Background: Glass ionomers have good biocompatibility and the ability to adhere to both enamel and dentin. However, they have certain demerits, mainly low tensile and compressive strengths. Therefore, this study was done to assess consistency and compressive strength of glass ionomer reinforced by different amount of hydroxyapatite. Materials and Methods: In this study hydroxyapatite materials were added to glass ionomer cement at different ratios, 10%, 15%, 20%, 25% and 30% (by weight). The standard consistency test described in America dental association (ADA) specification No. 8 was used, so that all new base materials could be conveniently mixed and the results would be of comparable value and the compressive strength test described by British standard specification for zinc polycarboxylate cement was used in this study. Results: Different consistencies of materials produced a disc of varying sizes. The amount of the powder (in milligram) was mixed with 0.5 ml of liquid to produce a consistency giving a disc of 3 cm±1mm in diameter were 500 mg for glass monomer cement, 450 mg for glass ionomer cement reinforced by 10%, 5% and 30% of hydroxyapatite and 350 mg for glass ionomer cement reinforced by 20% and 25% of hydroxapatite. The results showed that the glass ionomer cement reinforced by hydroxyapatite has higher compressive strength than conventional glass ionomer. Conclusion: The addition of hydroxyapatite to conventional glass ionomer requires less powder to liquid ratio. Addition of hydroxyapatite to glass ionomer cement increased its compressive strength.
mixtures of cyclohexane + n-decane and cyclohexane + 1-pentanol have been measured at 298.15, 308.15, 318.15, and 328.15 K over the whole mole fraction range. From these results, excess molar volumes, VE , have been calculated and fitted to the Flory equations. The VE values are negative and positive over the whole mole fraction range and at all temperatures. The excess refractive indices nE and excess viscosities ?E have been calculated from experimental refractive indices and viscosity measurements at different temperature and fitted to the mixing rules equations and Heric – Coursey equation respectively to predict theoretical refractive indices, we found good agreement between them for binary mixtures in this study. The variation of th
... Show More
<p class="0abstract">Image denoising is a technique for removing unwanted signals called the noise, which coupling with the original signal when transmitting them; to remove the noise from the original signal, many denoising methods are used. In this paper, the Multiwavelet Transform (MWT) is used to denoise the corrupted image by Choosing the HH coefficient for processing based on two different filters Tri-State Median filter and Switching Median filter. With each filter, various rules are used, such as Normal Shrink, Sure Shrink, Visu Shrink, and Bivariate Shrink. The proposed algorithm is applied Salt& pepper noise with different levels for grayscale test images. The quality of the denoised image is evaluated by usi
... Show More
(4)
(2)
A solar cell was manufactured from local materials and was dyed using dyes extracted from different organic plants. The solar cell glass slides were coated with a nano-porous layer of Titanium Oxide and infused with two types of acids, Nitric acid and Acetic acid. The organic dyes were extracted from Pomegranate, Hibiscus, Blackberry and Blue Flowers. They were then tested and a comparison was made for the amount of voltage they generate when exposed to sunlight. Hibiscus sabdariffa extract had the best performance parameters; also Different plants give different levels of voltage.
(7)
(4)
(1)
(6)
Background: Esthetic treatment is the options of patient seeking orthodontic treatment. Therefore this study was conducted to measure the concentration of Aluminum, Nickel, Chromium and Iron ions released from combination of monocrysralline brackets with different arch wires immersed in artificial saliva at different duration, to evaluate the corrosion point on different parts of the orthodontic appliances before and after immersion in artificial saliva, and to evaluate the corrosion potential of each group of the orthodontic appliances. Material and methods: Eighty orthodontic sets prepared. Each set represents half fixed orthodontic appliance, from the central incisor to the first molar, for the maxillary arch, each set consisted of molar
... Show MoreObjective:This study involved synthesis of a new series of different five-membered heterocyclic derivatives, testing their antioxidant activity, and examining their potential in vitro antimicrobial agents. Methods: The synthesis of the derivatives involved a three-step process. Initially, succinyl chloride was reacted with methanol, followed by a reaction with 80% hydrazine hydrate through a nucleophilic addition-elimination mechanism, resulting in the formation of succinohydrazide (I). This compound was then employed as a precursor for the synthesis of Schiff bases (II), and (III) by reacting it with m-nitro benzaldehyde and p-nitro benzaldehyde. Following this, a ring closure reaction was applied using thioglycolic acid, glycolic acid,
... Show More
(1)
Background: The marginal seal is essential for sealant success because penetration of bacteria under the sealant might allow caries onset or progression. The aim of the present study was to estimate and compare the microleakage of pit and fissure sealant after various methods of occlusal surface preparation. Materials and methods: Thirty non-carious premolars extracted for orthodontic reasons were equally divided into three groups. In group one, occlusal fissures were opened with round carbide bur, in group two, occlusal surfaces of the teeth were cleaned with a dry pointed bristle brush and samples of group three were cleaned with a slurry of fine flour of pumice in water using rubber cup. Then fissures of all teeth were etched using 35% p
... Show More