One of the most important problems in tablet process is to control the flow of the catalyst through the hopper; Controlling the flow can be done either by changing the size of particles or added the different lubricant (stearic acid, starch, graphite) or blending of different lubricants. The study showed that we can control (increase or decrease) on the flow of the catalyst through the hopper by blending different lubricants for the constant percentage. The flow increasing when particles size (0.6 mm) and then decrease with or without lubricants, no effect on flow when particles size lower than (0.2 mm) with use that lubricants, and good flow on (0.4 mm) when use stearic acid and starch.

Copper oxide thin films were deposited on glass substrate using Successive Ionic Layer Adsorption and Reaction (SILAR) method at room temperature. The thickness of the thin films was around 0.43?m.Copper oxide thin films were annealed in air at (200, 300 and 400°C for 45min.The film structure properties were characterized by x-ray diffraction (XRD). XRD patterns indicated the presence of polycrystalline CuO. The average grain size is calculated from the X-rays pattern, it is found that the grain size increased with increasing annealing temperature. Optical transmitter microscope (OTM) and atomic force microscope (AFM) was also used. Direct band gap values of 2.2 eV for an annealed sample and (2, 1.5, 1.4) eV at 200, 300,400oC respect

A two-year study (harvest years 2019 and 2020) was conducted to investigate the effect of a commercially available biofertilizer, in combination with variable nitrogen (N) rate, on bread baking quality and agronomic traits in hard winter wheat grown in conventional (CONV) and organic (ORG) farming systems in Kentucky, USA. The hard red winter wheat cultivar ‘Vision 45’ was used with three N rates (44, 89.6 and 134.5 kg/ha as Low, Med and High, respectively) and three biofertilizer spray regimes (no spray, one spray and two sprays). All traits measured were significantly affected by the agricultural production system (CONV or ORG) and N rate, although trends in their interactions were inconsistent between years. In Y2, yield was

In the present work, the effect of isolated dust particles (FeO) with radius of the grain 0.1μm - 0.5μm of main plasma characteristics are investigated experimentally in direct current system by using magnetic field. The present of dust particle in the air plasma did effect on Paschen minimum and on the plasma properties in low pressure region. The effect of dust particles on discharge voltage, discharge current, plasma potential, floating potential, electron density, electron temperature and Debye length was investigation by using magnetic field. The measurements of parameters are taken by four cylindrical Langmuir probes. The results show the present of dust causes decreasing in discharge voltage with increase pressure while the disc

 A pots experiment was conducted in the plastic house of Kalar Horticulture station Province of Sulaimania, by using soil brought from one of Kalar region fields during growing season of 2007-2008, to study the effect of increasing levels of urea fertilizer which is           (0, 0.20,0.40,0.80) g/pot which equals to (0,100,200,400) kg urea/ha, and super phosphate fertilizer which is (0,0.24,0.48)gm/pot which is equal (0,120,240) kg sup/ha, in nutrition state of wheat IPA 95 component, clay determining  Nitrogen, Phosphor and Potassium content in green part and seeds.        The Completely Randomized Design was used with three replication per t

In this study, SnO2 nanoparticles were prepared from cost-low tin chloride (SnCl2.2H2O) and ethanol by adding ammonia solution by the sol-gel method, which is one of the lowest-cost and simplest techniques. The SnO2 nanoparticles were dried in a drying oven at a temperature of 70°C for 7 hours. After that, it burned in an oven at a temperature of 200°C for 24 hours. The structure, material, morphological, and optical properties of the synthesized SnO2 in nanoparticle sizes are studied utilizing X-ray diffraction. The Scherrer expression was used to compute nanoparticle sizes according to X-ray diffraction, and the results needed to be scrutinized more closely. The micro-strain indicates the broadening of diffraction peaks for nano

Field and laboratory experiments were conducted during the course of study to
test if the sunflower residues along or with 50% full rate of trifluralin herbicide has
any impact on mycorrhizal association and soil nitrification which are important
processes for improving growth and productivity of crops. Results revealed that
incorporation of sunflower residues significantly increased spores number at 2, 4
and 6 weeks of residue decomposition compared to control treatment. However,
when the residues applied in combination with reduced rate of trifluralin herbicide,
sporulation was appreciably decreased by sunflower residues at 3 t ha-1 but it
remains almost the same at 6 t ha-1 rate of residues. Field soil amended

The aim of this work is to evaluate some mechanical and physical
properties (i.e. the impact strength, hardness, flexural strength,
thermal conductivity and diffusion coefficient) of
(epoxy/polyurethane) blend reinforced with nano silica powder (2%
wt.). Hand lay-up technique was used to manufacture the composite
and a magnetic stirrer for blending the components. Results showed
that water had affected the bending flexural strength and hardness,
while impact strength increased and thermal conductivity decreased.
In addition to the above mentioned tests, the diffusion coefficient
was calculated using Fick’s 2nd law.

A thin CdS Films have been evaporated by thermal evaporation technique with different thicknesses (500, 1000, 1500 and 2000Å) and different duration times of annealing (60, 120 180 minutes) under 573 K annealing temperature, the vacuum was about 8 × 10-5 mbar and substrate temperature was 423 K. The structural properties of the films have been studied by X- ray diffraction technique (XRD). The crystal growth became stronger and more oriented as the film thickness (T) and duration time of annealing ( Ta) increases.