Effect of nano and micro SiO2 particles with different weight percent (2,4,6,8 and 10) %wt on the Interlaminar fracture toughness (GIc) of 16-plies of woven roving glass fiber /epoxy composites prepared by hand lay – up technique were investigated. The specimens were tested using DCB test (mode I).
Area method was used to compute the interlaminar fracture toughness. The results show that, GIc would increase with the increasing in the filler content, the main failure in microcomposites and nanocomposites was delamination in the layers, the delamination reduced with increasing in the filler content.

                In this investigation a high density polyethylene (HDPE) was used as a substitute to polyvinylchloride in the production of lead acid battery separators. This has been achieved by preparing mixtures of different percentages of the feed materials which include a high density polyethylene (HDPE) locally produced, filler materials such as silica and oils such as dioctylphthalate (DOP) or paraffin which were added to the mixture to improve the final properties of the separator. The materials were compounded by two roll-mills under the same conditions. The following parameters are involved:           &nb

Cu-Al-Ni shape memory alloy specimens has been fabricated using powder metallurgy technique with tube furnace and vacuum sintering environment , three range of Nb powder weight percentage (0.3,0.6,0.9)% has been added. Micro hardness and sliding wear resist has been tested followed by X-ray diffraction, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDX) for micro structure observation. The experimental test for the samples has showed that the increase of Nb powder weight percentage in the master alloy has a significant effect on increasing the hardness and decreasing the wear resist therefore it will enhance the mechanical properties for this alloy.

Aim: To evaluate the effect of two bonding systems and two curing systems on sealing ability of class V composite restorative materials. Materials and methods: This study was performed in vitro on 40 caries free upper first premolar teeth. The Standardized class V cavity preparation on buccal and lin- gual surfaces of each tooth was done. Then the teeth were randomly divided into two major groups each of twenty. 40 cavities were performed on these teeth and the first group7th generation bonding agent (i Bond) were applied according to the manufacturer instructions and single increment of univer- sal composite (XRV Herculite) from kerr were applied and twenty of the cavities were cured with con- ventional light cure device (astralis-5) and t

Background: A recent discoveries used for reconstruction in maxillofacial surgery is the composite bone graft materials. The availability of collagen I matrix make our choice to use this material in surgery .It is biomaterials that its structure could be modified by simple techniques. Studies to find a new materials use for bone reconstruction is to overcome the disadvantages of autogenous bone and the synthetic resorbable bone substitutes.

Objectives: This study was done to evaluate the effect of biphasic calcium phosphate collagen composite (ccpc) on healing of bone defects after oral surgical procedures.

Type of the study: A cross sectional study.

Method: It involved 60 patients, 35 male and 25 female, age (15-

In the present work the Buildup factor for gamma rays were studied in shields from epoxy reinforced by lead powder and by aluminum powder, for NaI(Tl) scintillation detector size ( ×? ), using two radioactive sources (Co-60 and Cs-137). The shields which are used (epoxy reinforced by lead powder with concentration (10-60)% and epoxy reinforced by aluminum powder with concentration (10-50)% by thick (6mm) and epoxy reinforced by lead powder with concentration (50%) with thick (2,4,6,8,10)mm. The experimental results show that: The linear absorption factor and Buildup factor increase with increase the concentration for the powders which used in reinforcement and high for aluminum powder than the lead powder and decrease with inc

A Laboratory study was conducted in quality control department ,state company for food stuff trading ministry of trade (2005-2006) on sunflower oil imported to Iraq from different origins included 12 trade marks, Complete random design was used with four replication .The purpose of the study is to know the origins effect on fatty acid percent and study the simple correlation between them, the result showed Turkish origin for trademark (Narin) was superior in Palmitic and Stearic fatty acid (10.41,3.29%).While Omanian origin for trademark Alsafwa was superior in Oleic(35.09%) and Syrian origin for trade mark Alnahraen was superior in Linoleic fatty acid percent 66.53% whereas Egyptian origin for trademark Alasel was superior in the percent

Spent catalysts for sulfuric acid production have large amount of vanadium and due to environmental authority it is required to reduce the vanadium contain of the spent catalyst. Experimental investigation was conducted to study the vanadium recovery from spent catalyst via leaching process using sodium hydroxide to study the effect of process variables (temperatures, sodium hydroxide molarities, leaching time and particle size) on vanadium recovery. The effect of process variables (temperature, particle size,molarities of sodium hydroxide and leaching time) on the percentages of vanadium recovery were investigated and discussed .It was found that the percentage of vanadium recovery increased with increasing temperature up to 100 , incre

Background: Poly-ether-ether-ketone(PEEK) has been introduced to many dental fields. Recently it was tested as a retainer wire‎ following orthodontic treatment. This study aimed to investigate the effect of changing the bonding spot size and location on the performance of PEEK retainer wires. Methods: A biomechanical study involving four three-dimensional finite element models was performed. The basic model was with a 0.8 mm cylindrical cross-section PEEK wire, bonded at the center of the lingual surface of the mandibular incisors with 4 mm in diameter composite spots. Two other models were designed with 3 mm and 5 mm composite sizes. The last model was created with the composite bonding spot of the canine away from the center of t

Background: Poly-ether-ether-ketone(PEEK) has been introduced to many dental fields. Recently it was tested as a retainer wire‎ following orthodontic treatment. This study aimed to investigate the effect of changing the bonding spot size and location on the performance of PEEK retainer wires. Methods: A biomechanical study involving four three-dimensional finite element models was performed. The basic model was with a 0.8 mm cylindrical cross-section PEEK wire, bonded at the center of the lingual surface of the mandibular incisors with 4 mm in diameter composite spots. Two other models were designed with 3 mm and 5 mm composite sizes. The last model was created with the composite bonding spot of the canine away from the center