Nano gamma alumina was prepared by double hydrolysis process using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, hydroxyle poly acid and CTAB (cetyltrimethylammonium bromide) as templates. Different crystallization temperatures (120, 140, 160, and 180) ⁰C and calcinations temperatures (500, 550, 600, and 650) ⁰C were applied. All the batches were prepared at PH equals to 9. XRD diffraction technique and infrared Fourier transform spectroscopy were used to investigate the phase formation and the optical properties of the nano gamma alumina. N₂ adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the particle size and the

In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f

     Polluted water has been considered a critical issue nowadays, threatening the environment and lives of living creatures. Because of technological and industrial advancements, as well as increased social activities of humans in various countries, pollution sources have multiplied. To reduce the impact of this problem, many techniques have been developed in order to reach zero discharge pollution. In the last decade, graphene oxide (GO) - a member of the graphene nanomaterials family, has been the focus of many research efforts in the water treatment sector because of its extraordinary properties. This review highlights the research efforts conducted to investigate GO as a novel adsorbent for water treatment applications and recen

Microwave heating is caused by the ability of the materials to absorb microwave energy and convert it to heat. The aim of this study is to know the difference that will occur when heat treating the high strength aluminum alloys AA7075-T73 in a microwave furnace within different mediums (dry and acidic solution) at different times (30 and 60) minutes, on mechanical properties and fatigue life. The experimental results of microwave furnace heat energy showed that there were variations in the mechanical properties (ultimate stress, yielding stress, fatigue strength, fatigue life and hardness) with the variation in mediums and duration times when compared with samples without treatment. The ultimate stress, yielding stress and fatigue streng

Nisoldipine (NSD) is a dihydropyridine class of calcium channel blockers used for hypertension treatment, it belongs to class II BCS (low solubility with high permeability), its absolute bioavailability is only 5% due to presystemic metabolism in the gut wall. It is also a substrate for a CYP3A and P-gp. Bilosomes are lipid bilayer vesicles incorporating bile salts in their walls to prevent degredation by GIT bile salts. The aim of this study is to prepare nisoldipine bilosomes as vesicular carrier and assess the effect of different formulation variables such as type of surfactant, amount of cholesterol, surfactant and sonication time on particle size, entrapment efficiency and poly dispersity index of the prepared bilos

The effect of approaching nozzle jet from the deposition surface
on structural, optical and morphology properties of copper oxide thin
films was studied. The film was prepared by homemade fully
computerized CNC spray pyrolysis deposition technique at
preparations speed (3, 4, 5, and 6 mm/sec). The repeated line mode
was used at deposition temperature equal 450 °C whereas the
spraying time was in the range of (15-30 min) according to the
deposition speed. The film exhibit polycrystalline structure with
preferred orientation along (-111), (022) and (011), (002) at a 2θ
value of (35.63o) and (38.8o) respectively. Optical band gaps were
recorded at these speed shows variance in value from (1.53-2.08 eV).
Fi

The aim of this study was to use low cost adsorbents, which consist of corn cobs as plant wastes adsorbents in treatment of Industrial waste water by fixed bed column technique and study the effect of two variables (pH value and contact time). The sample of plant waste (Corn cobs) was tested to determine its activity which gives the best performance in heavy metals removal and other pollutants (TSS, TDS and COD). Adsorption tests showed the corn cobs adsorbents had significant heavy metal removal efficiency. The best removal efficiency 95.05% of Cr was occurred at pH 5.4 and 4.18hr. Higher removal efficiency 99.90% of Ni was occurred at pH 6.5 and 2.38hr. While, lower removal efficiency 91.35% for Zn obtained at pH 6.5 and 0.15hr. Remova

The current study was designed for using banana peels to remove zinc, chromium and nickel from industrial waste-water. Three forms of these peels (fresh, dried small pieces and powder) were tested under some environmental factors such as pH, temperature and contact time. Current data show that banana peels are capable of removing zinc, chromium and nickel ions at significant capacity. Furthermore, the powder of banana peels had highest capability in removing all zinc, chromium and nickel ions followed by fresh peels whilst dried peels had the lowest bioremoving capacity again for all metals under test. The highest capacity was for chromium then nickel and finally zinc. All these data were significantly (LSD peel forms = 2.761 mg/l, LSD m

The aim of this study was to use low cost adsorbents, which consists of plant wastes in treatment of Industrial waste water by fixed bed column technique and study the effect of to two variables (pH value and contact time) on adsorption process. The sample of plant waste (Rice husk) was tested to determine its activity which gives the best performance in heavy metals removal and other pollutants (TSS, TDS and COD). Adsorption tests showed all tested plant adsorbents had significant heavy metal removal efficiency. The best removal efficiency 96.56% of Cr was occurred at pH 6.5 and 5hrs. Higher removal efficiency 99.02% of Ni was occurred at pH 6.5 and 0.15hr. While, lower removal efficiency 94% for Zn obtained at pH 5 and 2.83hrs. Removal