A particulate polymer composite material was prepared by reinforcing with the Aluminum Oxide (Al₂O₃) or Aluminum (Al) metallic particles with a particle size of (30) µm to an unsaturated Polyester Resin with a weight fraction of (5%, 10%, 15%, 20%).

Tensile test results showed the maximum value of elastic modulus reached (2400MPa.)  in the case of reinforcing with (Al) particles with weight fraction (20%) and (1500 MPa.)  in the case of reinforcing with (Al₂O₃) particles of the same weight fraction.

  When the impact and the flexural strength tests were done, the results showed that flexural strength (F.S), maximum shear stress (τ_max), impact strength

The wear behavior of alumina particulate reinforced A332 aluminium alloy composites produced by a stir casting process technique were investigated. A pin-on-disc type apparatus was employed for determining the sliding wear rate in composite samples at different grain size (1 µm, 12µm, 50 nm) and different weight percentage (0.05-0.1-0.5-1) wt% of alumina respectively. Mechanical properties characterization which strongly depends on microstructure properties of reinforcement revealed that the presence of ( nano , micro) alumina particulates lead to simultaneous increase in hardness, ultimate tensile stress (UTS), wear resistances. The results revealed that UTS, Hardness, Wear resistances increases with the increase in the percentage of

In the present study, the effects of brake pad particles of lung and liver histological sections were evaluated for (60) adult male mice. The animals were divided into three groups ( A,B,C) according to the periods of exposure (4, 8, and 12) weeks respectively exposed to brake pad particles in addition to the control groups (F) exposed to fresh air only. A special inhalation chamber designed locally has been used to expose the animals. The exposure to brake pad particles was (2.228) µg/m³ for 30 min/day, 5 days/week for (4,8and12) weeks respectively.

The examination in group (A) of the histological sections of the lung showed the thickness of interalveolar septa.  Also, a congestion of alveolar capillary was marked indicat

In this study, the consequences of treatment with brake pad particles on kidney and spleen were evaluatedthrough microscopic anatomy sections for 60 male albino mice. The animals were divided into six groups, the first three groups (A,B,C)  were exposed to brake pad particles depending on periods of exposure (4, 8, and 12weeks, respectively), while the other three groups were control groups,designated asF, which were exposed to laboratory fresh air only. A special locally-designed inhalation chamber was used to expose the animals. The exposure dose to brake pad particles (total suspended particles) was 2.228 µg/m³ for 30 min/day, 5 days/week,4, 8 and 12 weeks.The statistical analysis showed that the weights of organs for both

Oryza sativa japonica (ofada rice) is largely grown in Aramoko, Abakaliki and Ofada are communities and consumed by both the poor and rich in Nigeria. A total of twenty ofada rice farmlands were identified in each study area and rice samples were randomly collected, thoroughly mixed to make a representative sample from each farmland. Soil samples were collected in each farm to a depth of 5-15cm from at least eight different points and thoroughly mixed together to form a representative sample. The samples were thereafter taken to the laboratory for preparation and spectroscopic analysis. A well-calibrated NaI(Tl) gamma-ray detector was used in spectrometric analysis of the samples and descriptive statistics was used to analyze th