A particulate polymer composite material was prepared by reinforcing with the Aluminum Oxide (Al₂O₃) or Aluminum (Al) metallic particles with a particle size of (30) µm to an unsaturated Polyester Resin with a weight fraction of (5%, 10%, 15%, 20%).

Tensile test results showed the maximum value of elastic modulus reached (2400MPa.)  in the case of reinforcing with (Al) particles with weight fraction (20%) and (1500 MPa.)  in the case of reinforcing with (Al₂O₃) particles of the same weight fraction.

  When the impact and the flexural strength tests were done, the results showed that flexural strength (F.S), maximum shear stress (τ_max), impact strength

In the present study a new synthesis method has been introduced for the decoration of platinum(Pt) on the functionalized graphene nanoplatelet (GNP) and also highlighted the preparation method of nanofluids. GNP–Pt uniform nanocomposite was produced from a simple chemical reaction procedure, which included acid treatment for functionalization of GNP. The surface characterization was performed by various techniques such as XRD, FESEMand TEM. The effective thermal conductivity, density, viscosity, specific heat capacity and stability of functionalized GNP–Pt water based nanofluids were investigated in different instruments. The GNP–Pt hybrid nanofluids were prepared by dispersing the nanocomposite in base fluid without adding any surfac

Gastritis can be defined as histological inflammation of the gastric mucosa. It can be classified according to the time course of the disease as acute or chronic, histological findings, anatomic location, and pathological mechanisms. The objective of this study was to evaluation of serum levels of the proinflammatory cytokines IL-8, IL-17 and IL-22 in Helicobacter pylori infection and their association with the degree of gastritis histopathology in a sample of Iraqi patients. The case-control prospective study consists of 60 patients who attended the Gastrointestinal Tract Center at Al-Kindy Teaching Hospital during the period from December 2019 to April 2020. In addition, the control group included 60 apparently healthy individuals. Bio

This study aims to study some morphological and reproductional characteristics in eleven species of two genera belonging to the family of Asparagaceae, which are Bellevalia Lapeyrouse, 1808 and Ornithogalum Linnaeus, 1753 and the species are: Bellevalia chrisii Yildirim and Sahin, 2014; Bellevalia flexuosa Boissier, 1854; Bellevalia kurdistanica Feinbrun, 1940; Bellevalia longipes Post, 1895; Bellevalia macrobotrys Boissier, 1853; Bellevalia paradoxa Boissier, 1882; Bellevalia parva Wendelbo, 1973; Bellevalia saviczii Woronow, 1927; Ornithogalum brachystachys C. Koch, 1849; Ornithogalum neurostegium Boissier, 1882 and Ornithogalum pyrenaicum Linnaeus, 1753. These species were identified and compared with each other; the results showed th

The current study was to examine the reliability and effectiveness of using most abundant, inexpensive waste in the form of scrap raw zero valent aluminum ZVAI and zero valent iron ZVI for the capture, retard, and removal of one of the most serious and hazardous heavy metals cadmium dissolved in water. Batch tests were conducted to examine contact time (0-250) min, sorbent dose (0.25-1 g ZVAI/100 mL and 2-8 g ZVI/100 mL), initial pH (3-6), pollutant concentration of 50mg/L initially, and speed of agitation (0-250) rpm . Maximum contaminant removal efficiency corresponding to (90 %) for cadmium at 250 min contact time, 1g ZVAI/ 6g ZVI sorbent mass ratio, pH 5.5, pollutant concentration of 50 mg/L initially, and 250 rpm agitation speed wer

The gas sensing properties of Co3O4and Co3O4:Y nano structures were investigated. The films were synthesized using the hydrothermal method on a seeded layer. The XRD, SEM analysis and gas sensing properties were investigated for Co3O4and Co3O4:Y thin films. XRD analysis shows that all films are polycrystalline in nature, having a cubic structure, and the crystallite size is (11.7)nm for cobalt oxide and (9.3)nm for the Co3O4:10%Y. The SEM analysis of thin films obviously indicates that Co3O4possesses a nanosphere-like structure and a flower-like structure for Co3O4:Y.The sensitivity, response time and recovery time to a H2S reducing gas were tested at different operating