This study aims to investigate the degree of practicing the motivated classroom evaluation environment for learning and its relationship to different feedback patterns. To achieve the objectives of the study, the correlational descriptive research design was employed. A questionnaire was constructed consisting of two parts: the classroom evaluation environment (13) items, and feedback patterns (24) items on a five-point scale. The psychometric properties of the questionnaire were verified in terms of validity and reliability. The questionnaire was applied to a sample of (265) male and female teachers who work in the second cycle schools for grades (5-10) of basic education in all academic majors in the Governorate of Muscat in the Sultan

Abstract

In the present work, thermal diffusivity and heat capacity measurements have been investigated in temperature range between RT and 1473 K for different duplex stainless steel supplied by Outokumpu Stainless AB, Sweden. The purpose of this study is to get a reliable thermophysical data of these alloys and to study the effect of microstructure on the thermal diffusivity and heat capacity value. Results show the ferrite content in the duplex stainless steel increased with temperature at equilibrium state. On the other hand, ferrite content increased with increasing Cr/Ni ratio and there is no significant effect of ferrite content on the thermal diffusivity value at room temperature. Furthermore, the heat capacity of all sam

Background: To evaluate the bony supports of the teeth adjacent to the area of cleft in patient with unilateral cleft lip and palate and to compare these measurements with the measurements of the same teeth in non-cleft side by using CBCT. Materials and methods: The CBCT scans of 30 patients having cleft lip( unilateral) and palate(unilateral), were analyzed and the measurements of the alveolar bony support for teeth that are adjacent to the cleft area were measured with those teeth located on opposite side (non- clef) side. For each tooth, the measurements will taken for the distance between the( cementoenamel junction) (CEJ) and the bony crest (AC) at the( buccal area) was measured and the thickness of the buccal plate At zero, one, tw

The research aims to develop physical exercises with auxiliary training tools that work to develop the explosive power of the arms and legs, and then find out their effect on the accuracy of shooting from free throw and correction from jumping of advanced basketball players, as the researchers found a problem that these players have weakness in the skill of throwing Free throwing and shooting by jumping calculated with two points as a result of adopting unhealthy physical and technical positions, which led to a lack of focus and accuracy, and thus negatively affected the performance technique of free throw and jump shot, as most teams use traditional exercises without the use of auxiliary training tools, and this topic gave researchers the

Cold atmospheric plasma (CAP) is used widely in medical and biological fields because of non-thermal effected. Direct application of plasma is preferred in medical functions, so, direct application of cold plasma has obtained by the floating electrode dielectric barrier discharge (FE-DBD) system. The purpose of this paper to review the effect of (CAP) on the reproductive hormones (testosterone, LH, E2, progesterone, for male rats. The study appeared that no significant effect on E2 and progesterone hormone for all time of exposure, besides this significant difference in LH hormone (P<0.05) at 15 sec, (P<0.0001) at 30, 90 sec and (P<0.001) at 60 sec of exposure to plasma. Added to that significant difference (P<0.01) at 15, 30, 60 sec and no

Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

High performance self-consolidating concrete HP-SCC is one of the most complex types of concrete which have the capacity to consolidated under its own weight, have excellent homogeneity and high durability. This study aims to focus on the possibility of using industrial by-products like Silica fumes SF in the preparation of HP-SCC enhanced with discrete steel fibers (DSF) and monofilament polypropylene fibers (PPF). From experimental results, it was found that using DSF with volume fraction of 0.50 %; a highly improvements were gained in the mechanical properties of HP-SCC. The compressive strength, splitting tensile strength, flexural strength and elastic modulus improved about 65.7 %, 70.5 %, 41.7 % and 80.3 % at 28 days age, respectively

RHS Nasser, NHY Al-Afoun, SPECIALUSIS UGDYMAS, 2022