Performance of composite unprotected steel Beam-deck floor exposed to high temperature (fire flame)
...Show More Authors

An experimental program was conducted to determine the residual of composite Steel Beams-Reinforced Concrete (SB-RC) deck floors fabricated from a rolled steel beam topped with a reinforced concrete slab, exposed to high temperatures (fire flame) of 300, 500, and 700ºC for 1 hour, and then allowed to cool down by leaving them in the lab condition to return to the ambient temperature. The burning results showed that, by exposing them to a fire flame of up to 300ºC, no serious permanent deflection occurred. It was also noticed that the specimen recovered 93% of 19.2 mm of the deflection caused by burning. The recovered deflection of burned composite SB-RC deck floor at 500ºC was 40% of 77.9 mm of the deflection caused by burning with a residual deflection of 46.4 mm. The greatest deterioration occurred when exposed to 700ºC, at this temperature, a higher unrecoverable permanent deflection was recorded (160.3 mm) of the maximum measured burning deflection (173.8mm), indicating that the percent recovered deflection was 8%. Then, all composite SB-RC deck floors were loaded until failure to determine the percent decrease in their ultimate capacity. The results were compared with the behavior of composite SB-RC deck floor without burning (reference specimen).

View Publication Preview PDF
Quick Preview PDF
Publication Date
Wed Sep 01 2010
Journal Name
Materials & Design
Influence of glass addition and sintering temperature on the structure, mechanical properties and dielectric strength of high-voltage insulators
...Show More Authors

View Publication
Scopus (13)
Crossref (10)
Scopus Clarivate Crossref
Publication Date
Wed Mar 10 2021
Journal Name
Baghdad Science Journal
Effect of High Temperatures on Biological Performance ofTrogoderma granarium (Everts) (Coleoptera: Dermestidae)
...Show More Authors

The effect of three high temperatures for five exposure periods on the developments of larvae, pupae and adults of Trogoderma granarium (Everts) and their biological performance were investigated. The results revealed that the percent of mortality was increased as the temperature and the exposure period increased, e. g. exposing last instar larvae to 45°C for 6 hrs caused 100% death of this stage, while exposing adults (1-3) days old to the same temperature and exposure time resulted in that these adults did not able to survive more than 24 hrs.; in addition, the results showed that the ability of reproduction of adults was depended on the temperature, duration of exposure and the sex.

View Publication Preview PDF
Crossref
Publication Date
Thu Jun 01 2023
Journal Name
Iraqi Journal Of Physics
Preparation of SiO2:TiO2 for High-Performance Double Layer Anti-Reflection Coating
...Show More Authors

        In this work, an anti-reflection coating was prepared in the region (400-1000) nm of wavelength, with a double layer of silicon dioxide (SiO2) as an inner layer and the second layer of the mixture (SiO2) and titanium dioxide (TiO2) with certain ratios, as an outer layer using the chemical spraying method with a number of 6 sprays of layer SiO2 and 12 sprays of layer SiO2 - TiO2. Using the method of chemical spraying deposited on the glass as a substrate with a different number of sprays of SiO2, and a fixed number of TiO2-SiO2. The optical and structural properties were determined using UV-Vis spectroscopy and atomic force mi

... Show More
View Publication Preview PDF
Crossref (5)
Crossref
Publication Date
Thu Oct 06 2022
Journal Name
2022 9th International Conference On Electrical Engineering, Computer Science And Informatics (eecsi)
On the Performance of a Composite Right Left Hand Electromagnetic Bandgap Structure
...Show More Authors

This paper presents the design and analysis of composite right left hand (CRLH) electromagnetic bandgap (EBG) structure. The proposed unit cell is consistent of a dielectric substrate with dimensions of 5×5×1 mm 3 made of FR4-Epoxy with εr = 4.4 underneath of a conductive patch with dimensions of 4.4×4.4mm 2 . The unit cell is structured to perform a negative permittivity (ε) and negative permeability (µ) in different bands. The proposed unit cell is developed to 5G systems in the sub-6GHz bands. In this work, a complete analysis of the unit cell in terms of Sparameters, constitutive parameters and refraction index are evaluated using HFSS simulation package based on Finite Element Method (FEM).

View Publication
Scopus (6)
Crossref (4)
Scopus Crossref
Publication Date
Fri Dec 15 2023
Journal Name
Iraqi Journal Of Laser
Photocatalytic Performance of AgNPs-Zeolite Composite by Hydrothermal Synthesis for Water Splitting
...Show More Authors

Two samples of (Ag NPs-zeolite) nanocomposite thin films have been prepared by easy hydrothermal method for 4 hours and 8 hours inside the hydrothermal autoclave at temperatures of 100°C. The two samples were used in a photoelectrochemical cell as a photocatalyst inside a cell consisting of three electrodes: the working electrode photoanode (AgNPs-zeolite), platinum as a cathode electrode, and Ag/AgCl as a reference electrode, to study the performance of AgNPs-zeolite under dark current and 473 nm laser light for water splitting. The results show the high performance of an eight-hour sample with high crystallinity compared with a four-hour sample as a reliable photocatalyst to generate hydrogen for renewable energies.

 

View Publication Preview PDF
Crossref
Publication Date
Fri Sep 06 2024
Journal Name
Journal Of Optics
Optimization photodetection performance: investigation of doping effect on PVA/Y2O3 composite material
...Show More Authors

In this work, the photodetection performance of polyvinyl alcohol (PVA) nanofibers and its composite with yttrium oxide (Y2O3) at different concentrations (2.5, 5, 10) wt% are examined deposited on p-type Si with (111) orientation. Electrospinning technique was used to create nanofiber composites. Adding Y2O3 significantly impacts the PVA nanofibers where ultraviolet-visible (UV-Vis) spectroscopy optical absorption energy gap decreases with increased concentration (2.8, 2.6, and 2.3) eV. X-ray diffraction was used to investigate crystal structure, which is cubic structure. The chemical composition study was conducted using Fourier transform infrared spectroscopy (FTIR) spectra, which revealed the stretching vibrations related to the Y-O bon

... Show More
View Publication
Scopus (2)
Crossref (1)
Scopus Clarivate Crossref
Publication Date
Sat Jan 01 2022
Journal Name
Journal Of The Mechanical Behavior Of Materials
Influence of water-absorbent polymer balls on the structural performance of reinforced concrete beam: An experimental investigation
...Show More Authors
Abstract<p>This research investigated the influence of water-absorbent polymer balls (WAPB) on reinforced concrete beams’ structural behavior experimentally. Four self-compacted reinforced concrete beams of identical geometric layouts 150 mm × 200 mm × 1,500 mm, reinforcement details, and compressive strength <inline-formula> <alternatives> <inline-graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="graphic/j_jmbm-2022-0024_eq_001.png"></inline-graphic> <math xmlns:m="http://www.w3.org/1998/Math/MathML"> <msubsup> <mrow> </mrow></msubsup></math></alternatives></inline-formula></p> ... Show More
Crossref (2)
Crossref
Publication Date
Tue Dec 05 2023
Journal Name
Engineering, Technology &amp; Applied Science Research
The Fire Effect on the Performance of Reinforced Concrete Beams with Partial Replacement of Coarse Aggregates by Expanded Clay Aggregates
...Show More Authors

This paper aims to investigate the flexural behavior of reinforced concrete beams considering fire resistance by adding Lightweight Expanded Clay Aggregates (LECA) to the concrete mix as partial coarse aggregate replacement. LECA is a type of porous clay with a uniform pore structure with fine, closed cells and hard, tightly sintered skin. The experimental work comprised four reinforced self-compacted concrete beams. All the specimens were identical in their geometrical layout of 1600×240×200 mm, reinforcement details, and support condition (simply supported). For all the beams, the main reinforcement was provided by two bars, each having a diameter of 12 mm, while a bar of 6 mm diameter was employed for the top and shear reinforc

... Show More
View Publication
Scopus (7)
Crossref (6)
Scopus Clarivate Crossref
Publication Date
Sun Oct 01 2017
Journal Name
Journal Of Craniofacial Surgery
Is Orbital Floor Reconstruction With Titanium Mesh Safe?
...Show More Authors

View Publication
Scopus (11)
Crossref (13)
Scopus Clarivate Crossref
Publication Date
Mon May 13 2024
Journal Name
Journal Of Engineering And Applied Science
Assessment of using different ozone-friendly R22 alternative refrigerants in residential air conditioners in a high-ambient temperature country
...Show More Authors
Abstract<p>The performance of a vapor compression refrigeration system (VCRS)-based residential air conditioner operating in a high-ambient temperature (HAT) country was investigated using six zero-ODP (ozone depletion potential) refrigerants as replacements to R22. The non-flammable alternative refrigerants considered in the present research were R134a, R404A, R407C, R410A, R448A, and R507A. Using the basic conservation laws, the VCRS was modeled during steady-state operation and solved using engineering equation solver (EES) software. Coefficient of performance (COP), pressures and temperatures at compressor suction and discharge, Global Warming Potential (GWP), critical pressure and temperature, compressor </p> ... Show More
View Publication
Scopus (2)
Crossref (2)
Scopus Crossref