The present study aimed to synthesize selenium nanoparticles (SeNPs) using aqueous extract of black currant as a reducing agent. The green synthesized black currant selenium nanoparticles (BCSeNPs) were identified by color change. The characterization of SeNPs was achieved by Ultraviolet-visible (UV–VIS) spectroscopy, scanning electron microscopy (SEM), X–ray diffraction analysis (XRD), and Fourier transform infrared spectroscopy (FTIR). These tests were used to detect: stability, morphology, size, crystalline nature, and functional groups present on the surface of BCSeNPs. The results revealed appearance of the brick-red color indicating the specific color of selenium nanoparticles, and UV-Vis spectroscopy showed band absorbanc

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed re

The operating characteristics of optoelectronic devices depend critically on the properties physical of the constituent materials, interesting compound has been focused on this research formed from group III and V of the periodic table. Thin film n-InSb heterjuntion were successfully fabricated on p-Si substrates by thermal evaporation technique at different annealing temperature (as prepared, 400,500,600) °C. The effect of annealing temperature on the structural, surface morphology, optical and optoelectronic properties of InSb films were investigated and studied. The crystal structure of the film was characterized by X-ray diffraction and techniques. AFM techniques inspect the surface morphology of InSb films, the study presented the val

The presence of alkaloids in Crassula ovata is a topic that is still unexplored, as there are no published studies on the matter. This study demonstrates the presence of an alkaloid compound (and its class) for the first time in Crassula ovata. The plant material was defatted with n-hexane, and a Soxhlet apparatus was used for the extraction process, while the acid-base method was used for the isolation of alkaloids from the chloroform fractions. The quaternary alkaloid was precipitated from the aqueous layer spontaneously, in high quantity. By using standard spectroscopic methods (including liquid chromatography - mass spectroscopy) we were able to clarify the structure of the precipi¬tated compound as a tetrahydroprotoberberine a

In the present work, 9-fluorenone-2-carboxylic acid methyl ester (1) was prepared from 9-fluorenone-2-carboxylic acid and then converted into the acid hydrazide (2). Compound (2), is the key intermediate for the synthesis of several series of new compounds such as substituted 1,3,4-oxadiazole derivatives (3-6) were synthesized from the condensation of different substituted benzoic acids with compound (2) using POCl3 as condensing agent. Treatment of compound (2) with formic acid gave the N-formyl hydrazide (7), which upon refluxing with phosphorous pentoxide in benzene yielded the corresponding 5-(9-fluorenone-2-yl)-1,3,4-oxadiazole (8). Reaction of hydrazide (2) with phenyl isocyanate to give N-phenyl semicarbazide derivative (9), then thi

Porous Silicon (PS) layer has been prepared from p-type silicon by electrochemical etching method. The morphology properties of PS samples that prepared with different current density has been study using atom force measurement (AFM) and it show that the Layer of pore has sponge like stricture and the average pore diameter of PS layer increase with etching current density increase .The x-ray diffraction (XRD) pattern indicated the nanocrystaline of the sample. Reflectivity of the sample surface is decrease when etching current density increases because of porosity increase on surface of sample. The photolumenses (PL) intensity increase with increase etching current density. The PL is affected by relative humidity (RH) level so we can use

Nanocrystalline aluminophosphate AlPO₄-5 molecular sieves were synthesized by hydrothermal method (HTS). Synthesis parameters like time and temperature of crystallization were investigated. Type of template (R) and ratio of R/P₂O₅ were studied also. Characterization of the synthesized AlPO₄-5 were done by powder X-ray diffraction (XRD), scanning electron microscopy (SEM/EDX), Fourier transform infrared (FTIR), differential scanning calorimetry-thermogravimetry analysis (DSC-TGA), and N₂ adsorption-desorption BET analysis. XRD patterns results showed excellent crystallinity for two types of templates, di-n-propylamine (DPA) and tetrapropyl ammonium hydroxide (TPAOH) f