The concept of epiform modules is a dual of the notion of monoform modules. In this work we give some properties of this class of modules. Also, we give conditions under which every hollow (copolyform) module is epiform.

Rates of zinc consumption during cathodic protection of a copper pipeline carrying saline water were measured by the loss in weight technique. The study of sacrificial anode cathodic protection of short copper tube using zinc strip extended axially in the pipe revealed that : (i) The increase of zinc consumption with time of exposure (1-3 h's) at different flow rates (turbulent flow) (300-600 l/hr) while the temperature , solution concentration and the pH were fixed at 20ºC, 3.5%wt NaCl, and pH=8 respectively in absence and presence of bacteria.(ii)Increase of zinc consumption with flow rates (300-600 l/hr) at different temperatures (10-40ºC) while solution concentration and time of exposure were fixed at 3.5 %wt NaCl and 3hr's respective

Rates of zinc consumption during cathodic protection of a copper pipeline carrying saline water were measured by the loss in weight technique. The study of sacrificial anode cathodic protection of short copper tube using zinc strip extended axially in the pipe revealed that : (i) The increase of zinc consumption with time of exposure (1-3 h's) at different flow rates (turbulent flow) (300-600 l/hr) while the temperature , solution concentration and the pH were fixed at 20ºC, 3.5%wt NaCl, and pH=8 respectively in absence and presence of bacteria.(ii)Increase of zinc consumption with flow rates (300-600 l/hr) at different temperatures (10-40ºC) while solution concentration and time of exposure were fixed at 3.5 %wt NaCl and 3hr's respect

Abstract

This work involves studying corrosion resistance of AA 6061T6 butt welded joints using Two different welding processes, tungsten inert gas (TIG) and a solid state welding process known as friction stir welding, TIG welding process carried out by using Rolled sheet of thickness6mm to obtain a weld joint with dimension of (100, 50, 5) mm using ER4043 DE (Al Si₅) as filler metal and argon as shielding gas, while Friction stir welding process carried out using CNC milling machine with a tool of rotational speed 1000 rpm and welding speed of 50mm/min to obtain the same butt joint dimensions. Also one of weld joint in the same dimensions subjected to synergistic weld

Results showed high efficiency of the predator Chrysoperla carnea (Stephens) to attack and consume nymphal instars and adults of cabbage aphid, Brevicoryne brassicae (L.).The total average of the nymphal instars consumed by the larval stage of predator were 308.67, 285.9, 198.77, 154.7 for 1st ,2nd ,3rd ,4th nymphal instars respectively .While it was 110,107.9 for apterae and alatae respectively . Also, predation efficiency increases with the progress of the larval instars up to the third (last) which was the most voracious .The 1st instar nymph consumed by the larvae of the predator were 47,80,181.67 nymphs ,with predation rate of 14.71% , 23.75% and 50.13% for 1st ,2nd and 3rd larval instars

Some metal ions (Mn+2, Co+2, Ni+2, Cu+2,Zn+2 and Cd+2) complexes of quodridentats Schiff base derived from (2-hydroxy benzaldehyde and 4,4'-methylenedianiline as primary ligand and 3-picoline (3-pic) secondary ligand have been synthesized and characterized on the basis of their 1H ,13C-NMR, FT-IR, UV-Vis spectroscopy, conductivity measurements, elemental analysis, and magnetic moments, metal to ligands ratio in all complexes has been found to be (1:1:2) (M:Schiff base:3-pic), Schiff base behaves as neutral tetra dentate ligand with (N2,O2) system from the results obtained, the following general formula has suggested for the prepared complexes [M+2(2-mbd)(3-pic)2] and octahedral stereochemistry, Where M+2 = (Mn , Co , Ni , Cu , Zn and Cd), 2

Background: Alginate impression material is the irreversible hydrocolloid material that is widely used in dentistry. The contact time between alginate and gypsum cast could have a detrimental effect on the properties of the gypsum cast. The objective of this study is to evaluate the impact of various contact time intervals of Alginate impressions & type III dental stone on surface properties of stone cast. Materials and Methods: Time intervals tested were 1hour, 6 hours and 9 hours. Surface properties of stone cast evaluated were surface detail reproduction, hardness and roughness. Surface detail reproduction was determined using cylindrical brass test block in accordance with ISO 1563. Surface roughness was measured by profilometer