A study in the treatment and reuse of oily wastewater generated from the process of fuel oil treatment of gas turbine power plant was performed. The feasibility of using hollow fiber ultrafiltration (UF) membrane and nanofiltration (NF) membrane type polyamide thin-film composite in a pilot plant was investigated. Three different variables: pressure (0.5, 1, 1.5 and 2 bars), oil content (10, 20, 30 and 40 ppm), and temperature (15, 20, 30 and 40 ᵒC) were employed in the UF process while TDS was kept constant at 150 ppm. Four different variables: pressure (2, 3, 4 and 5 bar), oil content (2.5, 5, 7.5 and 10 ppm), total dissolved solids (TDS) (100, 200,300 and 400 ppm), and temperature (15, 20, 30 and 40 ᵒC) were manipulated with the help of statistical method of Taguchi in the RO process. Analysis of variable (ANOVA) and optimum condition was investigated. The study shows that pressure has the greatest impact on the flux of UF process, while temperature and pressure have similar contribution on flux of NF process. The temperature seems to have the greatest effect on TDS rejection. It was noticed that more than 96% oil removal can be achieved with flux of 624 L/m2.hr by UF process and that the fouling mechanism of UF process follows the cake/gel layer filtration model. It was observed that 100% removal of oil content can be achieved along with 79% for the TDS rejection and flux of 65 L/m2.hr by NF process. The result shows fouling in NF process follows the cake filtration model. It was concluded that the observed values are within ±5% of that the predicted which reflects a strong representative model. The treated wastewater has the characteristics that it can be reused in the process to reduce the operating cost.
(8)
A pulsed (TEA-0O2) laser was used to dissociate molecules of silane ethylene (C2I-14) and ammonia (NH3) gases, through collision assisted multiple photon dissociation (MPD) to deposit(SiC i_xNx) thin films, where the X-values are 0, 0.13 and 0.33, on glass substrate at T,----648 K. deposition rate of (0.416-0.833) nm/pulse and thickness of (500-1000)nm .Fourier transform infrared spectrometry (FT-IR) was used to study the nature of the chemical bonds that exist in the films. Results revealed that these films contain complex networks of the atomic (Si, C, and N), other a quantity of atomic hydrogen and chemical bonds such as (Si-N, C-N, C-14 and N-H).Absorbance and Transmittance spectra in the wavelength range (400-1100) nm were used to stud
... Show MoreAbstract
This Research aims for harnessing critical and innovative thinking approaches besides innovative problem solving tools in pursuing continual quality improvement initiatives for the benefit of achieving operations results effectively in water treatment plants in Baghdad Water Authority. Case study has been used in fulfilling this research in the sadr city water treatment plant, which was chosen as a study sample as it facilitates describing and analyzing its current operational situation, collecting and analyzing its own data, in order to get its own desired improvement opportunity be done. Many statistical means and visual thinking promoting methods has been used to fulfill research task.
... Show More
(2)
In this work Polyynes was synthesized by pulse laser ablation of graphite target in ethanol solution. UV-Visible Spectrophotometer, Fourier Transform Infrared Spectroscopy (FTIR) and Transmission electron microscopy (TEM) were used to study the optical absorption, chemical bonding, particle size and the morphology. UV absorption peaks coincide with the electronic transitions corresponding to linear hydrogen – capped polyyne (Cn+1H2), the absorption peaks intensity increased when the polyynes were produced at different laser energies and the formation rats of polyynes increased with the increasing of laser pulse number. The FTIR absorption peak at 2368.4 cm-1, 1640.0 cm-1 and 1276.
... Show More
(11)
Isolation and identification fungi of Emericella nidulans and Aspergillus flavus from a pinkish and yellowish artificial clay, by using potato dextrose agar (PDA). Results revealed that E. nidulans was the best for degrading anthracene (92.3%) with maximum biomass production (3.7gm/l), compared to A. flavus with the rate of degradation (89%) and biomass production of (1.2gm/l), when methylene blue was used as redox indicator after incubating in a shaker incubator 120rpm at 30Co for 8days. Results indicated that E. nidulans has a high ability of anthracene degradation with the rate of (84%), while A. flavus showed the lower level with (77%) by using HPLC.
(3)
The bacteria Azotobacter Vinelandii was taken from a central research in Baghdad, The purification of alginic acid which produced from the bacteria by several steps starting with precipitation with isopropanol (3:1) v/v , Washing by ppt with 100ml of isopropanol : distilled water (3:1) v/v , then the ppt was dissolved in warm distilled water and dialysis against distilled water from 24 h/s . To Complete the purification , gel filtration chromatography was conducted on sephacryl s-100 column followed by ion – exchange chromatography . Using DEAE cellulose column . The molecular Weight of purified al ginic acid was higher than that of blue dextran 2000,It was more than (2) millions Dalton .<
... Show MoreBackground: This in vitro study was carried out to evaluate the effects of various veneering dentin ceramic thicknesses and repeated firings on the color of lithium disilicate glass-ceramic (IPS e.max Press) and zirconium-oxide (IPS ZirCAD) all-ceramic systems, measured by clinical spectrophotometers (Easyshade Advance 4.0) . Materials and methods: The 72specimens cube-shaped have the dimension of about 11 mm in width, 14 mm in length, 1mm in thickness, these cores divided into 3 groups according to the type of material each group have (24)core specimens. Each group had been divided into three sub-groups (each having 8 specimens) according to veneering with dentin ceramic thicknesses: as 0.5, 1, or 2 mm (n=8). IPS e.max press and ZirCAD c
... Show More
The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di
Objectives: This study explored knowledge, attitude, and practice of infection control by dental students at College of Dentistry/ University of Baghdad, Iraq. Material and Methods: Three hundred dental students participated in this study. A self administrated questionnaire with 21 close ended questions related to use of personal protective equipments, infection control awareness, vaccination status, percutaneous exposures, and attitude towards treatment of patients with hepatitis B (HBV)/ or human immunodeficiency virus (HIV) was distributed to dental students. Data were analyzed using Statistical Package for Social Sciences (SPSS) version 21. Fisher exact and Chi-square test were used with significance level set to 0.05. Results: The