􀀑􀀃Pure Cu (CZTSe) and Ag dopant CZTSe (CAZTSe) thin films with Ag content of 0.1 and 0.2 were fabricated on coring glass substrate at R.T with thickness of 800nm by thermal evaporation method. Comparison between the optical characteristics of pure Cu and Ag alloying thin films was done by measuring and analyzing the absorbance and transmittance spectra in the range of (400-1100)nm. Also, the effect of annealing temperature at 373K and 473K on these characteristics was studied. The results indicated that all films had high absorbance and low transmittance in visible region, and the direct bang gap of films decreases with increasing Ag content and annealing temperature. Optical parameters like extinction coefficientrefractive index, and

The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved

 Zinc oxide (ZnO) transparent thin films with different oxygen flow rates (0.5, 1.0, and 1.5)Litter/min. were prepared by thermal evaporation technique on glass substrate at a temperature of 200℃ with rate (10±2)nm sec-1,  The crystallinity and structure of these films were analyzed  by X-ray diffraction (XRD). It exhibits a polycrystalline hexagonal wurtzite structure and the preferred orientation along (002) plane. The Optical properties of ZnO were determined through the optical transmission method using ulta violet–Visible spectrophotometer with in wave length (300-1100)nm. The optical transmittance of the ZnO films increases from 75% to 85% with increase flow rate of O2, and the optical band gap of ZnO

The synthesis, characterization and mesomorphic properties of two new series of triazine-core based liquid crystals have been investigated. The amino triazine derivatives were characterized by elemental analysis, Fourier transforms infrared (FTIR), 1HNMR and mass spectroscopy. The liquid crystalline properties of these compounds were examined by differential scanning calorimetry (DSC) and polarizing optical microscopy (POM). DSC and POM confirmed nematic (N) and columnar mesophase textures of the materials. The formation of mesomorphic properties was found to be dependent on the number of methylene unit in alkoxy side chains.

A novel series of chitosan derivatives were synthesized via reaction of chitosan with carbonyl compounds and grafted it’s by with different amine compounds substituted hydrogen. The produced polymers were characterized by different analyses FTIR, 1HCNMR, XRD, DSC and TGA. Solubility in water as well as many solvent was investigated, antibacterial activity of chitosan and its derivatives against two types of bacteria E. coli and S. aureus was also investigated. The results showed that derivatives sort of have antibacterial activities against Esherichia coli (Gram negative) better than chitosan whilst compound IX has better antibacterial against Staphylococcus aureus (Gram positive). SEM analysis showed that increase of surface roughness wi

A novel series of chitosan derivatives were synthesized via reaction of chitosan with carbonyl compounds and grafted it’s by with different amine compounds substituted hydrogen. The produced polymers were characterized by different analyses FTIR, 1HCNMR, XRD, DSC and TGA. Solubility in water as well as many solvent was investigated, antibacterial activity of chitosan and its derivatives against two types of bacteria E. coli and S. aureus was also investigated. The results showed that derivatives sort of have antibacterial activities against Esherichia coli (Gram negative) better than chitosan whilst compound IX has better antibacterial against Staphylococcus aureus (Gram positive). SEM analysis showed that increase of surface roughness wi

In this research , phthallic anhydride ring is opened with 4-methyl aniline and acetone as a solvent to results the compound [I] that reacted with dimethyl sulphate and anhydrous sodium carbonate formation to phathalate ester [II], while the acid hydrazide compound [III], was obtained from mixed the compound [II]with hydrazine hydrate, Synthesis four type of shiff bases[IV]a-d was synthesized from the reaction of acid hydrazide [III] with aromatic aldehyde or ketone , when reacted Shiff bases with phthalic anhydride or naphthalicanhydride,I get eight derivatives of oxazepine [V]a-d , [VI]a-d. The bacterial activity of the new compounds studied by four species of bacteria: Esherichia Coli, Enterobactecloacae (Gram negative) and staphylococcu

Using photo electrochemical etching technique (PEC), porous silicon (PS) layers were produced on n-type silicon (Si) wafers to generate porous silicon for n-type with an orientation of (111) The results of etching time were investigated at: (5,10,15 min). X-ray diffraction experiments revealed differences between the surface of the sample sheet and the synthesized porous silicon. The largest crystal size is (30 nm) and the lowest crystal size is (28.6 nm) The analysis of Atomic Force Microscopy (AFM) and Field Emission Scanning Electron Microscope (FESEM) were used to research the morphology of porous silicon layer. As etching time increased, AFM findings showed that root mean square (RMS) of roughness and po

      In this research, the structural and optical properties were studied for Bi2O3 and Bi2O3: Al  thin  films  with   different  doping   ratios  ( 1, 2, 3 ) %  ,  which  were  prepared  by  thermal evaporation  technique under  vacuum , with  thickness  ( 450 ± 20 ) nm  deposited  on  glass substrates  at  room  temperature ( 300 ) K , Structural   measurements by ( XRD)  techniques demonstrated   that  all   samples  prepared   have  polycrystalline  structure   with  tetragonal structure and  a preferred orientation  [ 201 ]   the &n

In this study, Cobalt Oxide nanostructure was successfully prepared using the chemical spray pyrolysis technique. The cobalt oxide phase was analysed by X-ray Diffraction (XRD) and proved the preparation of two cobalt oxide phases which are Co3O4 and CoO phases. The surface morphology was characterized by Scanning Electron Microscope (SEM) images showing the topography of the sample with grain size smaller than 100 nm. The optical behavior of the prepared material was studied by UV-Vis spectrophotometer. The band gap varied as 1.9 eV and 2.6 eV for Co3O4 prepared from cobalt sulphate precursor, 2.03 eV and 4.04 eV for Co3O4 prepared from cobalt nitrate precursor, 2.04 eV and 4.01 eV for CoO prepared from cobalt chloride precursor where th