The crystal compounds Tl2-xAg2-ySryBayCa2Cu3O10+& are successfully prepared in different concentrations (x, y=0.1, 0.2, 0.3, 0.4, 0.5) by solid state reaction process. The samples were then subjected to Nano technique under hydrolic pressure 8 ton/cm2. samples have been annealed in (850 C0) for 72 hours. The results show a best value at x, y=0.3 ratio of Ag, Ba. Electrical resistivity at x, y= 0.3 of Ag, Ba are obtained when the best value of Tc= 141 K. Samples morphology were also observed by AFM (in three dimensions), the best value of Nano is 91.74 nm at x, y= 0.3. Morphological structures of the surface were also observed by (SEM) and (EDX) show that there are dark regions and light which indicate the presence of heavy elements a

The purpose of this study is to deal with dust and interstellar molecular and atomic gas owing to obtaining a proportion of cold gas to dust and to understand the characteristics of the molecular gas in extragalactic data selected from the Herschel SPIRE/ FTS archive. The physical properties of a sample of 65 extragalactic spectra characterized by the activity of star formation were discussed in this work. Statistical analyses, using STATISTICA program, were made for the content of cold gas (MHI, MH₂), dust mass (M_dust), cold temperature of dust (T_d) and luminosities in Far-infrared to CO line radiations, while coefficients of partial correlation within those characteristics were established. The results

This work presents a five-period chaotic system called the Duffing system, in which the effect of changing the initial conditions and system parameters d, g and w, on the behavior of the chaotic system, is studied. This work provides a complete analysis of system properties such as time series, attractors, and Fast Fourier Transformation Spectrum (FFT). The system shows periodic behavior when the initial conditions xi and yi equal 0.8 and 0, respectively, then the system becomes quasi-chaotic when the initial conditions xi and yi equal 0 and 0, and when the system parameters d, g and w equal 0.02, 8 and 0.09. Finally, the system exhibits hyperchaotic behavior at the first two conditions, 0 and 0, and the bandwidth of the chaotic

The optical transmission and UV-VIS absorption spectra have been recorded in the wavelength range (200-1100m) for different composition of polyaniline and polyvinyl Alcohol(PVA ) blends thin films. Polyaniline was prepared in acidic medium to enhancement the solubility and processibility, The optical energy gap (Eopt) refractive index and optical dielectric constant real and imaginary part have been evaluated. The effects of doping percentage of prepared polyaniline on these parameters was discussed and the non –linear behavior for all these parameters was investigated.

New hydrazide compounds (A2) and (A9) were prepared from their corresponding esters (A1, A8) .These esters were also prepared from their precursors 5-ethoxy carbonyl-(4methoxyphenyl)-6-methyl-1,2,3,4-tetrahydropyrimidine-2-thione (A1) via multicomponent reaction type and from hippuric acid respectively. The hydrazide compounds were then allowed to react with some aldehydes forming the corresponding hydrazones (A3-7) and (A1014). The synthesized compounds were characterized by IR, 1H-NMR, 13C-NMR, and Mass spectroscopies and well discussed. .

       The Sr doped La1Ba1-xSrx Ca2Cu4O8.5+δ samples with 0 ≤ x ≤ 0.3 had been prepared using the solid state reaction. The samples were claimed at 800°C for 3hr, palletized and sintered at 860°C for 20hr in air . Dielectric constant and loss by means of capacitance have been investigated with frequencies in the range of 1kHZ to 1MHZ for our samples at room temperature. Also, Shore hardness has been measured. The dielectric constant and loss decrease slightly with the increase of frequency for all compounds. Additionally, the partial substitution of Sr+2 into Ba+2 sites never have effect on the dielectric properties. X-ray diffraction (XRD) analysis showed a tetragonal structure and the

In Baghdad governorate, samples of dried birds waste were obtained from poultry cages for investigate the of the presence of fungi. There was a high proportion of Candida spp., Rhodotorula spp. and filamentous fungi that obtained from the dry droppings. Al samples gave a positive results included 177 isolates, these isolates includes different Candida species 62 isolates (35.02%), Rhodotorula spp. 28 isolates (15.81%), and the following filamentous genera: Aspergillus spp. 50 isolates (28. 24%), (A. niger 20 isolate, A. flavus 18 isolate, A. fumigatus 12 isolate), Penicillium spp. 11 isolates (6.21%) and Mucor spp. 26 isolate (14.68%). The inhibitory effect of the used detergents (with concentration of 10-1 mg/ml.( was ranged from 35 mm

The aim of research is to show the effect of Ferric Oxide (Fe2O3) on the electricity production and wastewater treatment, since 2.5% of Ferric Oxide (Fe2O3) (heated and non heated) nanoparticles has been used. Characterization of nanoparticles was done using X-ray Diffraction (XRD) and Scan Electron Microscopy (SEM). The influence of acidity was also studied on both wastewater treatmenton the Chemical Oxygen demand (COD) and Biological Oxygen Demand (BOD) and voltage output was studied. From the results, it was infused that the dosage of 0.025 g/l and an initial pH 7 were founded to be optimum for the effective degradation of effluents. The results concluded that the treatment of anaerobic sludge wastewater using Ferric Oxide (Fe2O3) in

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b