Thermal pyrolysis kinetics of virgin high-density polyethylene (HDPE) was investigated. Thermal pyrolysis of HDPE was performed using a thermogravimetric analyzer in nitrogen atmosphere under non-isothermal conditions at different heating rates 4, 7, 10 °C/min. First-order decomposition reaction was assumed, and for the kinetic analysis Kissinger-Akahira-Sunose(KAS), Flynn-Wall-Ozawa(FWO) and Coats and Redfern(CR) method were used. The obtained values of  average activation energy by the KAS and FWO methods were equal to137.43 and 141.52 kJ/mol respectively, these values were considered in good agreement, where the  average activation energy value obtained by CR equation methods was slightly different which equal to 153.16 kJ/

Background: Many types of instruments and techniques are used in the instrumentation of the root canal system. These instruments and techniques may extrude debris beyond the apical foramen and may cause post-instrumentation complications. The aim of this study was to evaluate the amount of apically extruded debris resulted by using 4 types of nickel-titanium instruments (WaveOne, TRUShape 3D conforming files, Hyflex CM, and One Shape files) during endodontic instrumentation. Materials and methods: Forty freshly extracted human mandibular second premolar with straight canals and a single apex were collected for this study. All teeth were cut to similar lengths. Pre-weighted glass vials were used as collecting containers. Samples were randoml

Intrinsic viscosities have been studied for polyethylene oxide in water which has wide industrial applications. The polyethylene oxide samples had two different structures, the first one was linear and covers a wide range of molecular weight of 1, 3, 10, 20, 35, 99, 370, 1100, 4600, and 8000 kg/mol and the second one was branched and had molecular weights of 0.55 and 40 kg/mol.
Intrinsic viscosities and Huggins constants have been determined for all types and molecular weights mentioned above at 25ºC using a capillary viscometer. The values of Mark-Houwink parameters (K and a) were equal to 0.0068 ml/g and 0.67 respectively, and have not been published for this range of molecular weight in as yet.

Objectives Dental implant is a revolution in dentistry; some shortages are still a focus of research. This study use long duration of radiofrequency (RF)–magnetron sputtering to coat titanium (Ti) implant with hydroxyapatite (HA) to obtain a uniform, strongly adhered in a few micrometers in thickness. Materials and Methods Two types of substrates, discs and root form cylinders were prepared using a grade 1 commercially pure (CP) Ti rod. A RF–magnetron sputtering device was used to coat specimens with HA. Magnetron sputtering was set at 150 W for 22 hours at 100°C under continuous argon gas flow and substrate rotation at 10 rpm. Coat properties were evaluated via field emission scanning electron microscopy (FESEM), scanning electro

The present work deals with an experimental investigation of charging and discharging processes in thermal storage system using a phase change material PCM. Paraffin wax was used as the PCM which is formed in spherical capsules and packed in a cylindrical packed column which acted as an energy storage system. Air was used as the heat transfer fluid HTF in thermal storage unit. The effect of flow rate and inlet temperature of HTF on the time of charging and discharging process were studied. The results showed that the faster storage of thermal energy can be made by high flow rate of heat transfer fluid HTF and high inlet temperature of heat transfer fluid. It was found that at 65°C HTF inlet temperature, the melting and solidification pr

In this study the Bauxite has been activated and used to prepare two complexes: Bauxite - urea and Bauxite - melamine, these complexes were merged and polymerized with formaldehyde to prepare the complex Bauxite polymer - urea - melamine - formaldehyde (modified Bauxite). In the Bauxite-urea complex XRD results indicate that the urea molecules penetrate among the layers of the crystal plane (110) of the Gibbsite mineral while in the Bauxite-melamine the interaction was at the outer surface of the Bauxite forming minerals because the relatively large volume of the melamine molecule. FT-IR results show the interaction of these two bases with Bauxite was mainly based on the hydrogen bonding and in less extent on the coordination between N l

In this study, the effect of glass fiber reinforced polymer (GFRP) section and compressive strength of concrete in composite beams under static and low velocity impact loads was examined. Modeling was performed and the obtained results were compared with the test results and their compatibility was evaluated.‎ Experimental tests of four composite beams were carried out, where two of them are control specimen with 20 MPa compressive strength of concrete deck slab and 50 MPa for other. Bending characteristics were affected by the strength of concrete under impact loading case, as it increased maximum impact force and damping time at a ratio of 59% and reduced the damping ratio by 47% compared to the reference hybrid beam. Under stat