The present study included  the impact of the follow-up variation in the temperature of aqueous medium in the vertical migration behavior of different groups of Zooplankton, consisted species Cyclops vernalis, Daphnia magna, Diaptomus dilopatus, that have been grown in controlled in terms of light and pH laboratory conditions, so choosing temperature of respectively 16,20,24,28, and 32 ËšC. The result showed a clear change in the migration behavior of testing planktonic species, it was a negative relationship between temperatures arises and individual of D. magna in the water column.While being appositive relationship with individual of C. vernalis and the same with D. dilopatus. Also, the result revealed a different impact

The reliability of optical sources is strongly dependent on the degradation and device characteristics are critically dependent on temperature. The degradation behaviours and reliability test results for the laser diode device (Sony-DL3148-025) will be presented .These devices are usually highly reliable. The degradation behaviour was exhibited in several aging tests, and device lifetimes were then estimated. The temperature dependence of 0.63?m lasers was studied. An aging test with constant light power operation of 5mW was carried out at 10, 25, 50 and 70°C for 100hours. Lifetimes of the optical sources have greatly improved, and these optical sources can be applied to various types of transmission systems. Within this degradation range,

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

When employing shorter (sub picosecond) laser pulses, in ablation kinetics the features appear which can no longer be described in the context of the conventional thermal model. Meanwhile, the ablation of materials with the aid of ultra-short (sub picosecond) laser pulses is applied for micromechanical processing. Physical mechanisms and theoretical models of laser ablation are discussed. Typical associated phenomena are qualitatively regarded and methods for studying them quantitatively are considered. Calculated results relevant to ablation kinetics for a number of substances are presented and compared with experimental data. Ultra-short laser ablation with two-temperature model was quantitatively investigated. A two-temperature model

The stability and releasing profile of 2:1 core: wall ratio ibuprofen microcapsules prepared by aqueous coacervation (gelatin and acacia polymers coat) and an organic coacervation methods (ethyl cellulose and sodium alginate polymers coat) in weight equivalent to 300mg drug, were studied using different storage temperatures 40°C, 50°C ,60°C and refrigerator temperature 4°C in an opened and closed container for three months (releasing profile) and four months (stability study).It was found that, these ibuprofen microcapsules were stable with expiration dates of 4.1 and 3.1 years for aqueous and an organic method respectively.Aqueous prepared ibuprofen microcapsules were found more stable than those microcapsules prepared by or

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

120 samples were collected from children (ages between new born and 10 years) who infected with oral thrush. The results revealed that the Minimum Inhibitory Concentration (MIC) and Minimum Fungicidal Concentration (MFC) of extracted oil of lemon grass against C.albicans, C.tropicalis, C.keyfr, C.glabrata and C.guilliermondii were 1.25,1.25,1.25,2.5 and 2.5µl/ml and 2.5, 2.5, 2.5, 5 and 5 µl /ml respectively. while the (MIC) and (MFC) for the extraction oil of thyme against C.albicans, C.tropicalis, C.keyfr, C.glabrata and C.guilliermondii were 0.6, 0.6, 1.25, 1.25, and 1.25µl/ml and 1.25, 1.25, 2.5, 2.5, and 2.5µl/ml respectively . While the value of (MIC) and (MFC) for Nystatin against Candida species were 32 and 64 µg

 Abstract

In order to determine what type of photovoltaic solar module could best be used in a thermoelectric photovoltaic power generation. Changing in powers due to higher temperatures (25^oC, 35^oC, and 45^oC) have been done for three types of solar modules: monocrystalline , polycrystalline, and copper indium gallium (di) selenide (CIGS). The Prova 200 solar panel analyzer is used for the professional testing of three solar modules at different ambient temperatures; 25^oC, 35^oC, and 45^oC and solar radiation range 100-1000 W/m². Copper indium gallium (di) selenide module   has the lowest power drop (with the average percent

Tea is one of the important liquids that people drink. In Iraq, tea is the main beverage after water. The tea plant is known scientifically as Camellia sinensis, when planting and during growth needs to fertilizers, which contents remarkable amounts of Uranium. So it became important to study the concentrations of uranium found in tea. Eight samples of tea had been taking, which represent the most important species used in the Iraqi kitchen, and the Uranium concentrations were measured. The results showed that the average concentration of uranium for all samples were1.005 mg/L, while the average of the annual effective dose was 0.221 mSν/y. The results also indicated that green tea possesses small concentration of Uranium compared with