Polymer electrolytes were prepared using the solution cast technology. Under some conditions, the electrolyte content of polymers was analyzed in constant percent of PVA/PVP (50:50), ethylene carbonate (EC), and propylene carbonate (PC) (1:1) with different proportions of potassium iodide (KI) (10, 20, 30, 40, 50 wt%) and iodine (I₂) = 10 wt% of salt. Fourier Transmission Infrared (FTIR) studies confirmed the complex formation of polymer blends. Electrical conductivity was calculated with an impedance analyzer in the frequency range 50 Hz–1MHz and in the temperature range 293–343 K. The highest electrical conductivity value of 5.3 × 10^-3 (S/cm) was observed for electrolytes with 50 wt% KI concentration at room

  This study included prepared samples of epoxy reinforced by the novolac , aluminum , glass powder and epoxy reinforced by aluminum , glass powder and epoxy alone .They are used as reinforced materials of volum fraction amounting 40% .  The mechanical properties inclouded ( tensile , compressive and wear) where the wear test inclouded different applied loads (5,10,15) . From the results showed the epoxy reinforced by aluminum and glass powder has higher compressive strength (56.91) Mpa and higher tensile strength (132.2) Mpa .But the epoxy alone has higher wear rate and the epoxy reinforced by aluminum and glass powder which have higher elasticity of modulus from the tensile test (315.7) Mpa

The Reversed Phase High Performance Liquid Chromatography (RP-HPLC) has been used for the separation of Poly aromatic hydrocarbons(PAHs) by using column Reprosil 100 C 18 which was found to be a suitable one for this purpose. The result showed that using mobile phase of (Acetonitrile-water) Reversed Phase HPLC , flow rate of (1.2 ml/min) , column temperature (30CËš) and wave length of (254nm), give a complete separation with a good resolution . The total separation time was less than 20 min. The result of the study showed that the vegetables of Baghdad city were polluted by poly aromatic hydrocarbons(PAHs) in different places where samples taken because of drainage of the heavy water ,industrial trash and trash of oil colanders. -

The Reversed  Phase High Performance Liquid  Chromatography (RP-HPLC) has been used for the separation of  Poly aromatic hydrocarbons(PAHs) by using column Reprosil 100 C 18 which  was found to be a suitable one for this purpose. The result showed that using mobile phase of (Acetonitrile-water) Reversed Phase HPLC , flow rate  of (1.2 ml/min) , column temperature (30CËš) and wave length of (254nm), give a complete separation with a good resolution . The total separation time was less than 20 min. The result of the study showed that the vegetables of Baghdad city were   polluted by poly aromatic hydrocarbons(PAHs) in different places where samples taken because of drainage  of the heavy water ,ind

The semiconductor ZnO is one of II – VI compound group, it is prepare as thin films by using chemical spray pyrolysis technique; the films are deposited onto glass substrate at 450 °C by using aqueous zinc chloride as a spray solution of molar concentration 0.1 M/L. Sample of the prepared film is irradiating by Gamma ray using CS 137, other sample is annealed at 550°C. The structure of the irradiated and annealed films are analyzed with X-ray diffraction, the results show that the films are polycrystalline in nature with preferred (002) orientation. The general morphology of ZnO films are imaged by using the Atomic Force Microscope (AFM), it constructed from nanostructure with dimensions in order of 77 nm.
The optical properties o

Gypseous soils represented one of the most complex salty soils that faced the geotechnical engineers. Structures that built on gypsum soil will undergo unexpected distortions that will eventually contribute to catastrophic failure. The purpose of this article is to understand the durability of gypsum soil against wetting drying cycles after improvement with polyurethane polymer especially investigate the effect of the wetting-drying cycle on collapsibility. The soil was brought from Sawa lake in AL-Muthanna Governorate in Iraq, with gypsum content 65.5%,  A set of Odometer tests were performed to determine the collapsibility potential (CP) for treated and untreated gypsum soil.  The result shows that adding a different per

Polymers have the ability to extract water after they have been added to the mortar or concrete mixture. They provide the absorbed water during hydration functioning as internal water source. Absorption polymers can absorb up to hundred times of their own weight of pure water.This research deals with the use of water absorption polymer balls in concrete and study the volumetric change of these mixes and compared the results with reference mix (without polymers). Samples were cured both in air and in water for the mixes to compare results which show that samples in air behave for expansion while sample in water acted for shrinkage.