Study the Structural Properties of Porous Silicon and their Applications as Thermal Sensors
...Show More Authors

The photo-electrochemical etching (PECE) method has been utilized to create pSi samples on n-type silicon wafers (Si). Using the etching time 12 and 22 min while maintaining the other parameters 10 mA/cm2 current density and HF acid at 75% concentration.. The capacitance and resistance variation were studied as the temperature increased and decreased for prepared samples at frequencies 10 and 20 kHz. Using scanning electron microscopy (SEM), the bore width, depth, and porosity % were validated. The formation of porous silicon was confirmed by x-ray diffraction (XRD) patterns, the crystal size was decreased, and photoluminescence (PL) spectra revealed that the emission peaks were centered at 2q of 28.5619° and 28.7644° for etching time 12 and 22 min, respectively. Studying the capacitance and resistivity during temperature increasing and decreasing for both itching times shows clearly that the prepared pSi as a thermal sensor is working better and in more selectivity for 20 min itching time

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Wed Dec 30 2015
Journal Name
College Of Islamic Sciences
Phonological features   For spoken text in the language
...Show More Authors

This research attempted to take advantage of modern techniques in the study of the superstructural phonetic features of spoken text in language using phonetic programs to achieve more accurate and objective results, far from being limited to self-perception and personal judgment, which varies from person to person.
    It should be noted that these phonological features (Nabr, waqf, toning) are performance controls that determine the fate of the meaning of the word or sentence, but in the modern era has received little attention and attention, and that little attention to some of them came to study issues related to the composition or style Therefore, we recommend that more attention should be given to the study of

... Show More
View Publication Preview PDF
Publication Date
Wed Jun 01 2022
Journal Name
Iranian Journal Of Chemistry And Chemical Engineering
The Thermal Pre-processing Technique of the Bio-waste for Contaminated Water Treatment: Histological and Experimental Study
...Show More Authors

The current study suggested a thermal treatment as a necessary proactive step in improving the adsorption capacity of bio-waste for contaminants removal in wastewater. This approach was based on the experimental and histological investigation of biowaste pods shell. This investigation showed that these shells compose of parenchyma cells that store secondary metabolites compounds produced from cells were exhibited in present study. The results also reported that these compounds are extracted directly from the cells as soon as they are exposed to an aqueous solution, hampering their use as an adsorbent material. The increase in the weight of bio-waste adsorbent at unit liquid volume increases the production of secondary metabolites compounds

... Show More
View Publication
Publication Date
Sat Jul 02 2022
Journal Name
Journal Of Inorganic And Organometallic Polymers And Materials
Effect of Glycerin on Electrical and Thermal Properties of PVA/Copper Sulphate Gel Polymer Electrolytes
...Show More Authors

View Publication
Scopus (17)
Crossref (17)
Scopus Clarivate Crossref
Publication Date
Thu Sep 01 2016
Journal Name
Journal Of Saudi Chemical Society
Synthesis and investigation of thermal properties of vanadyl complexes with azo-containing Schiff-base dyes
...Show More Authors

Azo-Schiff base compounds (L1 and L2) have been synthesized from the reaction of m-hydroxy benzoic acid with 1,5-dimethyl-3-[2-(5-methyl-1H-indol-3-yl)-ethylimino]-2-phenyl-2,3- dihydro-1H-pyrazol-4-ylamine and with 3-[2-(1H-indol-3-yl)-ethylimino]-1,5-dimethyl-2-phenyl- 2,3-dihydro-1H-pyrazol-4-ylamine. The free ligands and their complexes were characterized based on elemental analysis, determination of metal, molar conductivity, (1H, 13C) NMR, UV–vis, FT-IR, mass spectra and thermal analysis (TGA). The molar conductance data revealed that all the complexes are non-electrolytes. The study of complex formation via molar ratio in DMF solution has been investigated and results were consistent to those found in the solid complexes with a rat

... Show More
View Publication Preview PDF
Scopus (39)
Crossref (29)
Scopus Clarivate Crossref
Publication Date
Thu Feb 27 2020
Journal Name
Iraqi Journal Of Science
Impact of ZnO Atomic Ratio on Structural, Morphological and Some Optical Properties of (SnO2)1-x (ZnO)x Thin Films
...Show More Authors

In this work, SnO2 and (SnO2)1-x(ZnO)x composite thin films with different ZnO atomic ratios (x=0, 5, 10, 15 and 20%) were prepared by pulsed laser deposition technique on clean glass substrates at room temperature without any treatment. The deposited thin films were characterized by x-ray diffraction atomic force microscope  and UV-visible spectrophotometer to study the effect of the ZnO atomic ratio on their structural, morphological and optical properties. It was found that the crystallinety and the crystalline size vary according to ZnO atomic ratio. The surface appeared as longitudinal structures which was convert to spherical shapes with increasing ZnO atomic ratio. The optical trans

... Show More
View Publication Preview PDF
Scopus (2)
Crossref (1)
Scopus Crossref
Publication Date
Thu Jun 30 2011
Journal Name
Al-khwarizmi Engineering Journal
Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
...Show More Authors

A comprehensive practical study of typical mechanical properties of welded Aluminum alloy AA7020-T6 (Al-Mg-Zn), adopting friction stir welding (FSW) technique and conventional metal inert gas (MIG) technique, is well achieved in this work for real comparison purposes. The essences of present output findings were concentrated upon the FSW samples in respect to that MIG ones which can be summarized in the increase of the ultimate tensile strength for FSW was 340 MPa while it was 232 MPa for MIG welding, where it was for base metal 400 MPa. The minimum microhardness value for FSW was recorded at HAZ and it was 133 HV0.05 while it was 70 HV0.05 for MIG weld at the welding metal. The FSW produce 2470 N higher than MIG welding in the bending t

... Show More
View Publication Preview PDF
Publication Date
Tue Dec 11 2018
Journal Name
Iraqi Journal Of Physics
Effect of annealing temperature on structural and optical properties of Cr2O3 thin films by PLD
...Show More Authors

In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Mon Feb 18 2019
Journal Name
Iraqi Journal Of Physics
Effect of annealed temperature on some structural, optical and mechanical properties of selenium thin film
...Show More Authors

In this paper a thin films of selenium was prepare on substrates of n-Si by evaporation in a vacuum technique with thickness about 0.5μm. And then an annealing process was done on samples at two temperature (100 and 200) C ° in a vacuum furnace (10-3 torr).
Some structural, optical and mechanical properties of prepared thin films were measured. Results showed that the prepared film was the crystallization, optical transmittance and micro hardness of the prepared thin films increased significantly after annealing.

View Publication Preview PDF
Crossref
Publication Date
Sat Dec 01 2018
Journal Name
Al-khwarizmi Engineering Journal
Experimental and Numerical Investigation for Simulation of Thermophysical Properties for Polypropylene 575 Polymer Melts in Single Screw Extruder
...Show More Authors

A numerical model for Polypropylene 575 polymer melts flow along the solid conveying screw of a single screw extruder under constant heat flux using ANSYS-FLUENT 17.2 software has been conducted. The model uses the thermophysical properties such as Viscosity, thermal conductivity, Specific heat and density of polypropylene 575 that measured as a function of temperature, and residence time data for process simulation. The numerical simulation using CFD models for single screw extruder and the polymer extrusion was analysed for parameters such as (thermal conductivity, specific heat, density and viscosity) reveals a high degree of similarity to experimental data measured. The most important outcome of this study is that geometrical, parame

... Show More
View Publication Preview PDF
Crossref
Publication Date
Tue Jan 14 2020
Journal Name
College Of Islamic Sciences
The Origin of Creation in Khattab (The Beginning of Creation) by Imam Ali (as) and Genesis (Comparative Study)
...Show More Authors

The research aims to answer the questions that revolve in the mind of mankind about how to create creation, how it existed prior to creation, who created existence, and the characteristics of that presence. The researcher also wanted to show that the culture of Imam Ali (peace be upon him) In the book of Adam, peace be upon him, God has punished Adam (peace be upon him) for not having sinned. Because his wife is the one who fed him the fruit of the tree, and this is contrary to what was stated in the sermon of Imam (peace be upon him) who Z Adam (peace be upon him) is the one who trusted Satan and Gwighth.We note that the approach of the rhetoric has pointed to the creation of angels and did not refer to the creation of Eve and the class

... Show More
View Publication