The effect of approaching nozzle jet from the deposition surface
on structural, optical and morphology properties of copper oxide thin
films was studied. The film was prepared by homemade fully
computerized CNC spray pyrolysis deposition technique at
preparations speed (3, 4, 5, and 6 mm/sec). The repeated line mode
was used at deposition temperature equal 450 °C whereas the
spraying time was in the range of (15-30 min) according to the
deposition speed. The film exhibit polycrystalline structure with
preferred orientation along (-111), (022) and (011), (002) at a 2θ
value of (35.63o) and (38.8o) respectively. Optical band gaps were
recorded at these speed shows variance in value from (1.53-2.08 eV).
Fi

The concepts of higher Bi- homomorphism and Jordan higher Bi- homomorphism have been introduced and studied the relation between Jordan and ordinary higher Bi- homomorphism also the concepts of Co- higher Bi- homomorphism and  Co- Jordan higher Bi- homomorphism introduced  and the relation between them in Banach algebra have also been studied.

Light soaking (LS) is widely employed to optimize CdTe-based solar cells, yet its microscopic origin remains controversial due to the entangled roles of illumination and thermal activation. Here, we establish a decoupled experimental strategy that independently disentangles light exposure and heating, revealing their fundamentally distinct and competing effects on defect dynamics in CdSeTe solar cells. Illumination alone induces a backward drift of acceptors under the light-enhanced built-in field, reducing apparent hole density and suppressing open-circuit voltage. In contrast, thermal activation promotes Cu redistribution toward the front junction and eliminates deep recombination centers, partially restoring device performance. Remarka

In this research, deposition of titanium oxide (TiO₂) and vanadium oxide (V₂O₅) thin film  in different mixing percentage  (0, 25 ,50, 75 and100)%   on the substrate of glass .The coating thickness was ( 50 nm  ).

In this research contact angle was measured and the effect of weather conditions. Results showed that the value of the contact angle of the prepared films reached its highest value at 50% (TiO₂+V₂O₅) was 160º.

The results showed that the optical transmittance of TiO₂ and V₂O₅ thin film decrease with increasing the deposition angle and decrease with increasing V₂O₅ pro

The effect of heat treatment on the optical properties of the bulk heterojunction blend nickel (II) phthalocyanine tetrasulfonic acid tetrasodium salt and Tris (8-hydroxyquinolinato) Aluminum (NiPcTs/Alq3) thin films which prepared by spin coating was described in this study. The films coated on a glass substrate with speed of 1500 rpm for 1.5 min and treated with different annealing temperature (373, 423 and 473) K. The samples characterized using UV-Vis, X ray diffraction and Fourier transform Infrared (FTIR) spectra, XRD patterns indicated the presence of amorphous and polycrystalline blend (NiPcTs/Alq3). The results of UV visible shows that the band gap increase with increasing the annealing temperature up to 373 K and decreases with

􀀤􀁅􀁖􀁗􀁕􀁄􀁆􀁗􀀑􀀃􀀬􀁑􀀃􀁗􀁋􀁌􀁖􀀃􀁕􀁈􀁖􀁈􀁄􀁕􀁆􀁋􀀏􀀃􀀤􀁊􀀤􀁏􀀔􀀐􀁛􀀬􀁑􀁛􀀶􀁈􀀕􀀃􀀋􀀤􀀤􀀬􀀶􀀌􀀃􀁆􀁒􀁐􀁓􀁒􀁘􀁑􀁇􀀃􀁄􀁏􀁏􀁒􀁜􀁖􀀃􀁓􀁕􀁈􀁓􀁄􀁕􀁈􀁇􀀃􀁉􀁒􀁕􀀃􀁇􀁌􀁉􀁉􀁈􀁕􀁈􀁑􀁗􀀃􀁛􀀃􀀋􀀓􀀑􀀖􀀏􀀃􀀓􀀑􀀙􀀃􀁄􀁑􀁇􀀃􀀓􀀑􀀜􀀌􀀃􀁅􀁜􀀃􀁐􀁈􀁏􀁗􀁌􀁑􀁊􀀃 􀁗􀁋􀁈􀁐􀀃 􀁌􀁑􀀃 􀁄􀁑􀀃 􀁈􀁙􀁄􀁆􀁘􀁄􀁗􀁈􀁇􀀃 􀁔􀁘􀁄􀁕􀁗􀁝􀀃 􀁗􀁘􀁅􀁈􀀃 􀀋􀀕􀀑􀀘􀀍􀀔􀀓􀀐􀀖􀀃 􀁗􀁒􀁕􀁕􀀌􀀑􀀃 􀀤􀀤􀀬􀀶􀀃 􀁚􀁌􀁗􀁋􀀃 􀁇􀁌􀁉􀁉