PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom

Experimental investigations had been done in this study to demonstrate the effect of natural particles used as a reinforcement material to unsaturated polyester resin. The tensile test and water absorption were investigated according to (ASTM D638) and (ASTM D570), respectively. The influence of sunflower husk and pomegranate husk particles, used as a reinforcement material, on the tensile strength, Young's modulus and water absorption with different weight fraction (3%, 7% and 10%) and particle grain size (50µm, 100 µm and 150 µm), has been investigated. The water absorption of polymer composites was studied by measuring the specimen weight before and after immersion in water for one hundred days. In the experiments of tensile test,

In this research we study the effect of UV radiation on pure PC samples and doped samples with plasticizer (DOP) for different exposure times (6, 12, 18, 24h). The study have been made on the change in the IR spectra causes by the UV radiation on both kinds of samples, besides the morphology changes were also studied by the optical microscope. From the results we conclude that the increasing of exposure causes the elaboration of CO₂ and C₂ gases.

In this research, we prepared a hybrid composite material of polymeric matrix hand cast method, composite material has been attended from epoxy resin EP as matrix materials reinforced woven roving fiber jute is constant volume fraction (13%), PVC fibers and woven glass fiber with different fraction on the properties of prepared composite materials to PVC fiber and glass fiber, some of mechanical tests were done at room temperature (impact test and banding test). Result shows that the values of (modulus bending elastic and fracture toughness) increase fraction of fiber with the increase of PVC, E-glass, there include (thermal conductivity and dielectric constant). Also experimental result indicated that the (thermal conductivity and diele

 

This work targeted studying organogel as a potential floating system. Organgel has an excellent viscoelastic properties, floating system posses a depot property.  Different formulations of 12-hydroxyoctadecanoic acid (HOA) in sesame oil were gelled and selecting F1, F3 and F5 HOA organogels for various examinations: tabletop rheology, optical microscopy, and oscillatory rheology studies. Also, the floating properties studies were conducted at in vitro and in-vivo levels. Lastly, the in-vitro release study using cinnarizine (CN) was to investigate the organogel depot property. Based on the results, the selected concentrations of HOA in sesame oil organogels showed temperature transitions fr

Introduction: This study was designed to examine the effects of addition of the combination of polymerized polymethyl methacrylate (PMMA) and zirconia (ZrO2) particles to heat cure PMMA resin on impact strength, surface hardness, and roughness. Methods: The 70% (w/w) of polymerized PMMA powder (particle size: 0.70mm) was mixed with 30% (w/w) of zirconia powder (ZrO2) (1mm) to produce PMMA-ZrO2 filler. Ninety acrylic specimens created were divided into three groups containing 0% wt (Control group), 2% wt, and 4% wt, PMMA-ZrO2 filler. Ten specimens were used for impact strength, surface hardness and roughness test, blindly. Data were analyzed via oneway ANOVA and the Tukey post hoc test using R 3.6.3. Results: There was statistically signific

In this study, Laser Shock Peening (LSP) effect on the polymeric composite materials has been investigated experimentally. Polymeric composite materials are widely used because they are easy to fabricate and have many attractive features. Unsaturated polyester resin as a matrix was selected and Aluminum powder with micro particles as a reinforcement material was used with different volume fraction (2.5%, 5% and 7.5%). Hand lay-up process was used for preparation the composites. Fatigue test with constant amplitude with stress ratio (R =-1) was carried out before and after LSP process with two levels of energy (1Joule and 2Joule). The result showed an increase in the endurance strength of 25.448% at 7.5% volume fraction when peened is 1J

     Heavy metal ion removal from industrial wastewater treatment systems is still difficult because it contains organic contaminants. In this study, functional composite hydrogels with photo Fenton reaction activity were used to decompose organic contaminants. Fe₃O₄ Nanoparticle, chitosan (CS), and other materials make up the hydrogel. There are different factors that affected Photo-Fenton activity including (pH, H₂O₂ conc., temp., and exposure period). Atomic force microscopy was used to examine the morphology of the composite and its average diameter (AFM). After 60 minutes of exposure to UV radiation, CS/ Fe₃O₄ hydrogel composite had degraded methylene blue (M.B.)

In this study, epoxy was used as a matrix for composite materials, with E-glass fiber, jute and PVC fiber which was woven roving fiber, as reinforcement with volume fraction (Vf= 30%). There are two of prepared types of epoxy non reinforced, epoxy reinforced with E-glass, jute and PVC fibers including study of mechanical tests (Impact test, Bending test) different temperature and thermal conductivity and calculating the temperatures coefficient at different temperature. Results show that elastic modulus at rate values decrease to the increase of temperature and the impact strength, impact energy and thermal conductivity increase with increase temperature.

Asthma is a chronic respiratory disorder in which immunological and structural cells play a role. The limits of conventional medicines necessitate the development of innovative therapeutic techniques for asthma. In the present study, we investigated the possible protective effect of cinnamic acid (CA) on ovalbumin-induced asthma in a mouse model. Sixty albino male mice BALB/c type weighing (20-30) grams were chosen at random and divided into five groups each one contains 12 animal: Group I: PBS/liquid paraffin control. Group II: asthma model group. Group III: cinnamic acid control group; mice received cinnamic acid (50 mg/kg) in liquid paraffin orally by gavage. Group IV: asthma model / group of (25 mg / kg) cinnamic acid; mice received