The inhibitive action of a blend of sodium nitrite/sodium hexametaphosphate (SN+SHMP) on corrosion of carbon steel in simulated cooling water systems (CWS) has been investigated by weight loss and electrochemical polarization technique. The effect of temperature, velocity, and salts concentrations on corrosion of carbon steel were studied in the absence and presence of mixed inhibiting blend. Also the effect of inhibitors blend concentrations (SN+SHMP), temperatures, and rotational velocity, i.e., Reynolds number (Re) on corrosion rate of carbon steel were investigated using Second-order Rotatable Design (Box-Wilson Design) in performing weight loss and corrosion potential approach. Electrochemical polarization measurements were used to study the behavior of carbon steel in different salts concentrations of (CWS) with pH = 7.5 in absence and presence of the inhibiting blend. The results show that the regression model (Box-Wilson Design) that has been developed using experimental data was used to verify that the interaction term of temperature with inhibitors blend and the square term of inhibitors blend are significant for corrosion rate in 0.05 N NaCl solution while the main variables are not pronounced. Also, it is found that the corrosion rate of carbon steel is increased with increasing temperature, rotational velocity, and NaCl salts concentration in uninhibited and inhibited solutions. Inhibition performance of NaNO2+ Na(PO3)6 was found to increase with its concentration up to 800 ppm inhibitors blend, and the corrosion potential is shifted to more positive direction with increasing rotational velocity, and inhibitor blend concentration.
The study aimed to test the hypothesis of Caldor to estimate the relationship between industrial production and GDP growth in Iraq using with Integration Framework and to determine the causal relationship in the short and long term using the error correction vector model for the period 1990-2016. the results showed a long-term equilibrium relationship between GDP and industrial output, while Ganger causality tests showed a causal relationship in the long run of GDP to output Subliminal thus illustrated the extent of the recession suffered by the industrial sector, which is supposed to be the driving force of the economy and the development and expansion of the productive base of the industry, so this study recommends attent
... Show More
For more than a decade, externally bonded carbon fiber reinforced polymer (CFRP) composites successfully utilized in retrofitting reinforced concrete structural elements. The function of CFRP reinforcement in increasing the ductility of reinforced concrete (RC) beam is essential in such members. Flexural and shear behaviors, ductility, and confinement were the main studied properties that used the CFRP as a strengthening material. However, limited attention has been paid to investigate the energy absorption of torsion strengthening of concrete members, especially two-span concrete beams. Hence, the target of this work is to investigate the effectiveness of CFRP-strengthening technique with regard to energy absorption of two-span RC
... Show More
(23)
(18)
(19)
(15)
(2)
This paper studies the behavior of reinforced Reactive Powder Concrete (RPC) two-way slabs under static and repeated load. The experimental program included testing six simply supported RPC two-way slabs of 1000 mm length, 1000 mm width, and 70 mm thickness. All the tested specimens were identical in their material properties, and reinforcement details except their steel fibers content. They were cast in three pairs, each one had a different steel fibers ratio (0.5 %, 1 %, and 1.5 %) respectively. In each pair, one specimen was tested under static load and the other under five cycles of repeated load (loading-unloading). Static test results revealed that increasing steel fibres volume fraction from 0.5 % to 1 % and from 1% to 1.5%,
... Show More
(12)
(3)
(3)
Static loads exposing to mechanical components can cause cracks, which are lead to form stress concentration regions causing the failure of structure. Generally, from 80% to 90% of structure failure is due to initiation of the cracks. Therefore, it is necessary to repair the crack and reduce its effect on the structure where the effect of the crack is modelled as an additional flexibility to the structure. In the last few years, piezoelectric materials have been considered as one of the most favourable repairing techniques. The piezoelectric material converts the applied voltage on it to a bending moment to counter the bending moment caused by the external load on the beam at the crack location. In this study, the design of the piez
... Show More