Wheat straw was modified with malonic acid in order to get low cost adsorbent have a good ability to remove copper and ferric ions from aqueous solutions, chemical modification temperature was 120°C and the time was 12 h. Parameters that affect the adsorption experiments were studied and found the optimum pH were 6 and 5 for copper and iron respectively and the time interval was 120 min and the adsorbent mass was 0.1 g. The values for adsorption isotherms parameters were determined according to Langmuir [qmax were 54.64 and 61.7 mg/g while b values were 0.234 and 0.22 mg/l] , Freundlich [Kf were 16.07 and 18.89 mg/g and n were 2.77 and 3.16], Temkin [B were 0.063 and 0.074 j/mol and At were 0.143 and 1.658 l/g] and for Dubinin-Radushkev

KE Sharquie, AA Noaimi, BAM Saleh, 2015

Objective: To assess the functional outcome, time to union, shoulder pain, blood loss, operative time, iatrogenic radial nerve injury, hospitalization, and infection. Methodology: It is a prospective randomized study on 30 patients with mid-shaft humerus fracture according to AO classification (1.2A1, 2, 3 and 1,2B) with functioning radial nerve. They were randomly dividing into two groups. Group A were treated by a closed antegrade interlocking nail, and group B treated by open reduction and locked compression plate fixation. The follow-up was up to 6 months, including time to union, shoulder pain, intraoperative blood loss, operative time and iatrogenic radial nerve injury. Functional outcome was assessed by quick DASH score. Resu

The dispersion of supported Pt and Pt–Ir reforming catalysts have been studied, after treatment with oxidative and reducing atmosphere. Methylcyclohexane dehydrogenation reaction in the absence of hydrogen was used as a test reaction. An attempt was made to relate the behavior of the catalysts upon subject to reaction, to the dispersion of the same type of catalysts upon treatment with similar atmosphere and temperatures which appeared in literature. The total conversion of reaction can be explained by a change in metal dispersion. Thus, methylcyclohexane dehydrogenation reaction appears to be a really “structure sensitive” reaction.

      The toluene yield increases as the oxidation temperature i

Etoricoxib (EXB) is a highly selective cox-2 inhibitor which belongs to the non-steroidal anti-inflammatory drug (NSAID). EXB is a class II drug according to the biopharmaceutical classification system (BCS), which possess a very low aqueous solubility in water.  In the present study, many trials were made to improve the aqueous solubility and dissolution rate of EXB by solid dispersion technique.

Eighteenth EXB formulas were formulated as a solid dispersion using a variety of hydrophilic polymers (as carriers)   including poloxamer 407 (PXM 407), poloxamer 188 (PXM 188) and polyethylene glycol 4000 (PEG 4000) at different drug: polymer ratios (1:1, 1:3 and 1:5). These formulas were prepared by two methods; solvent

Naproxen is a non steroidal anti inflammatory and antipyretic drug which has local irritation effect  on  the  stomach, and  unpleasant taste,  besides bad   flowability and light sensitivity .The drug was prepared as microcapsules by complex coacervation method using acacia-gelatin coating materials , and aqueous colloid polymer dispersion method ( ACPD ), using ethyl cellulose and sodium alginate coating materials . The results indicated that microcapsules prepared by 2:1  core:wall ratio is the best for both methods, with an average encapsulation efficiency (75%) and avarege yield (90%) .

Moreover the drug release was affected mainly by core : ratio ,pH enviroment and method of microenca

Pure and doped TiO 2 with Bi films are obtained by pulse laser deposition technique at RT under vacume 10-3 mbar, and the influence of Bi content on the photocvoltaic properties of TiO 2 hetrojunctions is studied. All the films display photovoltaic in the near visible region. A broad double peaks are observed around λ= 300nm for pure TiO 2 at RT in the spectral response of the photocurrent, which corresponds approximately to the absorption edge and this peak shift to higher wavelength (600 nm) when Bi content increase by 7% then decrease by 9%. The result is confirmed with the decreasing of the energy gap in optical properties. Also, the increasing is due to an increase in the amount of Bi content, and shifted to 400nm when annealed at 523

In this study, a double frequency Q-switching Nd:YAG laser beam (1064 nm and λ= 532 nm, repetition rate 6 Hz and the pulse duration 10ns) have been used, to deposit TiO2 pure and nanocomposites thin films with noble metal (Ag) at various concentration ratios of (0, 10, 20, 30, 40 and 50 wt.%) on glass and p-Si wafer (111) substrates using Pulse Laser Deposition (PLD) technique. Many growth parameters have been considered to specify the optimum condition, namely substrate temperature (300˚C), oxygen pressure (2.8×10-4 mbar), laser energy (700) mJ and the number of laser shots was 400 pulses with thickness of about 170 nm. The surface morphology of the thin films has been studied by using atomic force microscopes (AFM). The Root Mean Sq