Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

The largest use of x-ray in medical by dentists, employers or persons that needed by patients with specific conditions, lead to higher exposure of x-ray that may cause many diseases. In the present work radiography films have been used in evaluating the efficiency of using unsaturated polyester polymer reinforced with lead oxide (PbO) as shield material for medical x-ray devices, many parameters studied like concentration and thickness that they are increasing the attenuation of x-ray in them. The results show that the attenuation of X-ray increasing with concentration of reinforced material and with thickness, and the optical density decreases with increasing concentration from 0% to 50%, we chose 30% as suitable concentration to increase

The reaction of(2-oxo-2H-chromen-3-Carbonyl chloride)(k1) with hydrazine in boiling ethanol gives the hydrazide(K2).When compound (k2) reacts with various aromatic aldehydes ,the corres ponding Schiff bases(k3–k4) achieve new series of thiazotidines (k5–k6) and azetidinones (k7–k8) obtained from the reactions of appropriate Schiff bases with mercapto acetic acid and chloro acetyl chloride respectively. All the compounds are characterized by FT-IR,1H-NMR and GC-Ms.

Worldwide attention is being focused on  nanocrystalline  zeolites  and they are replacing conventional ones due to their pronounced potential in many fields. In this study, NaY zeolite has been prepared hydrothermally using sol –gel method and modified to the proton type by ion –exchange process. Characterization is made using X-ray diffraction (XRD), thermogravimetric analysis (TGA),  Fourier transform infrared spectroscopy (FTIR),  Atomic force microscopy (AFM), Brunauer –Emmet- Teller (BET) nitrogen adsorption method, Ammonia Temperature programmed desorption (NH₃-TPD) and Scanning electron microscopy( SEM).  The effect of aging time, silica to alumina ratio is studied and the results sh

In the present paper we report the synthesis of a new ligand [HL][(2-1-[(2-hydroxy-benzylidene)-hydrazono]-ethyl) benzene-1, 3, 5-triol and its complexes with (Mn", Fe", Cd", and Hg") The ligand was prepared in two steps. In the first step a solution of salicylaldehyed in methanol reacted under reflux with hydrazinemonohydrate to give an intermediate compound which reacted in the second step with 2, 4, 6-trihydroxidernonohydrate giving the tientioned ligand. The complexes were synthesis by direct reaction of the corresponding metal chloride with ligand. The ligand and the complexes have been characterized by spectroscopic methods [" H NMR, IR, UV-Vis,, atomic absorption], HPLC microanalysis along with conductivity measurements. From the abo

The present work involved synthesis of new thiozolidinone derivatives,These derivatives could be divided into three type of compounds; quinolin-2-one[V]a,b ,Schiff bases[VI]a,b and imide compounds[VII]a-d. The reaction p-Hydroxyacetophenone with thiosemicarbazide led to formation thiosemicarbazon compound [II], the reacted of thiosemicarbazone with chloro acetic acid in CH3CO2Na led to yield 4- thiazelidinone compound[III] in addition, thiosemicarbazide was POCl3 to [III] give [IV] compound used intermediates to synthesis new compounds of reacted with two type of coumarin in glacial acetic acid to give quinolin-2-one[V]a,b, The later compound refluxing with different benzaldehyde in dry benzene and glacial acetic acid give Schiff bases[VI]a

     The polyaniline powder was chemically manufactured by direct oxidation of aniline. The resulting polymer was characterized by the results of optical, measurements by (FT-IR) spectroscopy, we have detected some of the absorption peaks located at 3498, 2858 cm^-1, which correspond N-H vibrations, and C-H expansion of the aromatic ring respectively as well as stretching vibrations of quinoid ring have been observed. Structural properties, such as the surface topography using an atomic force microscope (AFM), and Surface composition by (SEM) have been studied. The structure of some pellets of polyaniline powder have been examined by using analytical X-ray diffraction technique, the pattern of obse

This work comprises the synthesis of new thioxanthone derivatives containing C-substituted thioxanthone. To obtain these derivatives, the o-mercapto benzoic acid was chosen as the starting material, which was reacted with dry benzene in sulfuric acid (98 %) to produce the thioxanthone (1). The 2,7-(disulfonyl phosphine imine) thioxanthone (4-8) were prepared from reaction of compound (1) with chlorosulfonic acid gave 2,7-(disulfonyl chloride) thioxanthone (2). Treatment of (2) with sodium azide to produce 2,7-(disulfonyl azide) thioxanthone (3). Condensation of (3) with phosphorus compounds afforded compounds (4-8). The 2,7-(disulfonamide) thioxanthone (9-21) was obtained when co