The aim of the present research is to study the dissolution and transport process of
benzene as a light nonaqueous phase liquid (LNAPL) in saturated porous media.
Unidirectional flow at water velocities ranged from 0.90 to 3.60 cm/hr was adopted to study
this process in a three dimensional saturated sand tank (100 cm×40 cm×35 cm). This tank
represents a laboratory-scale aquifer. The aquifer was constructed by packing homogeneous
sand in the rectangular tank. The experimental results were used to characterize the
dissolution behavior of an entrapped nonaqueous phase benzene source in a three dimensional
aquifer model. The time invariant average mass transfer coefficient was determined at each
interstitial velocit

Therapeutically and prophylactically using Microspheres containing doxycycline isolated from shell of shrimp. Low molecule weight poly lactic acid was prepared. In this study, Poly lactic acid (PLA)/ poly vinyl alcohol (PVA)/poly ethyleneglycol(PEG) loading doxycycline blend solutions was prepared. Also Poly lactic acid (PLA)-Tannin blend via solvent evaporation method was prepared. Microspheres of chitosan/gelatin microsphere loading doxycycline was prepared by emulsion crosslinking technique. Both microsphere and blends were characterized by Fourier transform infrared (FTIR) spectrophotometer. The FTIR spectra were shown distinguish bands. The in vitro release of doxcycline from its matrix at pH 7 was studied. The prophylactic

The novel heterocyclic organozinc compounds were prepared from the reaction of diazonum salt cytosine zinc chloride with thymol and vanilin as coupler components. The prepared compounds were characterized by elemental analysis and UV-Vis, FTIR and 1HMNR spectroscopic techniques. The biological activity was also studied for all prepared compounds. 

A new series of metal ions complexes of VO(II), Cr(III), Mn(II), Zn(II), Cd(II) and Ce(III) have been synthesized from the Schiff bases (4-chlorobenzylidene)-urea amine (L1) and (4-bromobenzylidene)-urea amine (L2). Structural features were obtained from their elemental microanalyses, magnetic susceptibility, molar conductance, FT-IR, UV–Vis, LC-Mass and 1HNMR spectral studies. The UV–Vis, magnetic susceptibility and molar conductance data of the complexes suggest a tetrahedral geometry around the central metal ion except, VOII complexes that has square pyramidal geometry, but CrIII and CeIII octahedral geometry. The biological activity for the ligand (L1) and its Vanadium and Cadmium complexes were studied. Structural geometries of com

Agent technology has a widespread usage in most of computerized systems. In this paper agent technology has been applied to monitor wear test for an aluminium silicon alloy which is used in automotive parts and gears of light loads. In addition to wear test monitoring، porosity effect on
wear resistance has been investigated. To get a controlled amount of porosity, the specimens have
been made by powder metallurgy process with various pressures (100, 200 and 600) MPa. The aim of
this investigation is a proactive step to avoid the failure occurrence by the porosity.
A dry wear tests have been achieved by subjecting three reciprocated loads (1000, 1500 and 2000)g
for three periods (10, 45 and 90)min. The weight difference a

4-methylaniline and its Schiff base derivative were intercalated into the Bentonite clay interlayers in a solid state reaction followed by a condensation reaction to produce two organo-clay composites. X-ray diffraction was used to identify the changes in basal spacing of montmorillonite layers which exhibited noticeable alteration before and after the formation of the composites. FT-IR spectra, on the other hand, were utilized for identifying the structural compositions of the prepared materials as well as the formation of the intercalated Schiff base derivative. The surface morphology of the composites was examined by Scanning Electron Microscopy SEM and Atomic Force Microscope AFM, which reflected some differences in the surface of prepa

An oral bi layer  sustained release (SR) strips of Sodium  Montelukast SMLT , which is selective  leukotriene  antagonist  , used  for  patients  suffered from mid-night asthma , were prepared successfully ,using different polymers, like guar  gum , carrageenan , and xanthan gum , by solvent casting method .

The results obtained by this study revealed  ,that best  fast  dissolving  film of  SMLT was  loaded  in carrageenan   polymer 57%  w\w (30mg.) ,  with  acceptable  physical properties, like film thickness , elastic endurance and  surface pH  .

Besides  to that , the  disintegration  t

Because of the conservation problems causes by the existence of water hyacinth (W.H) as an watery plant in water bodies of Iraq, our study aimed to make  use of (W.H) by isolation of microcrystalline cellulose, and a new method of preparation of Nano crystalline cellulose. Microcrystalline cellulose was produced using base bleaching method by sodium hypochlorite [NaOCl] to remove unorganized region of cellulose and lignin to create particles comprising of micro crystal and preparing of Nano crystalline cellulose from microcrystalline cellulose by acid hydrolysis and ultrasonic treatment. The Nano crystalline and microcrystalline cellulose characterized by AFM, FTIR, XRD and TGA. FT-IR spectra of microcrystalline cellules and Nano cr