In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850^oC) using single screw extruder and a mixing machine operated at a temperature between (190-200^oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength

‎تم في هذه الدراسة ، تزيين ‏رقائق أكسيد الجرافين (‏GO‏) بجسيمات ‏كوبلتيت النيكل النانوية ‏NiCo2O4‎‏(‏NC‏) عن طريق الترسيب في ‏الموقع ، وتم استخدام المتراكب ‏المحضر (‏NC: GO‏) كسطح ماز لإزالة ‏صبغة الميثيل الخضراء ( ‏MG‏) من ‏المحاليل المائية. تم التحقق من ‏التغطية الناجحة لأوكسيد الجرافين ‏بجزيئات كوبلتيت النيكل النانوية ‏‏(‏NC‏) باستخدام دراسات ‏FT-IR‏ وحيود ‏الأشعة السينية (‏XRD‏). كانت أحجام  ‏الجسيم

In the cuurent article, the photophysical properties of 3,6-bis(5-bromothiophen-2-yl)-2,5-bis(2-ethylhexyl)-2,5-dihydropyrrolo[3,4-c]pyrrole-1,4-dione were investigated. The visible absorption bands at 527, 558 and 362 nm in propylene carbonate and the compound was found to be fluorescent in solution and in the plastic film with emission wavelengths between 550- 750 nm. The Stokes Shift of P.C., acetonitrile, diethyl ether, Tetrahydrofuran THF, cyclohexane, dibutyl ether, and dichloromethane DCM  are 734, 836, 668, 601, 601, 719, and 804 cm^-1 in respectively. The Stokes Shift Δ was less in THF and cyclohexane, than the solvents, which indicates that the energy loss is less between the excitation and fluorescence states. The

Background: Studying and investigating the transverse strength(Ts), impact strength(Is), hardness (Hr) and surface roughness(Ra) of conventional and modified autopolymerizing acrylic resin with different weight percentages of biopolymer kraftlignin, after curing in different water temperatures; 40°C and 80°C. Material and Methods: Standard acrylic specimens were fabricated according to ADA specification No.12 for transverse strength, ISO 179 was used for impact testing, Shore D for hardness and profilometerfor surface roughness. The material lignin first dispersed in the monomer, then the powder PMMA is immediately added. Ligninadded in different weight percentages. Then cured using pressure pot (Ivomet) in two temperatures;40°C a

In this research, the kinetic studies of four isoenzymes of Asprtate aminotransferase, which partially purified from the urine of chronic renal failure patients were carried out .The four isoenzymes were obeyed Michaelis-Menton's equation and the optimum concentration of their substrate (Aspartic acid) was (166.5x10-3) mole/liter,and their Km values were determined. Four isoenzymesI,II,III,IV have shown an optimum pH at 7.4.The four isoenzymes obeyed Arrhenius equation up to 37º C and their Ea and Q10 constants were determined .

The present article discusses the synthesis of tetradentate Schiff base complexes formed by the condensation reaction of 2-hydroxy benzaldehyde and phthalohydrazide. The ligand (LH2) was detected using FT-IR spectra, 1H, 13C-NMR, UV-Vis spectroscopy, elemental microanalysis CHN, and mass spectrometry. The obtained solid complexes have been assessed using physicochemical and spectroscopic techniques, including UV-Vis, FT-IR, nuclear magnetic resonance (1H-NMR, 13C-NMR), mass spectrometry, thermal gravimetric analysis (TGA), and atomic absorption, in addition to complex conductivity and magnetic moment measurements. The infrared results demonstrated that ligands functioning as tetradentate ligands are chelated to metal ions via the ph