Low cost Co-Precipitation  method was used for Preparation of novel nickel oxide (NiO) nano particle thin films with Simple, with two different PH values 6, 12 and its effect on structural and optical properties as an active optical filter. Experimental results of structural properties X-ray diffraction (XRD) showed that both Nickel oxide nanoparticles with (PH=6 and 12) have polycrystalline structure smaller average particle size about 8.5 nm for PH=6 in comparison with PH=12. Morphological studies using Scanning electron microscopy (SEM) and  atomic force microscope (AFM)  show uniform nano rod distribution for PH=6 with smaller average diameter, average roughness as compared with NiO with

  To enlighten the extent of crude oil pollution effects on some anatomical characteristics of olive plant (Olea europaea ). Two years - old seedlings were chosen to grow under 5 levels of pollution (0.0, 0.5, 1.0, 2.0, and 3.0, liter/ plant). The experiment has been conducted in the experimental field of Natural History Research Center and Museum, University of Baghdad. It was designed as CRD experiment. Testing wood specimens were prepared after 2.5 years of growth. Fiber length, width, wall thickness, and wood specific gravity were measured. Results showed that olive plants could not resist the highest level ( 3 liters / plant ) of pollution .Fiber length was the most  affected property by treatment. All fiber dimensions wer

     In this study, the electron energy distribution function (EEDF), the electron swarm parameters , the effective ionization coefficients, and the critical field strength (dielectric strength) in binary He-H₂ gas mixture which is used as cryogenic for high-temperature superconducting power applications,  are evaluated using two-term solution  of the Boltzmann equation over the range of E/N ( the electric field to gas density) from 1 to 100 Td ( 1 Td=10^-17 Vcm²) at temperature 77 K and pressure 2MPa, taking into account elastic ( momentum transfer) and inelastic cross-sections. Using the electron energy distribution function (EEDF) electron swarm parameters (electron drift velocity, mean electron e

The aim of this study was to evaluate tensile properties of low and medium carbon ferrite -martensite dual phase steel, and the effect cryogenic treatment at liquid nitrogen temperature (-196 ºC) on its properties. Low carbon steel (C12D) and medium carbon steels (C32D & C42D) were used in this work. For each steel grade, five groups of specimens were prepared according to the type of heat treatment. The first group was normalized, the second group was normalized and subsequently subjected to cryogenic treatment then tempered at (200 ºC) for one hour, the third group was quenched from intercritical annealing temperature of (760 ºC) to obtain dual phase (DP) steel, the fourth and fifth groups were both quenched from (760 ºC), but

InSb alloy was prepared then InSb:Bi films have been prepared successfully by thermal evaporation technique on glass substrate at Ts=423K. The variation of activation energies(Ea1,Ea2)of d.c conductivity with annealing temperature (303, 373, 423, 473, 523 and 573)K were measured, it is found that its values increases with increasing annealing temperature. To show the type of the films, the Hall and thermoelectric power were measured. The activation energy of the thermoelectric power is much smaller than for d.c conductivity and increases with increasing annealing temperature .The mobility and carrier concentration has been measured also.

This work study the effect of laser surface heat treatment on physical properties (green density, density after sintering, theoretical density and porosity)of a composite material of an Al powder as a matrix with different percentage of B4C powder as additive material. This work was done by two stages: First stage: Production the maincomposite material which is contain Al powder with grain size 24μm as a matrix and B4C powder with grain size 50μm as additive with different weight percentage (5%,10%,15%,20%,25%,30%), and the powders Maxined for suitable time 15min, after that the mixture compacted with 2ton and sintered at 550C0. Second stage: Laser surface treatment was done for the productive composite material after sintering by usin

Abstract Additive manufacturing has been recently emerged as an adaptable production process that can fundamentally affect traditional manufacturing in the future. Due to its manufacturing strategy, selective laser melting (SLM) is suitable for complicated configurations. Investigating the potential effects of scanning speed and laser power on the porosity, corrosion resistance and hardness of AISI 316L stainless steel produced by SLM is the goal of this work. When compared to rolled stainless steel, the improvement is noticeable. To examine the microstructure of the samples, the optical microscopy (OM), scanning electron microscopy (SEM), and EDX have been utilized. Hardness and tensile strength were us