, 1.5%, and 2% of the cement weight with NS and NA separately, an

The limitations of conventional cement mortar as a widely used construction material include low tensile capacity, high permeability, and susceptibility to chemical degradation. The increasing demand for durable and sustainable construction materials has led to increased attention in modifying cementitious materials through nanotechnology. This study investigates the influence of nano-silica (NS) and nano-alumina (NA) on the physical, strength-related, and durability characteristics of cement mortar to determine the optimum nanomaterial type and dosage for performance enhancement. Six mortar mixes, in addition to a reference mix, were designed and prepared by adding 1%, 1.5%, and 2% of the cement weight with NS and NA separately, an

This research aims to examine the role of global green finance as a critical driver of both economic and environmental sustainability within small and medium-sized agricultural enterprises (SMEs) in Iraq. Utilizing a convergent mixed-methods framework, the study integrates qualitative interviews with key stakeholders and a quantitative survey of 300 agricultural SMEs to assess the barriers, enablers, and institutional conditions influencing the adoption of green finance. The findings indicate that, despite growing awareness and substantial latent demand for sustainability-linked investments, adoption is significantly constrained by institutional fragmentation, regulatory ambiguity, and resource limitations at the firm level. Grounded in Ins

Image quality has been estimated and predicted using the signal to noise ratio (SNR). The purpose of this study is to investigate the relationships between body mass index (BMI) and SNR measurements in PET imaging using patient studies with liver cancer. Three groups of 59 patients (24 males and 35 females) were divided according to BMI. After intravenous injection of 0.1 mCi of 18F-FDG per kilogram of body weight, PET emission scans were acquired for (1, 1.5, and 3) min/bed position according to the weight of patient. Because liver is an organ of homogenous metabolism, five region of interest (ROI) were made at the same location, five successive slices of the PET/CT scans to determine the mean uptake (signal) values and its standard deviat

   AlPO₄ solid acid catalyst was prepared in order to use it in transesterification reaction of edible oil after supporting it with tungsten oxide. The maximum conversion of edible oil was obtained 78.78% at catalyst concentration (5gm.), temperature 70°Ϲ, 30/1 methanol/edible oil molar ratio, and time 5hr. The study of kinetics of the transesterification reaction of edible oil indicates that the reaction has an order of 3/2, while the value of activation energy for  transesterification reaction is 51.367 kJ/mole and frequency factor equal 26219.13(L/ mol.minute).

The crystalline zeolite, namely faujasite type Y with SiO2/Al2O3 mole ratio of 5 was used as raw material for preparation of isomerization catalysts. A 0.5 wt % Pt/HY-zeolite catalyst was prepared by impregnation of the decationized HY-zeolite with chloroplatinic acid. The dectionized HY-zeolite was treated with HCl, HNO3 and HI promoters using different normalities and with different concentrations of Sn, Ni and Ti promoters by impregnation method to obtain acidic and metallic promoters' catalysts, respectively. A 0.5 wt% of Pt was added to above catalysts using impregnation method. Isomerization of n-hexane was carried out at different prepared catalysts. The isomerization temperature varied from 250–325° C over weight hourly space

AlPO4 solid acid catalyst was prepared in order to use it in transesterification reaction of edible oil after supporting it with tungsten oxide. The maximum conversion of edible oil was obtained 78.78% at catalyst concentration (5gm.), temperature 70°Ϲ, 30/1 methanol/edible oil molar ratio, and time 5hr. The study of kinetics of the transesterification reaction of edible oil indicates that the reaction has an order of 3/2, while the value of activation energy for  transesterification reaction is 51.367 kJ/mole and frequency factor equal 26219.13(L/ mol.minute).