A series of liquid crystals comprising a heterocyclics dihydro pyrrole and 1,2,3-triazole rings [VII]-[X] were synthesized by many steps starting from a reaction of 3,3'-dimethyl-[1,1'-biphenyl]- 4,4'-diamine with chloroacetyl chloride in a mixture of solutions DMF and TEA to synthesise the compounds [I], then the compounds [I] reacted with malononitrile in 1,4-dioxane and TEA solutions to produce compounds [II], then the first step is repeated with compound [II] where it reacted with chloroacetyl chloride in mixture of DMF and TEA to give compound [III], this compound reacted with sodium azide in the presence of sodium chloride and DMF as solvent to produce the compound [IV], which reacted with acrylic acid by a 1.3 dipolar reaction in sol

Abstract 

Locally natural occurring Iraqi rocks of Bauxite and Porcelanite (after pre calcinations at 1000^oC for 1hr) were used, with the addition of different proportions of MgO and Al₂O₃, to prepare refractory materials. The effects of these additives on the physical and thermal properties of the prepared refractories were investigated.

Many batches of Bauxite/MgO, Bauxite/Al₂O₃, Bauxite/MgO/Al₂O₃, and   Porcelanite/ MgO/Al₂O₃ were prepared. The mixture is milled and classified into different size fractions; fine (less than 45μm) 40%, middle (45-75μm) 40%, and coarse (75-106μm) 20% .

Porous asphalt paving is a modern design method that differs from the usual asphalt pavements' traditional designs. The difference is that the design structure of porous pavements allows the free passage of fluids through their layers, which controls or reduces the amount of runoff or water accumulated in the area by allowing the flow of rain and surface runoff.  The cross-structure of this type of paving works as a suitable method for managing rainwater and representing groundwater recharge. The overall benefits of porous asphalt pavements include environmental services and safety features, including controlling the build-up of contaminated metals on the road surface, rainwater management, resistance to slipping ac

In this research was study the effect of increasing the number of layers of the semiconductor films as PbS on the average grain sizes and illustrate the relationship between the increase in the average grain size and thickness of the membrane, and membrane was prepared using the easy and simple and does not need the complexity of which is that the chemical bath , and from an X-ray diffraction found that the material and the installation of a random cubic and when increasing the number of layers deposited note the emergence of a number of vertices of a substance and PbS at different levels but the level is more severe (200) as well as the value is calculated optical energy gap and found to be not affected by increase thickness and from th

In this research PbS thin film have been prepared by chemical bath deposition technique (CBD).The PbS film with thickness of (1-1.5)μm was thermally treated at temperature of 100°C for 4 hours. Some Structural characteristics was studied by using X-ray diffraction (XRD)and optical microscope photograph some of chemical gas sensing measurements were carried out ,it shown that the sensitivity of (CO2) gas depend on the grain Size and deposition substrate. The grain size of PbS film deposited on on glass closed to 21.4 nm while 37.97nm for Si substrate. The result of current-voltage characterization shwon the sensitivity of prepared film deposited on Si better than film on glass.

Gypsum Plaster is an important building materials, and because of the availabilty of its raw materials. In this research the effect of various additives on the properties of plaster was studied , like Polyvinyl Acetate, Furfural, Fumed Silica at different rate of addition and two types of fibers, Carbon Fiber and Polypropylene Fiber to the plaster at a different volumetric rate. It was found that after analysis of the results the use of Furfural as an additive to plaster by 2.5% is the optimum ratio of addition to that it improved the flexural Strength by 3.18%.
When using Polyvinyl Acetate it was found that the ratio of the additive 2% is the optimum ratio of addition to the plaster, because it improved the value of the flexural stre