The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f

The refractive indices, nD densities 𝜌, and viscosities  of binary mixtures of sulfolane + n -butanol + sec- butanol + iso- butanol + tert – butanol + n-propanol and iso- propanol were measured at 298.15K. Form experimental data, excess molar volum VE , excess molar refractivity ∆nD, excess molar viscosity  E and excess molar Gibbs free energy of activation of viscous flow G *E were calculated. From n-propanol – sulfolane and iso- propanol sulfolane mixtures showed negative ∆nD, n-butanol – sulfolane, sec-butanal – sulfolane, iso-butanol – sulfolane and tert- butanol sulfolane , nD was positive over the whole mole fraction rang , while VE ,  E and G *E show a negative deviation. The

Background: Tooth decay is still one of most common diseases of childhood, child’s primary teeth are important even though they aretemporary. This study was conducted to assess the physiochemical characteristic of saliva among caries experience preschool children and compared them with caries free matching in age and gender. Then an evaluation was done about these salivary characteristics to dental caries and evaluated the relation of body mass index to dental caries and to salivary variables. Materials and method: After examination 360 children aged 4-5 years of both gender. Caries-experiences was recorded according to dmfs index by (World Health Organization criteria 1987) during pilot study children with caries experience was di

Iron oxide(Fe3O4) nanoparticles of different sizes and shapes were synthesized by solve-hydrothermal reaction assisted by microwave irradiation using ferrous ammonium sulfate as a metal precursor, oleic acid as dispersing agent, ethanol as reducing agent and NaOH as precipitating agent at pH=12. The synthesized Fe3O4 nano particles were characterized by X-ray diffraction (XRD), FTIR and thermal analysis TG-DTG. Sizes and shapes of Fe3O4 nanoparticles were characterized by Scanning Electron Microscopy (SEM), and atomic force microscopy (AFM).

Background: Pumpkin seeds are a valuable source of high-quality protein and can be utilized as functional food ingredients due to their properties, such as solubility, foam formation, and stability. This study aims to produce protein isolate and its enzymatic hydrolysates from local pumpkin seeds to study their properties. Methodology: Preparing defatted pumpkin seeds for protein extraction, followed by the enzymes’ hydrolysis using Trypsin and Pepsin enzymes separately and together in two methods. The determination of amino acids and the degree of hydrolysis was conducted; moreover, protein properties were studied, including solubility, emulsifying activity, stability index, foaming capacity, and stability. Results: A protein sample was

The increasing requirement and use of dental implant treatments has rendered dental implantology indispensable in dentistry. The aim of this study is to determine the optimum concentration of calcium silicate to be incorporated into a polyetherketoneketone (PEKK) matrix used as an implant material to enhance the bioactivity and mechanical properties of the composite compared with unmodified PEKK. In this study, different weight percentage (wt%) of micro-calcium silicate (m-CS) is incorporated into PEKK with ethanol as a binder. Subsequently, the mixture is dried in a forced convection oven at 120°C and poured into customized molds to fabricate a bioactive composite via compression molding (310°C, 15 MPa, and 20 min holding time

Cadmium has been known to be harmful to human healthy , manily Via contaminated drinking water , food supplies , tobacco and industrial pollutant . The aim of this study was to determine the toxicity of new Cadmium (II) complex ( Bis[ 5- ( P- nitrophenyl ) – ? 4 – Phenyl- 1,2,4- triazole -3- dithiocarbamatohydrazide] cadmium (II) Hydra ( 0.5) and compare it with anticancer drug cyclophosphamide ( CP) in female albino mice . This complex causes to several alterations in Enzymatic activity of Glutamate Pyruvate Transaminase (GPT) and Alkaline Phosphatase (ALP ) in three organs after the treatment of mice with different doses of a new cadmium (II) complex ( 0.09 / 0.25ml , 0.18/ 0.5ml and 0.25mg /0.7 ml /30 gm of mous

Abstract As a part of our ongoing project on the design and synthesis of new 4-thiazolidinone derivatives with antimicrobial activity, four new 4-thiazolidinone derivatives carrying bromo, nitro, methyl, and chloro groups on the benzene ring were synthesized by starting with the 7-amino-4-methylcoumarin moiety, linking coumarin with various phenyl isothiocynate to form the thiourea group, and then cyclizing the derivatives, characterized by IR and 1HNMR, and assayed in vitro for their antimicrobial activity against Gram positive and Gram negative bacteria and fungi. Overall, 2-(4-methyl-2-oxo-2H-chromen-3-yl)-3-(4-nitrophenyl) thiazolidin-4-one to be the most powerful individuals in the series. Based on the observed data, it can be sta