Corrosion- induced damage in reinforced concrete structure such as bridges, parking garages, and buildings, and the related cost for maintaining them in a serviceable condition, is a source of major concern for the owners of these structures.
Fly ash produced from south Baghdad power plant with different concentrations (20, 25 and 30) % by weight from the cement ratio were used as a corrosion inhibitor as a weight ratio from the cement content.
The concrete batch ratio under study was (1:1.5:3) cement, sand and gravel respectively which is used in Iraq. All the raw materials used were locally manufactured.
Concrete slabs (250x250x70) mm dimensions were casted, using Poly-wood molds. Two steel bars were embedded in the central position of each slab at the mid- height (about 35 mm), with a space of 100 mm between each other.
A 16 concrete slabs were prepared (0, 20, 25 and 30) wt. % of fly ash. The specimens were partially immersed in 3.5 wt. % NaCl solution in order to predict the corrosion.
Half-cell potential test technique was used to estimate the corrosion rate which is occurred in the steel bar due to the migration of chloride ions through the concrete, depending on the ASTM C876-08.
The result shows that the potential values of steel in concrete were shifts to the positive direction with increasing the percentage of fly ash, because the reduction of porosity by the addition of fly ash which fill the pores and inhibit the chloride ions to reach to steel.
The results also show that the further increase of fly ash (30%) the possibility of carbonation is increased which result in reduction its alkalinity, thereby permitting corrosion of embedded steel.
The study is based on the selective binding ability of the drug compound procaine (PRO) on a surface imprinted with nylon 6 (N6) polymer. Physical characterization of the polymer template was performed by X-ray diffraction and DSC thermal analysis. The imprinted polymer showed a high adsorption capacity to trap procaine (237 µg/g) and excellent recognition ability with an imprinted factor equal to 3.2. The method was applied to an extraction column simulating a solid-phase extraction to separate the drug compound in the presence of tinoxicam and nucleosimide separately and in a mixture of them with a recovery rate more than the presence of tinoxicam and nucleosimide separately and in a mixture of them with a recovery rate of more t
... Show More
(1)
(1)
The research aims to identify how to enhance the quality of the human resources, focusing on four dimensions (efficiency, effectiveness, flexibility, and reliability), by adopting an adventure learning method that combines theoretical and applied aspects at the same time, when developing human resources and is applied using information technology, and that Through its dimensions, which are (cooperation, interaction, communication, and understanding), as the research problem indicated a clear deficiency in the cognitive perception of the mechanism of employing adventure learning dimensions in enhancing human resources quality, so the importance of research was to present treatments and proposals to reduce this problem. To achieve
... Show More
Abstract:
The aim of this research is to highlight the importance of achieving customer satisfaction by using information technology and Internet networks in the process of purchasing flight tickets, and switching from the traditional method of purchasing and payment operations to the electronic method, to reduce the financial and non-financial risks associated with the traditional purchasing process, as well as saving time, effort and costs for the customer. The researcher used the deductive approach in linking the variables (achieving customer satisfaction and Internet of Things technology for booking electronic tickets)
... Show MoreThe purpose of this study was to investigate the difference in mandibular trauma caused by two mechanisms for the delivery of missile injuries: firearms and improvised explosive devices (IEDs). The data investigated included sex, age, mechanism of injury, and other clinical and radiographic manifestations. Seventy consecutive patients, predominantly male, with a mean age of 28.6 ± 14 years (range 2–60 years) were enrolled: 38 patients (54.3%) sustained mandibular fractures caused by bullet injuries and 32 patients (45.7%) had mandibular fractures caused by IED explosion injuries. The study revealed that the differences in most of the investigated variables were not statistically significant; the only significant differences were the inci
... Show More
(7)
(8)
Under cyclic loading, aluminum alloys exhibit less fatigue life than steel alloys of similar strength and this is considered as Achilles's heel of such alloys. A nanosecond fiber laser was used to apply high speed laser shock peening process on thin aluminum plates in order to enhance the fatigue life by introducing compressive residual stresses. The effect of three working parameters namely the pulse repetition rate (PRR), spot size (ω) and scanning speed (v) on limiting the fatigue failure was investigated. The optimum results, represented by the longer fatigue life, were at PRR of 22.5 kHz, ω of 0.04 mm and at both v's of 200 and 500 mm/sec. The research yielded significant results represented by a maximum percentage increase in the fa
... Show More
(3)
(1)
Background: The repair of bone defects remains a major clinical orthopaedic challenge. Bone is a highly vascularised tissue reliant on the close spatial and temporal connection between blood vessels and bone cells to maintain skeletal integrity. This study aimed to study the efficacy of Panax ginseng as a osteoinducer in tibia of rat and as a stimulator for bone healing and to study the immunohistochemical expression of osteonectin as bone formation markers in experimental and control groups during bone healing. Material and method: : In this study thirty albino male rats , weighting (200-300) gram ,aged (2-3) months ,will be used under control conditions of temperature ,drinking and food consumption. The animals will subject for an
... Show MoreIn the present work the Buildup factor for gamma rays were studied in shields from epoxy reinforced by lead powder and by aluminum powder, for NaI(Tl) scintillation detector size ( ×? ), using two radioactive sources (Co-60 and Cs-137). The shields which are used (epoxy reinforced by lead powder with concentration (10-60)% and epoxy reinforced by aluminum powder with concentration (10-50)% by thick (6mm) and epoxy reinforced by lead powder with concentration (50%) with thick (2,4,6,8,10)mm. The experimental results show that: The linear absorption factor and Buildup factor increase with increase the concentration for the powders which used in reinforcement and high for aluminum powder than the lead powder and decrease with inc
... Show More
Twelve species from Brassicaceae family were studied using two different molecular techniques: RAPD and ISSR; both of these techniques were used to detect some molecular markers associated with the genotype identification. RAPD results, from using five random primers, revealed 241 amplified fragments, 62 of them were polymorphic (26%).
ISSR results showed that out of seven primers, three (ISSR3, UBC807, UBC811) could not amplify the genomic DNA; other primers revealed 183 amplified fragments, 36 of them were polymorphic (20%). The similarity evidence and dendrogram for the genetic distances of the incorporation between the two techniques showed that the highest similarity was 0.897 between the va
... Show More
(3)
This study was aimed to estimate the influence of Conocarpus erectus L. residues, and some micronutrients on growth and production of potato. This research was conducted at one of the fields of the College of Agricultural Engineering Sciences - University of Baghdad. The experiment was implemented using factorial arrangement (4X3X3) within randomized complete block design with three replicates. Conocarpus fertilizer was represented the first factor with three levels (7.5, 15, 30 ton.ha-1), which symbolized (C2, C3, C4). Mineral fertilizer as recommended dose as a control, which symbolized (C1). The second factor was foliar spraying with three levels of iron (0, 100, 200 mg.L-1), which symbolized (F0, F1, F2). The third factor is fol
... Show More
(6)
(1)
Objective: to evaluate the results of (Modification of Russe method) in treatment of nonunion fracture scaphoid bone by bone graft with external splintage (plaster of paris cast (pop ). Methods:Prospective study done on 26 patients (24 male, 2 female), age range between 25-42 years (mean age 34 years), fracture site at middle 1/3 with minimal displacements with no carpal bone or radial bone injury, technique of Matte- Russe method (explore the bone through volar approach using bone graft from iliac crest (cortico-cancellous peg plus cancellus bone) with thumb spica for 90 days with period of follow up 12-18 months. Results: out of 26 patients treated by this method , 23 patients (88.5%) union was achieved radiologically by the end of 3rd mo
... Show More