Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

EP/ metal composites were prepared as adhesives between two steel rods. Epoxy resin (EP) was used as a matrix with metal as fillers (Al, Cu, Fe,).
The preparation method for tensile adhesion tests includes two steel rods with adhesive composites between the rods to measure adhesion strength Sad and adhesion toughness Gad.
Results of tensile adhesion tests show that EP/ metals composite have maximum strength Sad for certain weight percentage of metals 2.95 and 9MPa at 10% for EP/Al and EP/Cu composite and 8.2MPa at 40% for EP/Fe composites

Background: The marginal seal is essential for sealant success because penetration of bacteria under the sealant might allow caries onset or progression. The aim of the present study was to estimate and compare the microleakage of pit and fissure sealant after various methods of occlusal surface preparation. Materials and methods: Thirty non-carious premolars extracted for orthodontic reasons were equally divided into three groups. In group one, occlusal fissures were opened with round carbide bur, in group two, occlusal surfaces of the teeth were cleaned with a dry pointed bristle brush and samples of group three were cleaned with a slurry of fine flour of pumice in water using rubber cup. Then fissures of all teeth were etched using 35% p

The love of the world and its lusts are the head of sins and the corruptors of religion, and the one who loves and loves them who prefers them over the hereafter is one of the most pitiful of creation, and the least intelligent of them, as he prefers imagination over reality, sleep over wakefulness, fleeting shadow over eternal bliss and the mortal abode over the eternal abode, and he sold the life of eternity for the most luxurious life. In life, it is dreams and sleep or as a fleeting shadow, and as it was said: The intelligent person is not deceived.
The reason for choosing this topic is due to two things:
The first: When I contemplated the reasons for the differences and conflicts that afflicted our wounded and occupied country

with an organized propaganda campaign. This military campaign was helped to formulate its speech by many institutions, research centers, and knowledge and intelligence circles in order to mobilize public opinion gain supporters and face the opponents by different means depending on a variety of styles to achieve its required effects. 
          After the US occupation of Iraq, US media fighters sought to influence the Iraqi public opinion and making them convinced them of the important presence of US military forces in Iraq which necessitated finding its justification through the use of persuasive techniques in its intensive propaganda campaigns. 
  This research discusses the most important

Four antimony compounds were used in this inves as additives to retard combustion of unsaturated polyester and epoxy resins, namely: 1. Tetraethyl ammonium tribromoethylantimonates (additive I). 2. Tetraethyl ammonium chlorodibromoethylantimonates (additive II). 3. Tetraethyl ammonium trichloroethylantimonates (additive III). 4. Tetraethyl ammonium bromodichloroethylantimonates (additive IV). The effects of these additives on flammability of unsaturated polyester and epoxy resins have been studied by using sheets of the resins with weight percentages of (0.5,1.0,1.5,2.0,2.5&3.0%) of the additives in dimensions of (150 X150X3)mm .Three standard test methods were used to measure the flame retardation which are: (ASTM:D -2863), (ASTM:D-635

The study was conducted during the spring season of 2000 and2001. The objective was to study the changes in leaves number of sunflower plants and its leaf area during growth stages under hardening conditions to drought tolerance. Agricultural practices were made according to recommendations.Asplit-split plots design was used with three replications.The main plots included irrigation treatments:irrigation to100%(full irrigation),75and50%of available water.The sub plots were the cultivars Euroflor and Flame.The sub-sub plots represented four seed soaking treatments:Control(unsoaking), soaking in water ,Paclobutrazol solution(250ppm),and Pix solution(500ppm). The soaking continued for 24 hours then seeds were dried at room temperature

The objective of the work was to study the changes in height and stem diameter of sunflower plants during growth stages under hardening conditions to drought tolerance. Field experiments were carried out during the spring season of 2000 and2001. Agricultural practices were made according to recommendations.Asplit-split plots design was used with three replications.The main plots included irrigation treatments:irrigation to100%(full irrigation),75and50%of available water.The sub plots were the cultivars Euroflor and Flame.The sub-sub plots represented four seed soaking treatments:Control(unsoaking), soaking in water ,Paclobutrazol solution(250ppm),and Pix solution(500ppm). The soaking continued for 24 hours then seeds were dried at room

Abstract: Colloidal gold nanoparticles (ringworm Palm or in the form of paper willow) have been prepared from HAuCl4 containing aqueous solution by hot chemical reduction method. The colloidal gold nanoparticles were characterized by SEM, EDX, and UV-VIS absorption spectroscopy. It was found that the variation of reduction time from boiling point affects the size of the nanoparticles and also in chemical reduction approach the size of nanoparticles can be controlled by varying the amount of variation the volume of reductant material with respect to the volume of HAuCL4.