A set newly complexes with the general formula [M(L)Cl2] are resulting from the reaction of a new schiff base ligand [Ethyl (6R,7R)-7-((E)-2-((2-ethoxy-2- oxoethoxy)imino)-2-(2-(((E)-4-nitrobenzylidene) amino) thiazol -4- yl) acetamido) -8- oxo -3- vinyl -5- thia -1-aza bicyclo [4. 2.0] oct -2- ene -2- carboxylate] (L). This ligand was derived from the reaction of the two substances 4-nitrobenzaldehyde and precursor (P). Reaction the ligand with metal ions M= Mn(II), Co(II), Ni(II), Cu(II) and Cd(II) afforded new complexes which are characterized by FT-IR and Electronic Spectra. These measurements indicate that the complexes have a tetrahedral geometry. The Penicillin-Binding Protein 3 (PBP3) of Staphylococcus aureus and the target protein

The study involved preparing a new compound by combining Schiff bases generated from compounds for antipyrine, including lanthanide ions (lanthanum, neodymium, erbium, gadolinium, and dysprosium). The preparation of the ligand from condensation reactions (4-antipyrinecarboxaldehyde with ethylene di-amine) at room temperature, and was characterization using spectroscopic and analytical studies ( FT-IR, UV-visible spectra, ¹H-NMR, mass spectrometry, (C.H.N.O), thermogravimetric analysis (TGA), in addition to the magnetic susceptibility and conductivity measurement of the synthesis complexes, among the results we obtained from the tests, we showed that the ligand behaves with the (triple Valence) lanthanide ions, the multidentate

Thin films of Zinc Selenide ZnSe have been prepared by using thermal evaporation in vacuum technique (10-5Torr) with thickness (1000, 2700, 4000) A0 and change electrode material and deposited on glass substrates with temperature (373K) and study some electrical properties at this temperature . The graphs shows linear relation between current and voltage and the results have shown increases in the value of current and electrical conductivity with increase thickness and change electrode material from Aluminum to Copper

The study of surface hardness, wear resistance, adhesion strength, electrochemical corrosion resistance and thermal conductivity of coatings composed from sodium silicate was prepared using graphite micro-size particles and carbon nano particles as fillers respectively of concentration of (1-5%), for the purpose of covering and protecting the oil distillation towers. The results showed that the sodium silicate coating reinforced with carbon nano-powder has higher resistance to stitches, mechanical wear, adhesive and thermal conductivity than graphite/sodium silicate composite especially when the ratio 5% and 1%, the electrochemical corrosion test confirmed that the coating process of stainless steel 304 lead to increasin

thin films of se:2.5% as were deposited on a glass substates by thermal coevaporation techniqi=ue under high vacuum at different thikness