The present research was conducted to synthesis Y-Zeolite by sol-gel technique using MWCNT (multiwalled carbon nanotubes) as crystallization medium to get a narrow range of particle size distribution with small average size compared with ordinary methods. The phase pattern, chemical structure, particle size, and surface area were detected by XRD, FTIR, BET and AFM, respectively. Results shown that the average size of Zeolite with and without using MWCNT were (92.39) nm and (55.17) nm respectively .Particle size range reduced from (150-55) nm to (130-30) nm. The surface area enhanced to be (558) m2/g with slightly large pore volume (0.231) km3/g was obtained. Meanwhile, degree of crystallization decreased to 120%.

The aim of this research is to design and construct a semiconductor laser range finder
operating in the near infrared range for ranging and designation. The main part of the range finder is the
transmitter which is a semiconductor laser type GaAs of 0.904 mm wavelength with a beam expander,
and the receiver with its collecting optics. The characteristics of transmitter pulse width were 200ns and
threshold current 10 Amp. and maximum operating current 38 Amp. The repetition rate was set at 660 Hz
and maximum output power about 1 watt. The divergence of the beam was 0.268o. A special computer
code was used for optimum optical design and laser spot size analysis and for calculation of atmosphere
attenuation.

The x-ray fluorescence (XRF) of Znpc molecule with (flow of Ar) and Znpc molecule with (grow in N2) showed two peaks at (8.5and 9.5 Kv) referring to orbital transition ) K?-shell & K?-shell) respectively. The study of x-ray diffraction (XRD) where it was observed good growth of the crystal structure as a needle by the sublimation technique with a ?-phase of (monoclinic structure ) . Using Bragg equation the value of the interdistance of the crystalline plane (d-value) were calculated. We noticed good similarity with like once in the American Standards for Testing Material (ASTM) .Powder Diffraction File (PDF) Program was used to ensure the information obtained from (ASTM) . The output of (PDF) was compared with celn program, where the val

Biodiesel is popular as an eco-friendly fossil fuel alternative. Neem oil is manufactured from Azadirachta indica seeds. Transesterifying triglycerides with alcohol in the presence of a synthesized CaO nanocatalyst is the most common biodiesel synthesis procedure—recent advances, difficulties, and prospects in laser feedstock pretreatment to boost reactivity and reduce energy use. Oil pre-treatment with a 540-nm green laser is cost-effective and environmentally friendly. This study examined neem oil with and without laser pretreatment for biodiesel synthesis. CaO nanocatalysts were synthesised using Sol–gel and characterised using XRD and SEM. According to catalyst recyclability, the CaO nanocatalyst did not lose activity after five re

Hydrogen and nanocarbon were produced by the catalytic decomposition of electrocracking gas obtained by the pyrolysis of liquid organic waste via electric arc discharge. The GIAP-16 (NiO-Al2O3) industrial catalyst was used to reduce the maximum decomposition temperature to 700 °C. In a fixed-bed reactor, under atmospheric pressure, reasonable amounts of high-purity hydrogen were produced, accompanied by deposits of nanocarbon by-product. The NiO-Al2O3 catalyst showed excellent catalytic activity. X-ray powder diffraction analysis of the NiO-Al2O3 composite revealed the presence of cubic NiO and rhombohedral Al2O3, which were chemically stable. However, above 500 °C, NiAl2O4 began to appear. The specific surface area of the catalyst was de

In this work the production of activated carbon (AC) from Imperata is done by microwave assisted Potassium hydroxide (KOH) activation and using this activated carbon for the purpose of the uptake of amoxicillin (AMX) by adsorption process from aqueous solution. The effects for irradiation power (450-800W), irradiation time (6-12min) as well as impregnation ratio (0.5-1 g/g) on the AMX uptake and yield AMX uptake at an initial concentration of AMX (150 mg/g). The optimum conditions were 700 W irradiation power, 10 min time of irradiation, as well as 0.8 g/g impregnation ratio with 14.821% yield and 12.456 mg/g AMX uptake. Total volume of hole and the area of the surface (BET) are 0.3027 m³/g, and 552.7638 m²/g respectively. The properti

The fresh water green alga Chlorella vulgaris was selected to study its ability to degrade one of polycyclic aromatic hydrocarbon (PAHs)known is anthracene (ANT). ANT is widely used in artificial products such as wood preservatives; insecticides; dye and coating materials. This algae was cultivated in CH-10 medium under constant laboratory conditions and exposed to different concentrations (1, 3, and 5 mg/l) of anthracene for 3, 5, 7, 9 and 15 days, with the concentration of ANT measured  by high performance liquid chromatographic analysis (HPLC). The results showed that C.vulgaris has high ability to reduce anthracene to 80% at 1mg/Lcon centration after 3 days and 100% after 5 days, while at 3 and 5 mg / L concent

The effect of different antibiotics on growth pigment and plasmid curing of Serratia marcescens were studied, S. marcescens was cultured in media containing(16_500)µg/ml of antibiotics, curing mutants unable to produce prodigiosin and lost one plasmid band were obtained of of ampicillin, amoxillin, antibiotics concentrations (64 500) µg/ml metheprim, ultracloxam, azithromycin, cephalexin and erythromycin treated with (350 500) µg/ml of The mutant cells rose- light color and and refampicin revealed S.marcescens inhibited ciprodar and tetracyclin, lincomycin did not lost the plasmid band chlaforan