Background: to evaluate the effect of different dentifrices on the surface roughness of two composite resins (nanofilled-based and nanoceramic – based composite resins). Materials and methods: Forty specimens (diameter 12 mm and height of 2mm) prepared from different composite resin materials: Z350 (nanofilled composite, and Ceram-X (nanoceramic) .they were subjected to brushing simulation equivalent to the period of 1 year. The groups assessed were a control group brushed with distilled water (G1), Opalescence whitening toothpasteR (G2), Colgate sensitive pro-relief (G3) and Biomed Charcoal Toothpaste (G4). The initial and final roughness of each group was tested by surface roughness tester. The results were statistically analyzed using

The study aims to identify the symptoms of PTSD among displaced Yazidi women according to age, marital status, educational level, and type of status (displaced or survivor). The study also seeks to identify the effect of the relaxation program on reducing PTSD among displaced Yazidi women. The research sample included (60) Yazidis for the statistical analysis sample and (5) for the experimental sample in the Dohuk governorate. For achieving the research objectives, a scale was used from the PTSD Checklist for DSM-5 (PCL-5), as well as a relaxation program was prepared. The researchers reached the following results that there is an average level of PTSD symptoms among displaced Yazidi women, there are no statistically significant differen

A Laboratory study was conducted in quality control department ,state company for food stuff trading ministry of trade (2005-2006) on sunflower oil imported to Iraq from different origins included 12 trade marks, Complete random design was used with four replication .The purpose of the study is to know the origins effect on fatty acid percent and study the simple correlation between them, the result showed Turkish origin for trademark (Narin) was superior in Palmitic and Stearic fatty acid (10.41,3.29%).While Omanian origin for trademark Alsafwa was superior in Oleic(35.09%) and Syrian origin for trade mark Alnahraen was superior in Linoleic fatty acid percent 66.53% whereas Egyptian origin for trademark Alasel was superior in the percent

Fresh water production from saline or waste water utilizing solar stills is the secured future approach in water industry with low cost and no environmental pollution accompanied with low productivity. In this work, the effect of inserting different available materials in a passive Single Slope Solar SSS stills on their productivity is accomplished. Side by side tests are performed on a conventional still, and three SSS stills inserted with carbon filter media, Copper wire mesh, and Cellulose sheets. All these stills are symmetrical in dimensions with 0.5 m2 base area tested for 20mm water level. The stills have been manufactured, instrumented, and tested in July 2021 under DhiQar-Iraq climate conditions (latitude 31.2° N, longitude 46.34

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3

A successful synthesis of mesoporous Santa Barbara amorphous (SBA-15) with nanoparticle size was attempted using prepared sodium silicate from Iraqi high silica sand. EO20PO70EO20 copolymer was used as a template at highly acidic conditions (pH < 2). The effect of crystallization temperature of (100, 110, 120, and 130 0C), and crystallization time of (24, 48, 72, and 120 h) on surface properties was studied. The experiments were characterized using XRD, FTIR, AFM, BET, and FESEM. The XRD and FTIR tests represent amorphous SBA-15 without any impurities. Decreasing average particle size distribution increased the surface area, and decreased the porosity (pore volume, and pore size) in all experiments. The texture properties were su