Catalytic Reforming of Iraqi Naphtha over Pt-Ti / HY Zeolite Catalyst
...Show More Authors

In the present work, zeolite Y has been synthesized successfully by sol-gel method.Zeolite was synthesized by crystallization of the final gel which consist from seeding and feed stock gels at  85 oC. HY zeolite was prepared by an ion exchange process with ammonium chloride solution and then loaded with different percentages of  platinum and titanium by the wet - impregnation method.

X-ray Diffraction (XRD), X-ray Florescence (XRF), Scanning Electron Microscopy (SEM), BET surface area and, Crushing strength were used to characterize the synthesized and prepared catalysts . Results showed high crystallinity  90%  with silica to alumina ratio 5 for HY, high surface area of 600 m2/g and pore volume of 0.38 cm3/g.

The activity of the prepared zeolite was investigated using a pilot plant unit for the catalytic reforming of Iraqi heavy naphtha. All prepared catalysts were investigated at temperatures of 490,500 and 510oC ,pressure of 20 bar, H2 /HC  ratio 3 and LHSV 1.4.hr-1.

Reformate was produced with 86 RON and 94% yield at 510ºC and 20 bar using 0.13 wt.% Pt - 0.75 wt.% Ti  loaded on synthesized HY.

View Publication Preview PDF
Quick Preview PDF
Publication Date
Sun Mar 30 2008
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Effect of Promoters on the Catalytic Activity of the Iosmerization Catalyst
...Show More Authors

The crystalline zeolite, namely faujasite type Y with SiO2/Al2O3 mole ratio of 5 was used as raw material for preparation of isomerization catalysts. A 0.5 wt % Pt/HY-zeolite catalyst was prepared by impregnation of the decationized HY-zeolite with chloroplatinic acid. The dectionized HY-zeolite was treated with HCl, HNO3 and HI promoters using different normalities and with different concentrations of Sn, Ni and Ti promoters by impregnation method to obtain acidic and metallic promoters' catalysts, respectively. A 0.5 wt% of Pt was added to above catalysts using impregnation method. Isomerization of n-hexane was carried out at different prepared catalysts. The isomerization temperature varied from 250–325° C over weight hourly space

... Show More
View Publication Preview PDF
Publication Date
Sat Oct 19 2024
Journal Name
Chemical Papers
Hydroisomerization of n-hexane over Pt/TiO2 catalysts
...Show More Authors

One of the most important processes to obtain gasoline with high octane numbers is isomerization. In this paper, Pt/TiO2 was prepared successfully by using the sol–gel method by hydrolysis of titanium tetraisopropoxide as a titania source with ethanol and then platinum was loaded on the synthesized catalyst; the result shows that the sample prepared has a good crystallinity with a surface area of about 85 m2 /g and a pore volume of 0.1938 cm3 /g, while XRD shows that the prepared sample was anatase phase. The efect of both temperature and liquid hourly space velocity of the prepared catalyst was achieved by hydroisomerization of n-hexane in a fxed bed reactor with a temperature of 200–275 °C and LHSV 0.5–2h−1. The results show

... Show More
View Publication
Crossref
Publication Date
Mon Jun 05 2023
Journal Name
Journal Of Engineering
The use of Prepared Zeolite Y from Iraqi kaolin for Fluid Catalytic Cracking of Vacuum Gas Oil
...Show More Authors

The faujasite type Y zeolite catalyst was prepared from locally available kaolin. For prepared faujasite type NaY zeolite X-ray, FT-IR, BET pore volume and surface area, and silica/ alumina were determined. The Xray and FT-IR show the compatibility of prepared catalyst with the general structure of standard zeolite Y. BET test shows that the surface area and pore volume of prepared catalyst were 360 m2 /g and 0.39 cm3 /g respectively.
The prepared faujasite type NaY zeolite modified by exchanging sodium ion with ammonium ion using ammonium nitrate and then ammonium ion converted to hydrogen ion. The maximum sodium ion exchange with ammonium ion was 53.6%. The catalytic activity of prepared faujasite type NaY, NaNH4Y and NaHY zeolites

... Show More
View Publication Preview PDF
Publication Date
Thu Dec 30 2021
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Synthesis and Characterization of Ni-WO3/Sulfated Zirconia Nano catalyst for Isomerization of N-Hexane and Iraqi Light Naphtha
...Show More Authors

This work deals with preparation of Sulfated Zirconia catalyst (SZ) for isomerization of n-hexane model and refinery light naphtha, as well as enhanced the role of promoters to get the target with the mild condition, stability, and to prevent formation of coke precursors on strong acidic sites of the catalyst. The prepared SZ catalysts were characterization by fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Brunauer –Emmett-Teller (BET) surface area analysis, Thermogravimetric Analysis (TGA), Scanning Electron Microscope (SEM) and atomic force microscopy (AFM) Analyzer. The results illustrate that the maximum conversion and selectivity for n-hexane isomerization with Ni-WSZ and operating temperature of 150 °C

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Tue Mar 01 2016
Journal Name
Journal Of Engineering
The Catalytic Activity of Modified Zeolite Lanthanum on the Catalytic Cracking of Al-Duara Atmospheric Distillation Residue.
...Show More Authors

Atmospheric residue fluid catalytic cracking was selected as a probe reaction to test the catalytic performance of modified NaY zeolites and prepared NaY zeolites. Modified NaY zeolites have been synthesized by simple ion exchange methods. Three samples of modified zeolite Y have been obtained by replacing the sodium ions in the original sample with lanthanum and the weight percent added are 0.28, 0.53, and 1.02 respectively. The effects of addition of lanthanum to zeolite Y in different weight percent on the cracking catalysts were investigated using an experimental laboratory plant scale of fluidized bed reactor.

The experiments have been performed with weight hourly space velocity (WHSV) range of 6 to 24 h

... Show More
View Publication Preview PDF
Publication Date
Thu Nov 01 2018
Journal Name
Molecular Catalysis
Hydrodesulfurization of Thiophene over $γ$-Mo2N catalyst
...Show More Authors

Catalytic removal of the S-content from thiophene is a central step in efforts aiming to reduce the environmental burdens of transportation fuels. In this contribution, we investigate the hydrodesulfurization (HDS) mechanisms of thiophene (C4H4S) over γ-Mo2N catalyst by means of density functional theory (DFT) calculations. The thiophene molecule preferentially adsorbs in a flat mode over 3-fold fcc nitrogen hollow sites. The HDS mechanism may potentially proceed either unimolecularly (direct desulfurization) or via H-assisted reactions (hydrogenation). Due to a sizable activation barrier required for the first Csingle bondS bond scission of 54.6 kcal/mol, we predict that the direct desulfurization to contribute rather very insignificant

... Show More
Publication Date
Sat Jan 13 2018
Journal Name
Journal Of Engineering
Investigating the Influence of the Cerium loading in prepared Y zeolite from Iraqi kaolin on its Catalytic Performance
...Show More Authors

In this study, the effects of different loading doses of cerium in the prepared NaY zeolite from Iraqi kaolin were investigated. Al-Duara  refinery atmospheric residue fluid catalytic cracking was selected as palpation reaction for testing the catalytic activity of cerium loading NaY zeolite.  The insertion of cerium in NaY zeolites has been synthesized by simple ion exchange methods. Three samples of modified zeolite Y have been obtained by replacing the sodium ions in the original sample with cerium and the weight percent added are 0.35, 0.64, and 1.06 respectively. The effects of cerium loading to zeolite Y in different weight percent on the cracking catalysts were studied by employing a laboratory fluidized

... Show More
View Publication Preview PDF
Publication Date
Fri Jan 01 2021
Journal Name
Materials Today: Proceedings
Pyrolysis of scrap tire by utilizing zeolite as catalyst
...Show More Authors

View Publication
Scopus (5)
Crossref (3)
Scopus Clarivate Crossref
Publication Date
Mon Sep 30 2019
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Synthesized 2nd Generation Zeolite as an Acid-Catalyst for Esterification Reaction
...Show More Authors

MCM-48 zeolites have unique properties from the surfaces and structure point of view as it’s shown in the results ,and unique and very sensitive to be prepared, have been experimentally prepared and utilized as a second-generation/ acid - catalyst for esterification reactions of oleic acid as a model oil for a free fatty acid source with Ethanol. The characterization of the catalyst used in the reaction has been identified by various methods indicating the prepared MCM-48 is highly matching the profile of common commercial MCM-48 zeolite. The XRF results show domination of SiO2 on the chemical structure with 99.1% and  agreeable with the expected from MCM-48 for it's of silica-based, and the SEM results show the cubic c

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Thu Jun 30 2011
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
CRACKING ACTIVITY OF PREPARED Y-ZEOLITE CATALYST USING CUMENE ON FLUIDIZED BED REACTOR
...Show More Authors

The catalytic activity of faujasite type NaY catalysts prepared from local clay (kaolin) with different Si/Al ratio was studied using cumene cracking as a model for catalytic cracking process in the temperature range of 450-525° C, weight hourly space velocity (WHSV) of 5-20 h1, particle size ≤75μm and atmospheric pressure. The catalytic activity was investigated using experimental laboratory plant scale of fluidized bed reactor.
It was found that the cumene conversion increases with increasing temperature and decreasing WHSV. At 525° C and WHSV 5 h-1, the conversion was 42.36 and 35.43 mol% for catalyst with 3.54 Si/Al ratio and Catalyst with 5.75 Si/Al ratio, respectively, while at 450° C and at the same WHSV, the conversion w

... Show More
View Publication Preview PDF