Adsorption techniques are widely used to remove certain classes of pollutants from wastewater. Phenolic compounds represent one of the problematic groups. Na-Y zeolite has been synthesized from locally available Iraqi kaolin clay. Characterization of the prepared zeolite was made by XRD and surface area measurement using N2 adsorption. Both synthetic Na-Y zeolite and kaolin clay have been tested for adsorption of 4-Nitro-phenol in batch mode experiments. Maximum removal efficiencies of 90% and 80% were obtained using the prepared zeolite and kaolin clay, respectively. Kinetics and equilibrium adsorption isotherms were investigated. Investigations showed that both Langmuir and Freundlich isotherms fit the experimental data quite well. On the

Zeolite Y nanoparticles were synthesized by sol - gel method. Dffirent samples using two silica sources were prepared.
Sodium metasilicate (Na2SiO3) (48% silica) and silicic acid silica (H2SiO3) (75% silica) were employed as silica
source and aluminum nitrate (Al(NO3)3.9H2O) was the aluminum source with tetrapropylammonium hydroxide
(TPAOH) as templating agent.
The synihesized-samples were characterized by X-ray diffraction, showed the requirement of diffirent aging time for
complete crystallization to be achieved. Transmission Electronic Microscope (TEM) images, showed the particles were
in the same range of 30 - 75 nm. FT-IR spectroscory, showed the synthesized samples having the zeolite Y crystal
properties. The i

Aniline and its derivatives are common contaminants in various wastewaters and represent a serious worry for societies health and a challenge to ecologists due to their dangers effects on to the human health.

ZSM-5 zeolite was prepared from locally available materials (kaolin and rice husk) for adsorption of aniline from synthetic wastewater. Characterization of the prepared zsm-5, kinetics and thermodynamic of the adsorption process were investigated.

The characterization results of the prepared zsm-5 zeolite showed that the surface area was 270.1 m²/g and pore volume 0.21828 cm³/g. The silica to alumina ratio (Si/Al) was 166. 47 and the sodium content was 11 wt. %. The atomic force microscope (AFM)

Oro slippery tablets (OSTs) is a technique used to improve swallowing of tablets for patients with dysphagia. The aim of this study was to formulate irbesartan and hydrochlorothiazide as Oroslippery tablets (OST) containing 150 mg irbesartan and 25 mg hydrochlorothiazide for dysphagia patients. A simple and rapid method of analysis was developed and validated according to the ICH guideline using HPLC with UV detector. Tablets were prepared by direct compression and then coated with the slippery coat of three different concentrations of the slippering substance “xanthan gum’ (2%, 3% and 4%) in Opadry Colorcone® and evaluated according to USP. Slipperiness test was performed using Albino rabbits. Results showed that 2% xanthan gum gav

Faujasite type NaY zeolite catalyst was prepared from locally available kaolin, then the prepared NaY zeolite have been modified by exchanging of sodium ion with ammonium to produce NH4Y zeolite. NH4Y zeolite was converted to HY zeolite by ion exchanging with oxalic acid. Zinc and nickel promoters have been added to the prepared HY zeolite catalyst, and the effect of these promoters on the catalytic activity of the prepared HY catalyst was studied in fluid catalytic cracking process using light gas oil as a feedstock. The experimental results show that the promoted catalyst gives higher gas oil conversion and gasoline yield than HY zeolite catalyst at the same reaction temperature and WHSV. It was also found that the promoted catalyst gi

0

This work deals with the separation of benzene and toluene from a BTX fraction. The separation was carried out using adsorption by molecular sieve zeolite 13X in a fixed bed. The concentration of benzene and toluene in the influent streams was measured using gas chromatography. The effect of flow rate in the range 0.77 – 2.0 cm3/min on the benzene and toluene extraction from BTX fraction was studied. The flow rate increasing decreases the breakthrough and saturation times. The effect of bed height in the range 31.6 – 63.3 cm on benzene and toluene adsorption from BTX fraction was studied. The increase of bed height increasing increases the break point values. The effect of the concentration of benzene in the range 0.0559 – 0.2625g/