This article reviews the construction of organic solar cell (OSC) and characterized their optical and electrical properties, where indium tin oxide (ITO) used as a transparent electrode, “Poly (3-hexylthiophene- 2,5-diyl) P3HT / Poly (9,9-dioctylfluorene-alt-benzothiadiazole) F8BT” as an active layer and “Poly(3,4-ethylenedioxythiophene)-poly (styrene sulfonate)” PEDOT: PSS which is referred to the hole transport layer. Spin coating technique was used to prepared polymers thin film layers under ambient atmosphere to make OSC.  The prepared samples were characterized after annealing process at (80 ͦ C) for (30 min) under non-isolated circumference. The results show a value of filling factor (FF) of (2.888), (0.233) and (0.28

So far synthesis of Gonadotropin Releasing Hormone (GnRH) analogues reported in the literature has clarified some aspects of structural activity of the naturally released GnRH. As a part of continuing efforts for further understanding of this relationship, the present investigation was undertaken which involved synthesis and biological evaluation of two GnRH analogues, firstly, by replacement of the amino acid L-Argenine in the 8^th position at the backbone structure of the natural hormone by the amino acid D-Alanine; and secondly, by replacement of the amino acid L-Glycine in the 10^th position by D-Alanine also at the backbone structure of the nature hormone, to obtain the following analogues respectively:

P

Background: Acute leukemias (ALs) are a heterogeneous group of malignancies with various clinical, morphological, immunophenotypic, and molecular characteristics. Distinguishing between lymphoid and myeloid leukemia is often performed by flow cytometry. This study aimed to evaluate the immunophenotypic characterization and expression of immuno-markers in both acute myeloid leukemia (AML-M0) and acute T-cell lymphoblastic leukemia (T-ALL).

Methods: A retrospective cross-sectional study was conducted in the Pathology Department/Teaching Laboratories/Medical City/Iraq and included all patients newly diagnosed with AL from 5 January to 10 December 2018. Immunophenotypic analysis wa

This paper details the process of designing, analysing, manufacturing, and testing an integrated solid-state hydrogen storage system. Analysis is performed to optimise flow distribution and pressure drop through the channels, and experimental investigations compare the effects of profile shape on the overall power output from the fuel cell. The storing of hydrogen is given much attention in the selection of a storage medium, and the effect of a cooling system to reduce the recharging time of the hydrogen storage vessel. The PTFE seal performed excellently, holding pressure over 60 bar, despite requiring changing each time the cell is opened. The assembly of the vessel was simple and straightforward, and there was no indication of pressure

Erbium, as optical probe, doped silicate sol-gel glass with
different Er concentrations was formed by wet chemical synthesis
method using ethanol, water and tetraethaylorthosilicate
[Si(OC2H5)4] precursor. Erbium ions were incorporated into silica
sol-gel matrix via dissolution of Erbium chloride solution into the
initial Si(OC2H5)4 precursor sol. Aluminum (Al) as a co-dopant was
added to the final precursor in the form of Aluminum chloride
(AlCl3) solution. The prepared samples were analyzed using atomic
absorption analysis, X-ray diffraction and spectroscopic tests. The
experimental results concerned with the transmission spectra suggest
that the final samples have a good transparency and homogeneity.
A

The chromatographic behaviour of liquid crystalline compounds benzylidene-p-aminobenzoic acid and 4-(p-methyl benzylidene)-p-aminobenzoic acid as stationary phases for the separation of dimethylphenol isomers was investigated. These isomers were analysed on benzylidene-p-aminobenzoic acid within a nematic range of 169-194 ◦C with a temperature interval of 5 ◦C. Better peak resolution was at a column temperature of 190 ◦C. The analysis was repeated on a 4-(p-methyl benzylidene)-p-aminobenzoic acid column at a nematic temperature of 256 ◦C, which represented the end of the nematic range, and gave the optimum peak resolution. It was found that isomer better separation was obtained at 20% loading for both liquid crystal materials. Other